dc.creator.ID |
SIMÕES, T. M. S. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/4339479357451457 |
pt_BR |
dc.contributor.advisor1 |
RODRIGUES, Rodrigo Araújo. |
|
dc.contributor.advisor1ID |
RODRIGUES, R. A. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/7538420607868266 |
pt_BR |
dc.contributor.referee1 |
RODRIGUES, Rachel de Queiroz Ferreira. |
|
dc.contributor.referee1ID |
RODRIGUES, R. Q. F. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/3982816841191397 |
pt_BR |
dc.contributor.referee2 |
ROSENDO, Rosana Araújo. |
|
dc.contributor.referee2ID |
ROSENDO, R. A. |
pt_BR |
dc.description.resumo |
As resinas compostas representam os materiais mais utilizados em restaurações
estéticas dos elementos dentários. Para tal necessitam em sua composição de
partículas de carga que proporcionem melhor lisura superficial, facilitando os
procedimentos de polimento, ao mesmo tempo em que contribuem para o aumento
na resistência mecânica. O objetivo deste estudo foi comparar a resistência à
compressão de duas resinas compostas utilizadas na Clínica-Escola de Odontologia
da UFCG/Patos-PB com diferentes cargas inorgânicas, variando a distância de
fotopolimerização. Foram confeccionados 60 corpos de prova das duas marcas
estudadas, de acordo com ISO 4049, sendo estes submetidos à mensuração da
Microdureza Vickers, após a polimerização, variando a distância da ponteira do
fotopolimerizador em relação ao corpo de prova. Os dados foram tabulados e
analisados no software SPSS (versão 21) e após a aplicação dos testes estatísticos
de Kruskal Wallis e Mann Whitney foi observada diferença estatística significante nas
comparações feitas com a distância de 3mm para resina Llis®, cuja carga inorgânica
é formada por partículas de vidro de bário-alumínio. Isso mostra que algumas
marcas não permitem um distanciamento da ponta do fotopolimerizador, o que caso
não respeitado pode afetar a dureza das resinas compostas. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Saúde e Tecnologia Rural - CSTR |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Odontologia |
pt_BR |
dc.title |
Avaliação da microdureza vickers de dois compósitos variando a composição e distância de fotopolimerização. |
pt_BR |
dc.date.issued |
2015-05-26 |
|
dc.description.abstract |
Composite resins represent restorative materials most used for rehabilitation of
dental cavities in anterior teeth. To this need in the composition of filler particles
which provide improved surface smoothness, making the polishing procedure, while
contributing to the increase in the mechanical strength. The aim of this study was to
compare the compressive strength of two composite resins used in the School Clinic
of Dentistry UFCG / Patos-PB with different inorganic fillers, varying the distance
curing. 60 specimens of the two brands studied will be made in accordance with ISO
4049, and these will be subjected to measurement of Vickers Microhardness, after
polymerization, varying the distance of the tip of the curing light to the body of
evidence. Data were analyzed with SPSS (version 21) software and after the
application of statistical tests of Kruskal Wallis and Mann Whitney statistical
difference was observed in comparisons with distance from 3mm to Llis® resin, which
is formed by inorganic filler particles barium-aluminum glass. This shows that some
brands do not allow a separation of the tip of the curing light, which if not met can
affect the hardness of composite resins. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/26041 |
|
dc.date.accessioned |
2022-06-29T17:52:05Z |
|
dc.date.available |
2022-06-29 |
|
dc.date.available |
2022-06-29T17:52:05Z |
|
dc.type |
Trabalho de Conclusão de Curso |
pt_BR |
dc.subject |
Resinas compostas |
pt_BR |
dc.subject |
Fotopolimerização |
pt_BR |
dc.subject |
Microdureza de Vickers |
pt_BR |
dc.subject |
Resistência à compressão - resinas |
pt_BR |
dc.subject |
Clínica Escola de Odontologia - CSTR UFCG |
pt_BR |
dc.subject |
Software SPSS |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SIMÕES, Thamyres Maria Silva. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Evaluation of Vickers microhardness of two composites varying the composition and light curing distance. |
pt_BR |
dc.identifier.citation |
SIMÕES, Thamyres Maria Silva. Avaliação da microdureza vickers de dois compósitos variando a composição e distância de fotopolimerização. 2015. 41f. Trabalho de Conclusão de Curso (Artigo), Curso de Bacharelado em Odontologia, Centro de Saúde e Tecnologia Rural, Universidade Federal de Campina Grande - Patos - Paraíba - Brasil, 2015. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/26041 |
pt_BR |