Avaliação da resistência à corrosão de revestimento à base de inconel 625 utilizando os processos de soldagem MIG e plasma pó.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA
→
Mestrado em Engenharia Mecânica.
→
Ver item

dc.creator.ID	SANTOS, A. X.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/0810494477757052	pt_BR
dc.contributor.advisor1	MACIEL, Theophilo Moura.
dc.contributor.advisor1ID	MACIEL, T. M.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/9476858938351846	pt_BR
dc.contributor.referee1	SANTOS, Marco Antonio dos.
dc.contributor.referee1ID	SANTOS, M. A	pt_BR
dc.contributor.referee1Lattes	http://lattes.cnpq.br/4825985900425353	pt_BR
dc.contributor.referee2	SANTANA, Renato Alexandre Costa de.
dc.contributor.referee2ID	SANTANA, R. A. C.	pt_BR
dc.contributor.referee2Lattes	http://lattes.cnpq.br/1438381290031148	pt_BR
dc.description.resumo	As falhas por corrosão são as principais causadoras de vazamento na indústria do petróleo. Por esta razão tem sido muito estudada a utilização de novos materiais com melhores resistências a este fenômeno. Uma das alternativas mais utilizadas, devido ao menor custo envolvido, é a aplicação de revestimentos com estes materiais através de processos de soldagem. Este trabalho teve como objetivo inicialmente encontrar os melhores parâmetros de soldagem para se obter o perfil geométrico dos cordões de solda mais adequado para este fim, principalmente a diluição, utilizando planejamento experimental estatístico fatorial em dois níveis e determinar em seguida a resistência à corrosão dos cordões depositados utilizando dois processos de soldagem. Foram utilizados o processo Plasma Pó (PTA-P) e o processo MIG (Metal Inert Gás) ambos automatizados, e como metal de adição, a liga AWS ER NiCrMo-3, à base de Ni , conhecida comercialmente como Inconel 625, na forma de pó com granulometria de 63 µm no processo PTA-P e na forma de arame com diâmetro de 1,2 mm no processo MIG. Como metal de base utilizou-se chapas do aço API 5L X70 utilizado na fabricação de dutos para transporte de petróleo. A resistência à corrosão dos revestimentos foi avaliada por polarização potenciodinâmica linear e espectroscopia de impedância eletroquímica. Foram avaliados também o percentual de Fe e os valores de microdureza na superfície dos revestimentos, Os resultados mostraram que o reforço, a penetração e a diluição dos revestimentos depositados pelo processo PTA-P assim como os seus valores de microdureza foram menores do que aqueles obtidos pelo processo GMAW. Os revestimentos obtidos pelo processo PTA-P também apresentaram melhores resultados de resistência à corrosão.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.title	Avaliação da resistência à corrosão de revestimento à base de inconel 625 utilizando os processos de soldagem MIG e plasma pó.	pt_BR
dc.date.issued	2014-02-28
dc.description.abstract	The corrosion failures are the main cause of leakage in oil industry. Because of this new materials with higher corrosion resistance have been researched. One of the alternatives more used, for its low cost, is the application of coating by welding process. This work aimed first to find the better welding parameters to obtain the more adequate weld bead geometry, mainly the dilution, using a factorial statistical experimental design on two levels, and following to determinate its corrosion resistance using two welding process. Automatized Plasma Transferred Arc- Powder (PTA-P) and Metal Inert Gas (MIG) were used. The AWS ER NiCrMo-3Ni alloy, knowing as Inconel 625, in powder form with grain size 63 µm and in wire with 1,2 mm diameter were used as filler metals. API 5L X70 steel plate, used in pipeline for oil and gas transportation was used as base metal. The corrosion resistance was evaluated using linear potentiodynamic polarization and electrochemical impedance spectroscopy analysis. The Fe percents and microhardness test in weld bead surface were also done. The results showed that the weld bead hardness and its penetration and dilution obtained by PTA-P process were lower than those obtained by GMAW process. The coating obtained by PTA-P process also presented better corrosion resistance.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/2818
dc.date.accessioned	2019-02-18T17:39:17Z
dc.date.available	2019-02-18
dc.date.available	2019-02-18T17:39:17Z
dc.type	Dissertação	pt_BR
dc.subject	Revestimento	pt_BR
dc.subject	Resistência à Corrosão	pt_BR
dc.subject	Processo PTA-P	pt_BR
dc.subject	Processo MIG	pt_BR
dc.subject	Inconel 625	pt_BR
dc.subject	Coating	pt_BR
dc.subject	Corrosion Resistance	pt_BR
dc.subject	PTA-P process	pt_BR
dc.subject	MIG process	pt_BR
dc.rights	Acesso Aberto	pt_BR
dc.creator	SANTOS, Aureliano Xavier dos.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Evaluation of corrosion resistance of 625 inconel-based coating using the MIG and plasma plasma welding processes.	pt_BR
dc.identifier.citation	SANTOS, Aureliano Xavier dos. Avaliação da resistência à corrosão de revestimento à base de inconel 625 utilizando os processos de soldagem MIG e plasma pó. 2014. 150f. Dissertação (Mestrado em Engenharia Mecânica) – Programa de Pós-Graduação em Engenharia Mecânica, Centro de Ciência e Tecnologia, Universidade Federal de Campina Grande, Paraíba, Brasil, 2014. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/2818	pt_BR