dc.creator.ID |
BEZERRA NETA, I. A. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/4237409241499220 |
pt_BR |
dc.contributor.advisor1 |
MENEZES, Romualdo Rodrigues. |
|
dc.contributor.advisor1ID |
MENEZES, R. R.. |
pt_BR |
dc.contributor.advisor1ID |
Menezes, Romualdo R. |
pt_BR |
dc.contributor.advisor1ID |
Menezes, Romualdo Rodrigues. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/1169292996645931 |
pt_BR |
dc.contributor.referee1 |
SANTANA, Lisiane Navarro de Lima. |
|
dc.contributor.referee1ID |
SANTANA, L. N. L. |
pt_BR |
dc.contributor.referee1ID |
Santana, Lisiane Navarro Lima. |
pt_BR |
dc.contributor.referee1ID |
De Lima Santana, Lisiane Navarro. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/4057799848801141 |
pt_BR |
dc.contributor.referee2 |
BRAGA, Aluska do Nascimento Simões. |
|
dc.contributor.referee2ID |
SIMÕES, A. N. |
pt_BR |
dc.contributor.referee2ID |
BRAGA, A.N.S. |
pt_BR |
dc.contributor.referee2ID |
A. Nascimento;Simões, Aluska N. |
pt_BR |
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/2429557575387821 |
pt_BR |
dc.description.resumo |
Materiais nanoestruturados à base de dióxido de titânio (TiO2) têm apresentado
grande potencial para o desenvolvimento de biomateriais devido às suas excelentes
propriedades físico-químicas. Sendo assim, o presente trabalho tem como objetivo
produzir scaffolds nanofibrilares de TiO2 e híbrido de poli(ácido lático)/dióxido de titânio
(PLA/TiO2) por fiação por sopro em solução visando sua aplicação na regeneração de
tecido ósseo. As nanofibras de TiO2 foram obtidas empregando etanol, dimetil
carbonato e isopropóxido de titânio (TTIP) com proporção em volume 1:1:0,8,
respectivamente. Enquanto, as nanofibras híbridas foram produzidas com TTIP e
ácido acético na proporção (em volume) 1,2:1. Os scaffolds de TiO2 foram produzidos
por prensagem uniaxial utilizando fibras não calcinadas e calcinados a
500, 600 e 700 °C. As nanofibras híbridas obtidas de TiO2/PLA foram colocadas na
estufa a 60 °C, resultando em um scaffold híbrido constituído de TiO2 e PLA. Os
scaffolds de TiO2 e o híbrido foram caracterizados por microscopia eletrônica de
varredura (MEV), difração de raios X (DRX), espectroscopia de infravermelho por
transformada de fourrier (FTIR), microtomografia computadorizada, análise térmica
diferencial (DTA) e gravimétrica (TGA). A análise morfológica mostrou que os
scaffolds nanofibrilares de TiO2 calcinados apresentaram uma quantidade menor de
beads e uma morfologia uniforme e sem defeitos. Através da análise de DRX e FTIR
foi verificada a formação das fases anatase na temperatura de 500 °C e de rutilo na
temperatura de 600 °C. Enquanto o híbrido apresenta uma banda, o que indica seu
comportamento predominantemente amorfo. As imagens microtomográficas
revelaram que os scaffolds de TiO2 produzidos a 700 °C e o híbrido apresentaram
uma estrutura interligada e altamente porosa. Enquanto os scaffolds produzidos por
prensagem e calcinação apresentaram porosidade inferior a 5%. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Engenharia Elétrica e Informática - CEEI |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de Materiais |
pt_BR |
dc.title |
Desenvolvimento de scaffolds de TiO2 e TiO2/PLA obtidos por fiação por sopro em solução. |
pt_BR |
dc.date.issued |
2020-02-10 |
|
dc.description.abstract |
Nanostructured materials based on titanium dioxide (TiO2) have great potencial for the
development of biomaterials due to their excellent physical and chemical
characteristics. Thus, the present work aims to produce nanofibrillary scaffolds of TiO2
and hybrid of poly (lactic acid) / titanium dioxide (PLA / TiO2) by solution blow
spinning that uses its regeneration of bone tissue. As TiO2 nanofibers were used in the
use of ethanol, dimethyl carbonate and titanium isopropoxide (TTIP) with a 1: 1: 0,8
volume ratio, respectively. While the hybrid nanofibers were produced with TTIP and
acetic acid in the proportion (by volume) 1.2: 1. TiO2 scaffolds was used by uniaxial
compression, using uncalcined and calcined fibers at 500, 600 and 700 ° C. As
nanofibers Hybrid cut TiO2 / PLA were placed in the oven at 60 ° C, resulting in a hybrid
scaffold consisting of TiO2 and PLA. The TiO2 scaffolds and the hybrid used were
characterized by scanning electron microscopy (MEV), X-ray diffraction (DRX), Fourier
transform infrared spectroscopy (FTIR), thermogravimetry (TGA), differential thermal
analysis (DTA) and computerized microtomography. The morphological analysis
showed that the calcined TiO2 nanofibrillary scaffolds presented a smaller number of
beads and a uniform morphology. Through the analysis of DRX and FTIR, the
formation of anatomical phases was verified at a temperature of 500 ° C and at a
temperature of rutile use of 600 ° C. While the hybrid has a band, which indicates its
predominantly amorphous behavior. As microtomographic images revealed the TiO2
scaffolds applied at 700 ° C and the hybrid showed an interconnected and highly
porous structure. While the scaffolds produced by pressing and calcination showed
porosity below 5%. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/27199 |
|
dc.date.accessioned |
2022-09-14T18:15:55Z |
|
dc.date.available |
2022-09-14 |
|
dc.date.available |
2022-09-14T18:15:55Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Biomateriais |
pt_BR |
dc.subject |
Scaffolds Nanofibrilares |
pt_BR |
dc.subject |
Híbrido |
pt_BR |
dc.subject |
Dióxido de Titânio |
pt_BR |
dc.subject |
Biomaterials |
pt_BR |
dc.subject |
Nanofibrillary Scaffolds |
pt_BR |
dc.subject |
Hybrid |
pt_BR |
dc.subject |
Dioxide of Titanium |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
BEZERRA NETA, Ione Amorim. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Development of TiO2 and TiO2/PLA scaffolds obtained by solution blow spinning. |
pt_BR |
dc.identifier.citation |
BEZERRA NETA, Ione Amorim. Desenvolvimento de scaffolds de TiO2 e TiO2/PLA obtidos por fiação
por sopro em solução. 2020. 74 fl. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2020. |
pt_BR |