dc.creator.ID |
OLIVEIRA, S. V. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/2988178262762974 |
pt_BR |
dc.contributor.advisor1 |
ARAÚJO, Edcleide Maria. |
|
dc.contributor.advisor1ID |
ARAÚJO, E. M. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/1097999681102529 |
pt_BR |
dc.contributor.referee1 |
PEREIRA, Celeste Margarida Correia. |
|
dc.contributor.referee1ID |
PEREIRA, C. M. C. |
pt_BR |
dc.contributor.referee2 |
LIMA, Antonio Gilson Barbosa de. |
|
dc.contributor.referee2ID |
LIMA, A. G. B. |
pt_BR |
dc.contributor.referee3 |
PAZ, Renê Anísio da. |
|
dc.contributor.referee3ID |
PAZ, R. A. |
pt_BR |
dc.contributor.referee4 |
MELO, Tomás Jeferson Alves de. |
|
dc.contributor.referee4ID |
MELO, T. J. A. |
pt_BR |
dc.contributor.referee5 |
NEVES, Gelmires de Araújo. |
|
dc.contributor.referee5ID |
NEVES, G. A. |
pt_BR |
dc.description.resumo |
Nanocompósitos com matriz de PEAD foram preparados por
intercalação por fusão, com a finalidade de analisar o efeito antichama deste
materiaí. Para o desenvolvimento dos nanocompósitos, foram utilizadas as
argilas montmorilonita (MívIT), organofílica (OMMT) e um retardante de chama
(RCP) com os percentuais de 1, 3, 6 e 9% em massa. O polietileno enxertado
com anidrído maléico (PE-g-MA) foi usado como compatibilizante dos sistemas.
O PEAD e seus sistemas foram avaliados por: DRX, MET, MEV, propriedades
mecânicas (tração e impacto), HDT, DSC, TG e inftamabilidade (UL94HB,
índice de oxigênio (LOI) e calorimetria de cone). Os difratogramas de raios X
apresentaram uma aparente intercalação e esfoliação parcial como também
formação de microcompósito. A dispersão e a distribuição da argila e do
retardante de chama foram observadas a partir das morfologias obtidas por
MEV. Por MET foi observado que o sistema com 1% de argila OMMT
apresentou predominância de esfoliação. Já o sistema com 3% de OMMT
apresentou esfoliação parcial e, esta reduziu a medida que o teor de argila
aumentou. Comparando-se as propriedades mecânicas do PEAD em relação
aos sistemas, foi verificado que o módulo de elasticidade praticamente não foi
alterado. Por TG foi verificado que as cargas MMT, OMMT e RCP atuaram
melhorando o comportamento térmico dos nanocompósitos em relação a matriz
de PEAD. Por DSC foi visto que a presença da argila alterou a cristalínídade da
matriz. Os resultados obtidos para o índice de oxigênio revelaram que tanto o
PEAD quantos seus sistemas apresentaram propriedades antichama. Por meio
dos testes de inflamabilidade horizontal, foi verificado que a presença de 1% de
argila MMT reduziu em 25% a inflamabilidade do PEAD. Por calorimetria de
cone foi verificado que o sistema que contem 9% de argila OMMT diminuiu em
33% a inflamabilidade dos nanocompósitos. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
ENGENHARIA DE MATERIAIS |
|
dc.title |
Nanocompósitos de polietileno/argila bentonítica com propriedades antichama. |
pt_BR |
dc.date.issued |
2013-07 |
|
dc.description.abstract |
HOPE nanocomposites were prepared by melt intercalation, in order to
examine the fiame retardant effect of this material For the development of
nanocomposites were used the clay montmoriilonite (MMT), organoclay
(OMMT) and flame retardant (RCP) with the percentage of 1, 3, 6 and 9 wt%.
Grafted polyethylene with maleic anhydride (PE-g-MA) was used as a
compattbilizer of the systems. HOPE and its systems were evaluated: XRD,
TEM, SEM, mechanical properties (tensile and impact), HDT, DSC, TG and
fiammability (UL94HB, oxygen index (LOI) and cone calorimetry). The X-ray
diffraction showed an apparent partial intercalation and exfoliation as well as
formation of rnicrocomposite. The phase morphology of the systems obtained
from the SEM showed dispersion and distribution of clay and flame retardancy.
By TEM it was observed that the system with 1% OMMT clay showed a
predominance of exfoliation. Already the system with 3% OMMT showed partial
exfoliation and exfoliation is reducing as the clay content increased. Comparing
the mechanical properties of the HDPE to systems it was found that the elastic
modulus practically was not changed. By TG it was seen that MMT, OMMT and
RCP acted improving the thermal behavior of the nanocomposites compared to
HDPE matrix. By DSC it was observed that the presence of clay altered the
crystallinity of the matrix. The results obtained for the oxygen index revealed
that both HDPE and their systems presented flame retardant properties. By
means of the horizontal fiammability tests, it was found that the presence of 1 %
MMT clay reduced 25% the fiammability of HDPE. By cone calorimetry was
found that the system contains 9% of OMMT clay decreased by 33% the
fiammability of nanocomposites. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/3021 |
|
dc.date.accessioned |
2019-03-04T10:54:08Z |
|
dc.date.available |
2019-03-04 |
|
dc.date.available |
2019-03-04T10:54:08Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
Nanocompósitos |
|
dc.subject |
Nanocompósitos |
|
dc.subject |
Nanocomposites |
|
dc.subject |
Nanocompuestos |
|
dc.subject |
PEAD |
|
dc.subject |
Anti-chama |
|
dc.subject |
Retardante de llama |
|
dc.subject |
Flameproof |
|
dc.subject |
Argila organifilica |
|
dc.subject |
Organiphilic clay |
|
dc.subject |
Arcilla organifílica |
|
dc.subject |
Calorimetria |
|
dc.subject |
Calorimetría |
|
dc.subject |
Calorimetry |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
OLIVEIRA, Sara Verusca de. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Nanocomposites of polyethylene / bentonite clay with antichama properties. |
pt_BR |
dc.identifier.citation |
OLIVEIRA, Sara Verusca de. Nanocompósitos de polietileno/argila bentonítica com propriedades antichama. 2013. 147f. (Tese de Doutorado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2013. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/3021 |
pt_BR |