dc.creator.ID |
RAMOS, S. M. L. S. |
pt_BR |
dc.contributor.advisor1 |
KIMINAMI, Ruth Herta Goldschmidt Aliaga. |
|
dc.contributor.advisor1ID |
KIMINAMI, R. H. G. A. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/7643216999108223 |
pt_BR |
dc.contributor.advisor2 |
COSTA, Edson Guedes da. |
|
dc.contributor.advisor2ID |
COSTA, E. G. |
pt_BR |
dc.contributor.referee1 |
LACERDA, Maria do Socorro de. |
|
dc.contributor.referee1ID |
LACERDA, M. S. |
pt_BR |
dc.description.resumo |
O efeito da adição de alumina (0,005 mol %) nas características elétricas varistoras dos sistemas : a) 96 ZnO. 3Bi²O³. CO³O£ (mol %); b) 98,5 ZnO. Bi²O³.0,5 CO³O£ (mol %); c) 95ZnO.. 3Bi²O³.CO³O£.MnO2 (mol %) e d) 98 ZnO. Bi²O³.0,5CO³O£.0,5MnO (mol %) foi analisado em amostras sintetizadas a 1000°C, 1100°C e 1150°C. Para os sistemas "a" e "d" observou-se uma queda nas características elétricas. No caso do sistema "a" deve ter sido causada provavelmente pela inibição do crescimento dos grãos pelos, íons Al³+ em excesso; e no caso do sistema "d" torna-se necessário a análise microestritural. Os sistemas "b" e "c" apresentam uma considerável melhoria no comportamento não-óhmico. No caso do sistema "b", para justificar esta melhoria, torna-se necessário a análise microestrutural. Já sistema "c", o efeito pode ser atribuído possivelmente ao aumento da resistividade nos contornos dos grãos. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de Materiais. |
pt_BR |
dc.title |
Efeito da adição de alumina nas características elétricas de varistores à base de óxido de zinco (ZnO). |
pt_BR |
dc.date.issued |
1991-01-24 |
|
dc.description.abstract |
The effect of the addition of alumina (0.005 mol %) on the varistor electrical characteristics of the systems: a) 96 ZnO. 3Bi²O³. CO³O² (mol %); b) 98.5 ZnO. Bi²O³.0.5 CO³O£ (mol %); c) 95ZnO.. 3Bi²O³.CO³O£.MnO2 (mol %) and d) 98 ZnO. Bi²O³.0.5CO³O£.0.5MnO (mol %) was analyzed in samples synthesized at 1000°C, 1100°C and 1150°C. For systems "a" and "d" a drop in electrical characteristics was observed. In the case of the "a" system, it must have been probably caused by the inhibition of grain growth by excess Al³+ ions; and in the case of the "d" system, microstructural analysis becomes necessary. Systems "b" and "c" show a considerable improvement in non-ohmic behavior. In the case of system "b", to justify this improvement, a microstructural analysis is necessary. In the "c" system, the effect can possibly be attributed to the increase in resistivity at the grain boundaries. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/26458 |
|
dc.date.accessioned |
2022-07-27T18:10:59Z |
|
dc.date.available |
2022-07-27 |
|
dc.date.available |
2022-07-27T18:10:59Z |
|
dc.type |
Trabalho de Conclusão de Curso |
pt_BR |
dc.subject |
Estágio supervisionado - Engenharia de Materiais |
pt_BR |
dc.subject |
Varistores de óxido de zinco |
pt_BR |
dc.subject |
Alumina em varistores de óxido de zinco |
pt_BR |
dc.subject |
Supervised Internship - Materials Engineering |
pt_BR |
dc.subject |
Zinc Oxide Varistors |
pt_BR |
dc.subject |
Alumina in zinc oxide varistors |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
RAMOS, Suédina Maria de Lima Silva. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Effect of alumina addition on electrical characteristics of zinc oxide (ZnO)-based varistors. |
pt_BR |
dc.identifier.citation |
RAMOS, Suédina Maria de Lima Silva. Efeito da adição de alumina nas características elétricas de varistores à base de óxido de zinco (ZnO). 1991. 57f. (Relatório de Estágio) Curso de Bacharelado em Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba - Campus II - Campina Grande - PB - Brasil, 1991. Disponível em: tp://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/26458 |
pt_BR |