Caracterização de compósitos de polietileno de baixa densidade/atapulgita e avaliação dos efeitos do tratamento ácido da carga sobre as propriedades do compósito.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA
→
Mestrado em Engenharia Química
→
Ver item

dc.creator.ID	SILVA, M. A.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/2504013054091301	pt_BR
dc.contributor.advisor1	CARVALHO, Laura Hecker de.
dc.contributor.advisor1ID	CARVALHO, L. H.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/6358009621640820	pt_BR
dc.contributor.referee1	FRANÇA, Kepler Borges.
dc.contributor.referee2	SWARNAKAR, Ramdayal.
dc.contributor.referee3	NAVÁRRO, Rômulo Feitosa.
dc.description.resumo	As propriedades mecânicas dos compósitos de polietileno de baixa densidade com diferentes cargas, convencionais (talco e carbonato de cálcio) e não convencionais (atapulgita tratada com ácidos minerais e não tratada), foram estudadas. As propriedades avaliadas foram a resistência à tração, o módulo de flexão e a resistência ao impacto. Foram estudadas também a dureza e o grau de cristalinidade do polimero e seus compósitos. Os resultados experimentais mostraram que a atapulgita, devido ã sua constituição fibrosa, atuou como carga reforçante para o polietileno, o que foi comprovado pelo aumento na resistência à tração dos compósito com até 30%, em peso, de carga incorporada. Comparações feitas com compósitos de polietileno de baixa densidade, utilizando cargas como talco e carbonato de cálcio, classificadas como inertes, mostraram que apenas a dureza e a resistência ao impacto apresentaram um aumento, sendo que o compósito que apresentou maior energia absorvida no teste de impacto foi o de 20%, em peso, de carga (talco) incorporada. Estudou-se o efeito de tratamentos da atapulgita com os ácidos clorídrico e nítrico, e comprovou-se, após o tratamento, uma maior porosidade da carga e um aumento da resistência mecânica do compósito, atribuído ao fenómeno do "acoplamento mecânico" e maior adsorção física da carga ao polímero. O tratamento com ácido nítrico foi o que promoveu uma maior resistência mecânica aos compósitos, e o efeito da adição de cargas no polietileno mostrou que apenas para 10%, em peso, de carga incorporada houve aumento no grau de cristalinidade e que, para as demais percentagens (20 a 40%, em peso), as cargas agiram como inibidoras de cristalização.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia química
dc.title	Caracterização de compósitos de polietileno de baixa densidade/atapulgita e avaliação dos efeitos do tratamento ácido da carga sobre as propriedades do compósito.	pt_BR
dc.date.issued	1992-12
dc.description.abstract	The mechanical properties of low-density polyethylene composites densities with different conventional fillers (talc and calcium carbonate) and unconventional (atapulgite treated with mineral acids and untreated), were studied. The evaluated properties were the tensile strength, flexural strength and impact strength. The hardness and the degree of crystallinity of the polymer and its composites. The experimental results showed that atapulgite, due to its fibrous constitution, acted as a charge reinforcement for polyethylene, which was evidenced by the increase in resistance to the composite traction with up to 30% by weight of incorporated filler. Comparisons made with low density polyethylene composites using such as talc and calcium carbonate, classified as inert, have shown that only hardness and impact resistance showed an increase, being that the composite that presented the highest energy absorbed in the impact test was or 20% by weight of the filler (talc) incorporated. The effect of treatments of atapulgite with hydrochloric and nitric acids, and it was verified, after treatment, increased porosity of the load and increased resistance mechanics of the composite, attributed to the phenomenon of "mechanical coupling" and greater physical adsorption of the charge to the polymer. Treatment with nitric acid was which promoted a greater mechanical resistance to the composites, and the effect of the The addition of fillers in polyethylene showed that only 10% by weight of there was an increase in the degree of crystallinity and that, for the other percentages (20 to 40% by weight), the charges acted as inhibitors of crystallization.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/3100
dc.date.accessioned	2019-03-11T10:29:20Z
dc.date.available	2019-03-11
dc.date.available	2019-03-11T10:29:20Z
dc.type	Dissertação	pt_BR
dc.subject	Polietileno - Compósitos
dc.subject	Polietileno - Compuestos
dc.subject	Polyethylene - Composites
dc.subject	Tratamento Ácido
dc.subject	Acid Treatment
dc.subject	Tratamiento Ácido
dc.subject	Densidades do Polietileno
dc.subject	Polyethylene Densities
dc.rights	Acesso Aberto	pt_BR
dc.creator	SILVA, Maristela Alves da.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Characterization of low density polyethylene/attapulgite composites and evaluation of the effects of the acid treatment of the load on the properties of the composite.	pt_BR
dc.identifier.citation	SILVA, Maristela Alves da. Caracterização de compósitos de polietileno de baixa densidade/atapulgita e avaliação dos efeitos do tratamento ácido da carga sobre as propriedades do compósito. 1992. 114 f. (Dissertação de Mestrado em Engenharia Química), Curso de Mestrado em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba - Campus II Campina Grande - Brasil, 1992. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/3100	pt_BR