dc.creator.ID |
SOUSA, A. R. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/9897600291568251 |
pt_BR |
dc.contributor.advisor1 |
RABELLO, Marcelo Silveira. |
|
dc.contributor.advisor1ID |
RABELLO, M. S. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/0384726674523131 |
pt_BR |
dc.contributor.advisor-co1 |
MELO, Tomás Jeferson A. |
|
dc.contributor.advisor-co1ID |
MELO, T. J. |
pt_BR |
dc.contributor.referee1 |
NAVARRO, Rômulo Feitosa. |
|
dc.contributor.referee1ID |
NAVARRO, R. F. |
pt_BR |
dc.contributor.referee2 |
ARAÚJO, Elmo Silvano de. |
|
dc.contributor.referee2ID |
ARAÚJO, E. S. |
pt_BR |
dc.description.resumo |
Os mecanismos de fotodegradação e stress cracking dos materiais
políméricos têm sido amplamente investigados de forma independente, com
grande número de relatos na literatura. Embora em condições de uso esses
dois tipos de degradação possam ocorrer de forma combinada e/ou
simultaneamente, não foram encontrados estudos abordando tal possibilidade.
Este trabalho teve como objetivo investigar a influência da fotodegradação no
stress cracking. Para isso, amostras de poliestireno moldadas por injeção
foram previamente expostas por diferentes intervalos de tempo á radiação
ultravioleta em laboratório e então submetidas ao butanol, que agiu como
líquido de stress cracking, sob diferentes níveis de tensionamento e
temperatura. Foram feitas caracterizações mecânicas, por meio de ensaios de
relaxação de tensão e de tração em diferentes taxas de deformação;
determinação da massa molar por cromatografia por exclusão de tamanho;
análise de superfícies dos corpos-de-prova, inclusive as de fratura após testes
mecânicos, por ensaios de microscopia ótica e eletrônica de varredura; e
espectroscopia no ultravioleta e no visível. Os resultados indicaram que a
fotodegradação provocou redução nas propriedades tênseis com o progresso
do tempo de exposição até 40 dias. Após 60 dias, houve recuperação parcial. A
radiação UV provocou grandes modificações na estrutura molecular do
poliestireno, resultando na redução das propriedades mecânicas.O poliestireno
virgem mostrou-se relativamente inerte ao ser exposto ao butanol na
temperatura ambiente (23°C) sem tensionamento externo. Apesar da pequena
absorção de líquido na temperatura ambiente, em tempos longos de exposição
ao butanol (140 dias), as faces das amostras que sofreram incidência prévia da
radiação ultravioleta por 30 dias mostraram-se intensamente fissuradas. Em
exposições ao butano! na temperatura de 60°C, o poliestireno apresentou
intensa plastificação. A avaliação da influência da fotodegradação no síress
cracking, mediante ensaio de relaxação, indicou diferentes comportamentos
entre o poliestireno virgem e o fotodegradado, com maiores valores de taxa de
relaxação para este último, em ensaios realizados sob as mesmas condições.
A resistência tênsil das amostras submetidas previamente ao ensaio de
relaxação sob butanol caiu drasticamente em relação às amostras ensaiadas
sem o liquido. Foi constatada uma complexa relação entre fotodegradação,
tempo de contato entre o líquido e o polímero, velocidade de deformação e
propriedades mecânicas. O aumento do nível de fotodegradação favoreceu a
intensificação do stress cracking. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia química |
|
dc.title |
Efeito combinado de fotodegradação e stress cracking no poliestireno. |
pt_BR |
dc.date.issued |
2004-07 |
|
dc.description.abstract |
The mechanisms of photodegradation and stress cracking of polymeric
materials have been vastly investigated on independent ways, with a lot of
reports at technical literature. Although under service conditions these two kinds
of degradation can occur under combined way and/or simultaneously, no work
about this possibility was found. The aim of this work was to investigate the
influence of photodegradation at the stress cracking. Injection moulded samples
of polystyrene were previously exposed to the ultraviolet radiation for different
times and then submitted to butanol a stress cracking agent, under several
levels of tensile loads and temperatures. Mechanical analyses were done using
stress relaxations and tensile tests at different strain rates. The molar mass was
determined by size exclusion chromatography; the moulded and fracture
surfaces of the samples after mechanical tests were analyzed by optical and
scanning electron microscopy; and spectroscopy at ultravilotet and visible. The
results indicated that the photodegradation caused reduction in tensile
properties with the progress of the exposure time up to 40 days. After 60 days
there was a partial recovery in tensile properties. The virgin (not exposed to UV
radiation) polystyrene was relatively inert to butanol exposure at room
temperature (23°C), without external stress. Despite the small liquid absorption
at room temperature, at long exposure times (140 days), the moulded surfaces
of samples that previously received direct incidence on UV radiation for 30 days
became highly cracked. The polystyrene after exposure to butanol at 60°C
became plasticized. The evaluation of the influence of the photodegradation at
the stress cracking using stress relaxation test showed different behaviour
between the virgin and photodegraded polystyrene, with higher stress relaxation
rates for the last. The tensile strength of samples previously submitted to stress
under the presence of butanol dropped drastically comparing to samples tested
without the liquid. A complex relation between photodegradation, contact time
between the polymer and liquid, strain rate at tensile tests and mechanical
properties was identified. The more photodegraded the polymer, the more
intense was the stress cracking. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/3010 |
|
dc.date.accessioned |
2019-03-01T17:06:06Z |
|
dc.date.available |
2019-03-01 |
|
dc.date.available |
2019-03-01T17:06:06Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Fotodegradação |
|
dc.subject |
Photodegradation |
|
dc.subject |
Fotodegradación |
|
dc.subject |
Stress cracking |
|
dc.subject |
Agrietamiento por estrés |
|
dc.subject |
Poliestireno |
|
dc.subject |
Polystyrene |
|
dc.subject |
Fotodegradação |
|
dc.subject |
Photodegradation |
|
dc.subject |
Fotodegradación |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SOUSA, Alexandre Rangel de. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Combined effect of photodegradation and stress cracking on polystyrene. |
pt_BR |
dc.identifier.citation |
SOUSA, Alexandre Rangel de. Efeito combinado de fotodegradação e stress cracking no poliestireno. 2004. 116f. (Dissertação de Mestrado em Engenharia Química), Programa de Pós-graduação em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2004. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/3010 |
pt_BR |