dc.creator.ID |
SILVA, P. V. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/5236186784633752 |
pt_BR |
dc.contributor.advisor1 |
NASCIMENTO, José Wallace Barbosa do. |
|
dc.contributor.advisor1ID |
NASCIMENTO, J. W. B. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/9274991135144621 |
pt_BR |
dc.contributor.referee1 |
LOPES NETO, José Pinheiro. |
|
dc.contributor.referee1ID |
LOPES NETO, J. P. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/1800101850675185 |
pt_BR |
dc.contributor.referee2 |
FURTADO, Dermeval Araújo. |
|
dc.contributor.referee2ID |
FURTADO, D. A. |
pt_BR |
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/9812880885367814 |
pt_BR |
dc.contributor.referee3 |
LOPES, Fernanda Fernandes de Melo. |
|
dc.contributor.referee3ID |
LOPES, F.F.M. |
pt_BR |
dc.contributor.referee3Lattes |
http://lattes.cnpq.br/7474887413239360 |
pt_BR |
dc.contributor.referee4 |
BARBOSA, Normando Perazzo. |
|
dc.contributor.referee4ID |
BARBOSA, N. P. |
pt_BR |
dc.contributor.referee4Lattes |
http://lattes.cnpq.br/6420367558476872 |
pt_BR |
dc.contributor.referee5 |
REZENDE, Maria Luiza. |
|
dc.contributor.referee5ID |
REZENDE, M. L. |
pt_BR |
dc.contributor.referee5Lattes |
http://lattes.cnpq.br/6519042338850617 |
pt_BR |
dc.description.resumo |
Na busca por alternativas que visam diminuir a energia de produção e os impactos ambientais,
as pesquisas voltaram a dar ênfase às fibras vegetais em compósitos por serem materiais
considerados menos onerosos e de origem renovável, quando comparadas com as fibras
sintéticas. O progresso das pesquisas e desenvolvimento de novas tecnologias, nesse sentido,
são necessários para a obtenção de um material que atenda às exigências do mercado,
funcionalidade e questões ambientais. A análise se torna mais complexa quando considerada a
relação da fibra com a matriz devido à grande quantidade de fatores que interferem nessa
interação entre a matriz, fibra, forma de processamento e interface. A partir do exposto, optou-
se em utilizar as fibras de caroá (Neoglaziovia variegata) e sisal (Agave sisalana), as quais são
espécies difundidas na Região Nordeste, geradoras de empregos diretos e indiretos em suas
cadeias produtivas. Desse modo, objetivou-se neste trabalho analisar o desenvolvimento de um
compósito cimentício reforçado com teor de 1% de fibras vegetais tratadas com licor
pirolenhoso, visando o reforço estrutural e uma maior longevidade do compósito e da interação
fibra/matriz. Os compósitos foram caracterizados mecanicamente por meio dos testes de flexão
em três pontos; tração por compressão uniaxial e fisicamente por meio do teste de absorção de
água, além de análises térmicas, DRX e morfológica. Já as fibras foram caracterizadas
utilizando testes físicos e mecânicos. Os resultados da microscopia indicaram que o tratamento
proporcionou uma maior limpeza na superfície da fibra, diminuindo a hidrofilicidade e
preservaram a integridade da fibra no compósito. Por outro lado, os ensaios mecânicos
mostraram que para o teste de flexão em três pontos houve uma redução na resistência das fibras
de sisal tratadas, enquanto as de caroá houve um aumento da resistência, ao passo que para o
teste de compressão axial as fibras sem tratamento obtiveram melhores relutâncias. Na
caracterização térmica as fibras sem tratamento alcançaram melhores resultados para a
condutividade térmica. Já no DRX as fibras impregnadas com licor pirolenhoso obtiveram
maior índice de cristalinidade. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Tecnologia e Recursos Naturais - CTRN |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA AGRÍCOLA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Construções Rurais e Ambiência |
pt_BR |
dc.title |
Compósitos com fibras de sisal e caroá com licor pirolhenoso em matriz cimentícia com metacaulim. |
pt_BR |
dc.date.issued |
2022-02-15 |
|
dc.description.abstract |
In the search for alternatives that aim to reduce production energy and environmental impacts,
research has again given emphasis to vegetable fibers in composites, as they are materials
considered less expensive and of renewable origin, when compared to synthetic fibers. The
progress of research and development of new technologies, in this sense, are necessary to obtain
a material that meets the requirements of the market, functionality and environmental issues.
