Utilização da polpa de sisal como elemento de reforço do concreto leve.

Mostrar registro simples

dc.creator.ID PADILHA, J.A.S. pt_BR
dc.creator.Lattes Use of sisal pulp as reinforcing element for lightweight concrete. pt_BR
dc.contributor.advisor1 TOLÊDO FILHO, Romildo Dias.
dc.contributor.advisor1ID TOLEDO FILHO,R.D. pt_BR
dc.contributor.advisor1Lattes http://lattes.cnpq.br/8449916971915629 pt_BR
dc.contributor.referee1 BARBOSA, Normando Perazo.
dc.contributor.referee2 KURUVILLA, Joseph.
dc.description.resumo O presente estudo visou o desenvolvimento de materiais compósitos leves reforçados com o resíduo do desfibramento da fibra de sisal na forma de polpa. A fibra de sisal e a polpa de bambu foram também utilizadas na investigação. Foram determinadas as propriedades físicas (densidade, absorção de água, índice de vazios e variações dimensionais) e mecânicas (resistência à compressão e flexão) dos compósitos bem como sua condutividade térmica. Além da cura em água procedeu-se a cura dos compósitos em autoclave visando melhorar as suas propriedades mecânicas. Uma técnica de produção usando energia de prensagem foi estudada com o objetivo de se produzir compósitos estruturais. A densidade dos compósitos variou de 900 a 1700 kg/m3 dependendo do traço, tipo de cura e processo produtivo utilizado. A absorção de água variou de 31 a 65% enquanto que o índice de vazios variou de 39,1 a 53,8%. Os compósitos apresentaram variações dimensionais variando de 0,97 a 2,29 mm/m. Os resultados obtidos indicaram valores de resistência à compressão variando de 0,89 a 35,0 MPa e módulo de ruptura de 0,45-3,13 MPa. A condutividade térmica dos compósitos variou de 0,16-0,44 W/m.K dependendo do teor de polpa de sisal e vermiculita presente na mistura. Com estes resultados os compósitos polpa de sisal-argamassa de vermiculita podem ser utilizados, dependendo do traço, tipo de cura e método de produção, como materiais isolantes, na produção de painéis divisórios e de componentes habitacionais, assim como na produção de elementos estruturais. pt_BR
dc.publisher.country Brasil pt_BR
dc.publisher.department Centro de Tecnologia e Recursos Naturais - CTRN pt_BR
dc.publisher.program PÓS-GRADUAÇÃO EM ENGENHARIA AGRÍCOLA pt_BR
dc.publisher.initials UFCG pt_BR
dc.subject.cnpq Engenharia agrícola.
dc.title Utilização da polpa de sisal como elemento de reforço do concreto leve. pt_BR
dc.date.issued 1999-11
dc.description.abstract The main objective of this study was to develop composite materiais reinforced with sisal pulp. Sisal fibres and bamboo pulp were also used in the investigation. It was determined the physical (density, water absorption, volume of voids and dimensional changes) and mechanical (compressive and flexural strength) properties of the composites as well as its thermal conductivity. Besides the water curing the composites were cured in autoclave in order to improve its mechanical performance. Compression moulding was used in order to produce composites for structural applications. The density of the composites ranged frora 900 to 1700 kg/m3 depending on the mix proportion, type of cure and method of production. The water absorption ranged from 31 to 65% whereas the volume of voids ranged from 39,1 to 53,8%. The dimensional changes ranged from 0,97 to 2,29 mm/m. Values of compression and flexural strength ranging from, respectively, 0,89 to 35 MPa and 0,45 to 3,13 MPa were observed for the composites. Thermal conductivity values between 0,16 and 0,44 W/m.K were observed depending on the content of sisal pulp and vermiculite present in the mix. The results indicated that depending on the mix proportion, cure condition and production method the composites can be used as insulating material, in the production of partition walls, house components as well as structural elements. pt_BR
dc.identifier.uri http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/2618
dc.date.accessioned 2019-01-29T18:04:47Z
dc.date.available 2019-01-29
dc.date.available 2019-01-29T18:04:47Z
dc.type Dissertação pt_BR
dc.subject Construções rurais.
dc.subject Sisal.
dc.subject Materiais leves - construção civil.
dc.subject Vermiculita - compósito.
dc.subject Tijolo - propriedades mecânicas.
dc.subject Compósitos de materiais - construção civil.
dc.subject Rural constructions.
dc.subject Lightweight construction materials.
dc.subject Vermiculite - composite.
dc.subject Brick - mechanical properties.
dc.subject Composites of materials - civil construction.
dc.rights Acesso Aberto pt_BR
dc.creator PADILHA, José Altair dos Santos.
dc.publisher Universidade Federal de Campina Grande pt_BR
dc.language por pt_BR
dc.title.alternative Use of sisal pulp as reinforcing element for lightweight concrete. pt_BR
dc.identifier.citation PADILHA, José Altair dos Santos. Utilização da polpa de sisal como elemento de reforço do concreto leve. 140f. 1999. (Dissertação de Mestrado em Engenharia Agrícola), Programa de Pós-Graduação em Engenharia Agrícola, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba - Campus II Campina Grande - Brasil, 1999. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/2618 pt_BR