dc.creator.ID |
KOJUCH, L. R. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/3964523666390921 |
pt_BR |
dc.contributor.advisor1 |
ARAÚJO, Edcleide Maria. |
|
dc.contributor.advisor1ID |
ARAÚJO, E. M. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/1097999681102529 |
pt_BR |
dc.contributor.referee1 |
MÉLO, Tomás Jeferson Alves de. |
|
dc.contributor.referee1ID |
MÉLO, T. J. A. |
pt_BR |
dc.contributor.referee2 |
LEITE, Amanda Melissa Damião. |
|
dc.contributor.referee2ID |
LEITE, A. M. D. |
pt_BR |
dc.description.resumo |
Membranas microporosas foram obtidas a partir de nanocompósitos de
poliamida 6.6 com 1 e 3% de argila bentonítica nacional, por meio do processo
de inversão de fases. Foram utilizados dois tipos de banho cie precipitação:
banho em água destilada e banho numa solução de água destilada com ácido
fórmico. Os nanocompósitos foram obtidos a partir da técnica de intercalação
por fusão e apresentaram estrutura intercalada e/ou parcialmente esfoliada,
como indicado por DRX. Por calorimetria exploratória diferencial (DSC),
observou-se que a presença da argila não alterou significativamente as
temperaturas de fusão dos nanocompósitos, se comparados com a da
poliamida pura. As membranas obtidas foram caracterizadas por MEV, DRX,
Medidas de fluxo e Permeação ao vapor d'água. De modo geral, as
membranas apresentaram uma morfologia assimétrica, detectadas por MEVs:
uma camada seletiva e uma camada porosa, com variações na sua
microestrutura. O banho de precipitação numa solução de água + ácido
propiciou a diminuição' da camada seletiva das membranas, se comparadas
com as membranas obtidas num banho de precipitação em água. De modo
geral, as membranas com 1% de argila e banho de precipitação em água
apresentaram fluxos relativamente bons para todas as pressões utilizadas (1, 2
e 3 bar). Para as membranas obtidas a partir de um banho de precipitação
numa solução de água + ácido, obteve-se um crescimento gradual da
permeação de vapor d'agua, à medida que se aumentou o teor de argila. Para
as membranas obtidas a partir de um banho de precipitação em água, houve
uma redução expressiva na permeabilidade em relação à PA 6.6 pura, na faixa
de 66 e 48%, para as membranas com 1 e 3% de argila, respectivamente.
Portanto, membranas microporosas obtidas a partir de nanocompósitos foram
obtidas, sendo que o tipo de banho de precipitação e a quantidade de argila
influenciou nas características morfológicas e de permeabilidade das mesmas. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.title |
Membranas poliméricas obtidas a partir de nanocompósitos de PA 6.6/argila montmorilonítica pela técnica de inversão de fases. |
pt_BR |
dc.date.issued |
2013-03 |
|
dc.description.abstract |
Microporous membranes were obtained from nanocomposites of polyamide 6.6
with 1 and 3% of national bentonite clay, by phase inversion process. It was
used two kinds of precipitation bath: with distilled water and a of formic acid.
The nanocomposites were obtained from the intercalation by melting technique
and presented exfoliated and / or partially exfoliated structure as shown by
XRD. By differential scanning calorimetry (DSC), it was observed that the
presence of the clay did not significantly alter the melting temperature of the
nanocomposites when compared with the pure polyamide. The membranes
were characterized by SEM, XRD, measurements of flow and water vapor
permeation. In general, asymmetric membranes showed a morphology detected
by SEM: A selective layer and a porous layer with variations in its
microstructure. The precipitation bath with acid solution led to a decrease in the
thickness of the selective layer of the membranes compared to membranes
obtained in a precipitation bath of water. In general, the membranes with 1%
clay and water bath precipitation showed relatively good permeate flux for all
used pressures (1, 2 and 3 bar). For membranes obtained from a
precipitation bath in a acid solution gave a gradual increase in water vapor
permeation, as it increased the clay content. For membranes obtained from
a precipitation bath with water, there was a significant reduction in the
permeability in relation to the pure PA 6.6, in the range of 66 to 48% for
membranes with 1% and 3% of clay, respectively. Therefore, microporous
membranes obtained from nanocomposites were obtained, and the
precipitation bath type and the amount of clay influenced on the morphology
and permeability of the membranes. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/3024 |
|
dc.date.accessioned |
2019-03-04T11:12:28Z |
|
dc.date.available |
2019-03-04 |
|
dc.date.available |
2019-03-04T11:12:28Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Membranas poliméricas |
|
dc.subject |
Polymeric membranes |
|
dc.subject |
Nanocompósitos |
|
dc.subject |
Nanocompuestos |
|
dc.subject |
Nanocomposites |
|
dc.subject |
Poliamida |
|
dc.subject |
Polyamide |
|
dc.subject |
Polyamide |
|
dc.subject |
Argila bentonítica |
|
dc.subject |
Arcilla de bentonita |
|
dc.subject |
Bentonite clay |
|
dc.subject |
Inversão de fases |
|
dc.subject |
Inversão de fases |
|
dc.subject |
Phase inversion |
|
dc.subject |
Inversión de fase |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
KOJUCH, Luana Rodrigues. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Polymeric membranes obtained from PA 6.6 nanocomposites / montmorillonite clay by the phase inversion technique. |
pt_BR |
dc.identifier.citation |
KOJUCH, Luana Rodriges. Membranas poliméricas obtidas a partir de nanocompósitos de PA 6.6/argila montmorilonítica pela técnica de inversão de fases. 2013. 88f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2013. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/3024 |
pt_BR |