The analysis becomes more complex when considering the relationship between the fiber and
the matrix due to the large number of factors that interfere in this interaction between the matrix,
fiber, processing form and interface. Based on the above, it was decided to use caroá
(Neoglaziovia variegata) and sisal (Agave sisalana) fibers, which are species widespread in the
Northeast Region, generating direct and indirect jobs in their production chains. Thus, the
objective of this work was to analyze the development of a cementitious composite reinforced
with a 1% content of vegetable fibers treated with pyroligneous liquor, aiming at the structural
reinforcement and a greater longevity of the composite and the fiber-matrix interaction. The
composites were mechanically characterized by means of three-point bending tests, tensile tests
by uniaxial compression and physically by means of the water absorption test, in addition to
thermal, XRD and morphological analyses. The fibers were characterized using physical and
mechanical tests. The microscopy results indicate that the treatment provided greater cleaning
on the surface of the fiber, reducing the hydrophilicity and preserving the integrity of the fiber
in the composite. On the other hand, the mechanical tests indicated that for the three-point
bending test there was a reduction in the strength of the treated sisal fibers while the caroá fibers
showed an increase in strength, while for the axial compression test the untreated fibers
obtained better results. In the thermal characterization the untreated fibers obtained better
results for the thermal conductivity. In the XRD, the fibers impregnated with pyroligneous
liquor obtained a higher crystallinity index. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/29406 |
|
dc.date.accessioned |
2023-04-18T12:29:10Z |
|
dc.date.available |
2023-04-18 |
|
dc.date.available |
2023-04-18T12:29:10Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
Agave sisalina |
pt_BR |
dc.subject |
Tratamento de fibra |
pt_BR |
dc.subject |
Neoglaziovia variegat |
pt_BR |
dc.subject |
Compósitos - fibras de sisal caroá |
pt_BR |
dc.subject |
Construções rurais e ambiência |
pt_BR |
dc.subject |
Agave sisalin |
pt_BR |
dc.subject |
Fiber treatment |
pt_BR |
dc.subject |
Composites - caroá sisal fibers |
pt_BR |
dc.subject |
Composites - caroá sisal fibers |
pt_BR |
dc.subject |
Tratamiento de fibra |
pt_BR |
dc.subject |
Neoglaziovia abigarrado |
pt_BR |
dc.subject |
Compuestos - fibras de sisal caroá |
pt_BR |
dc.subject |
Edificios y ambiente rural |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SILVA, Patrícia Venâncio da. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Composites with sisal and caroá fibers with pyrolent liquor in cementitious matrix with metakaolin. |
pt_BR |
dc.title.alternative |
Compuestos con fibras de sisal y caroá con licor pirolento en matriz cementosa con metacaolín. |
pt_BR |
dc.identifier.citation |
SILVA, Patrícia Venâncio da. Compósitos com fibras de sisal e caroá com licor pirolhenoso em matriz cimentícia com metacaulim. 2022. 118 fl. (Tese de Doutorado), Programa de Pós-Graduação em Engenharia Agrícola, Centro de Tecnologia e Recursos Naturais, Universidade Federal de Campina Grande - Paraíba - Brasil, 2022. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/29406 |
pt_BR |
dc.description.resumen |
En la búsqueda de alternativas que apunten a reducir la energía de producción y los impactos ambientales,
la investigación ha vuelto a poner el acento en las fibras vegetales en los composites por ser materiales
considerado menos costoso y de origen renovable, en comparación con las fibras
sintético. El progreso de la investigación y el desarrollo de nuevas tecnologías, en este sentido,
son necesarios para obtener un material que cumpla con los requisitos del mercado,
funcionalidad y problemas ambientales. El análisis se vuelve más complejo cuando se considera la
relación entre la fibra y la matriz debido a la gran cantidad de factores que interfieren en esta
interacción entre matriz, fibra, método de procesamiento e interfaz. Con base en lo anterior, se decidió
si utilizar fibras de caroá (Neoglaziovia variegata) y sisal (Agave sisalana), que son
especies muy extendidas en la Región Nordeste, generando empleos directos e indirectos en sus
cadenas productivas. Así, el objetivo de este trabajo fue analizar el desarrollo de un
compuesto cementoso reforzado con un 1% de contenido de fibras vegetales tratado con licor
piroleñoso, buscando el refuerzo estructural y una mayor longevidad del compuesto y la interacción
fibra/matriz. Los composites se caracterizaron mecánicamente mediante ensayos de flexión.
en tres puntos; tracción por compresión uniaxial y físicamente a través del ensayo de absorción de
agua, además de análisis térmicos, DRX y morfológicos. Las fibras se caracterizaron
mediante ensayos físicos y mecánicos. Los resultados de la microscopía indicaron que el tratamiento
proporcionó una mayor limpieza en la superficie de la fibra, disminuyendo la hidrofilia y
preservó la integridad de la fibra en el compuesto. Por otro lado, las pruebas mecánicas
mostró que para la prueba de flexión de tres puntos hubo una reducción en la fuerza de la fibra
sisal tratado, mientras que caroá hubo un aumento en la resistencia, mientras que para el
prueba de compresión axial, las fibras no tratadas tuvieron mejor reluctancia. En
caracterización térmica las fibras sin tratar lograron mejores resultados para la
conductividad térmica. En el DRX, las fibras impregnadas con licor piroleñoso obtenido
mayor índice de cristalinidad. |
pt_BR |