dc.creator.ID |
DIAS, R. T. V. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/9505866414116804 |
pt_BR |
dc.contributor.advisor1 |
LOPES NETO, José Pinheiro. |
|
dc.contributor.advisor1ID |
LOPES NETO, J. P. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/1800101850675185 |
pt_BR |
dc.contributor.referee1 |
NASCIMENTO, José Wallace Barbosa do. |
|
dc.contributor.referee1ID |
NASCIMENTO, J. W. B. |
pt_BR |
dc.contributor.referee2 |
RESENDE, Maria Luiza Souza. |
|
dc.contributor.referee2ID |
RESENDE, M. L. S. |
pt_BR |
dc.contributor.referee3 |
LOPES, Fernanda Fernandes de Melo. |
|
dc.contributor.referee3ID |
LOPES, F. F. M. |
pt_BR |
dc.description.resumo |
No estado da Paraíba há significativa concentração do mineral vermiculita
que, através da sua extração, gera matérias primas para construção civil. Durante seu
beneficiamento, toneladas de resíduos são gerados e depositados no meio ambiente de
forma inadequada, causando grandes impactos ambientais. Diante disto, esse trabalho
teve como objetivo analisar a viabilidade do uso do resíduo de vermiculita em
substituição a porção de areia fina natural na elaboração de argamassas de revestimento
com propriedades melhoradas. Foram coletadas amostras de resíduo de vermiculita na
mineradora Pedra Lavrada, Santa Luzia/PB, para realização de testes de caracterização,
buscando avaliar a sua aplicação em argamassas. Foram preparadas argamassas com
traço 1:4 (cimento: areia), com teores de substituição de areia fina por resíduo de 0%,
30%, 60% e 100%. Empregou-se o cimento Portland CP II-Z 32, com fator água/
cimento entre 0,65 e 0,85. As argamassas foram analisadas no estado endurecido através
dos ensaios de resistência à compressão, absorção por imersão e por capilaridade.
Diante do melhor resultado encontrado, foram confeccionadas placas para o teste do
comportamento térmico. A caracterização do resíduo de vermiculita mostrou uma
grande quantidade de finos o que acarretou em melhoria na resistência à compressão,
absorção de água por imersão e capilaridade nas argamassas, quando comparada a
argamassa de referência (0%). Os resultados da análise de comportamento térmico,
obtidos por meio do gradiente térmico entre as faces das placas, aparentaram variação
no gradiente térmico de até 40% superior para as placas que continham resíduo de
vermiculita quando comparado aos resultados obtidos na argamassa de referência (0%).
Com isso, é possível concluir que o resíduo de vermiculita é apropriado para fabricação
de argamassas de revestimento e garante propriedades melhoradas, principalmente
quanto ao seu comportamento térmico em comparação a argamassa de referência. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Tecnologia e Recursos Naturais - CTRN |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA AGRÍCOLA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de Agrícola |
pt_BR |
dc.title |
Desempenho termomecânico de argamassas com adição de resíduos de vermiculita para construções rurais. |
pt_BR |
dc.date.issued |
2018 |
|
dc.description.abstract |
In the state of Paraíba there is a significant concentration of the
vermiculite mineral that, through its extraction, generates raw materials for civil
construction. During its processing, tons of waste are generated and deposited in the
environment in an inadequate way, causing great environmental impacts. The objective
of this work was to analyze the feasibility of the use of the vermiculite residue in
substitution for the portion of natural fine sand in the elaboration of coating mortars
with improved properties. Samples of vermiculite residue were collected at Pedra
Lavrada, Santa Luzia / PB, to perform characterization tests, in order to evaluate their
application in mortars. Mortars with 1: 4 traces (cement: sand) were prepared, with
substitution contents of 0%, 30%, 60% and 100% fine sand. Portland cement CP II-Z
32, with water / cement factor between 0.65 and 0.85, was used. The mortars were
analyzed in the hardened state through the tests of resistance to compression, immersion
absorption and capillarity. Considering the best result found, plates were prepared for
the thermal behavior test. The characterization of the vermiculite residue showed a great
amount of fines, which led to an improvement in the compressive strength, water
absorption by immersion and capillarity in the mortar, when compared to the reference
mortar (0%). The results of the thermal behavior analysis, obtained by means of the
thermal gradient between the faces of the plates, showed a variation in the thermal
gradient of up to 40% higher for the plates containing vermiculite residue when
compared to the results obtained in the reference mortar (0% ). Thus, it is possible to
conclude that the vermiculite residue is suitable for the production of coating mortar and
guarantees improved properties, mainly in terms of its thermal behavior compared to the
reference mortar. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/28298 |
|
dc.date.accessioned |
2022-12-12T21:45:48Z |
|
dc.date.available |
2022-12-12 |
|
dc.date.available |
2022-12-12T21:45:48Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Construções rurais e ambiência |
pt_BR |
dc.subject |
Resíduo mineral |
pt_BR |
dc.subject |
Agregado alternativo |
pt_BR |
dc.subject |
Aproveitamento de rejeitos |
pt_BR |
dc.subject |
Compósito cimentício |
pt_BR |
dc.subject |
Comportamento térmico |
pt_BR |
dc.subject |
Argamassas - desempenho termomecânico |
pt_BR |
dc.subject |
Vermiculita - resíduos |
pt_BR |
dc.subject |
Logística reversa |
pt_BR |
dc.subject |
Reciclagem |
pt_BR |
dc.subject |
Mineralogia |
pt_BR |
dc.subject |
Geologia |
pt_BR |
dc.subject |
Rural buildings and ambience |
pt_BR |
dc.subject |
Mineral residue |
pt_BR |
dc.subject |
Alternative aggregate |
pt_BR |
dc.subject |
Use of tailings |
pt_BR |
dc.subject |
Cementitious composite |
pt_BR |
dc.subject |
Thermal behavior |
pt_BR |
dc.subject |
Mortars - thermomechanical performance |
pt_BR |
dc.subject |
Vermiculite - waste |
pt_BR |
dc.subject |
Reverse logistic |
pt_BR |
dc.subject |
Recycling |
pt_BR |
dc.subject |
Mineralogy |
pt_BR |
dc.subject |
Geology |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
DIAS, Renata Tomaz Vieira. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Thermomechanical performance of mortars with addition of vermiculite residues for rural buildings. |
pt_BR |
dc.description.sponsorship |
CNPq |
pt_BR |
dc.identifier.citation |
DIAS, Renata Tomaz Vieira. Desempenho termomecânico de argamassas com adição de resíduos de vermiculita para construções rurais. 2018. 75f. (Dissertação de Mestrado) Programa de Pós-Graduação em Engenharia Agrícola, Centro de Tecnologia e Recursos Naturais, Universidade Federal de Campina Grande - Paraíba - Brasil, 2018. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/28298 |
pt_BR |