dc.description.resumo |
O concreto é um material formado pela mistura entre cimento, brita, água, agregado
graúdo e miúdo, é de extrema importância para a construção civil, com isso sendo sempre
necessário pesquisas e aprimoramentos. Uma pesquisa importante é a influência das
altas temperaturas na resistência mecânica do concreto, visto que uma edificação está
sempre suscetível a falhas, e algumas dessas falhas podem causar o incêndio, causando
prejuízos materiais e até mesmo a perda da vida humana. O objetivo desse trabalho é a
realização de um estudo para a avaliação do nível de influência que as altas temperaturas
têm sobre o concreto, com relação a propriedades mecânicas de resistência à tração e
compressão. As temperaturas consideradas foram: ambiente (27°C), 150°C, 300°C,
450°C, 600°C e 750°C, foram feitos corpos de prova para o ensaio de compressão e
tração na flexão, totalizando 6 corpos de prova para cada nível de temperatura e ensaio,
onde foi aferido que a capacidade de carga do concreto diminui com o aumento da
temperatura, até um nível de 450°C a redução da resistência a compressão e a tração
são próximas, porém na temperatura de 600°C a redução resistência do concreto quando
comprimido é 20% maior do que quando tracionado. Foi possível identificar também o
aparecimento de fissuras no objeto de ensaio, a partir da temperatura de 600°C. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia Agroalimentar - CCTA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia Civil. |
pt_BR |
dc.title |
Análise do comportamento mecânico do concreto submetido à altas temperaturas. |
pt_BR |
dc.date.issued |
2023-07-12 |
|
dc.description.abstract |
Concrete is a material formed by the mixture of cement, gravel, water, coarse and fine
aggregates. It holds tremendous importance in the construction industry, making ongoing
research and improvements essential. One crucial area of study is the influence of high
temperatures on the mechanical strength of concrete, considering that a structure is
always susceptible to failures, and some of these failures can lead to fires, causing
material losses and even loss of human life. The objective of this work is to conduct a
study to evaluate the level of influence that high temperatures have on concrete,
specifically in terms of mechanical properties related to tensile and compressive strength.
The considered temperatures were: ambient temperature (27°C), 150°C, 300°C, 450°C,
600°C, and 750°C. Test specimens were prepared for compression and flexural tensile
strength tests, resulting in six specimens for each temperature and test, amounting to a
total of 6 specimens for each temperature and test. It was observed that the load-carrying
capacity of the concrete decreases as the temperature increases. Up to a temperature of
450°C, the reduction in compressive and tensile strength is similar. However, at a
temperature of 600°C, the reduction in compressive strength is 20% greater compared to
the reduction in tensile strength. It was also possible to identify the appearance of fissures
in the test specimens starting from a temperature of 600°C. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/31135 |
|
dc.date.accessioned |
2023-08-01T17:38:20Z |
|
dc.date.available |
2023-08-01 |
|
dc.date.available |
2023-08-01T17:38:20Z |
|
dc.type |
Trabalho de Conclusão de Curso |
pt_BR |
dc.subject |
Concreto |
pt_BR |
dc.subject |
Concrete |
pt_BR |
dc.subject |
Altas temperaturas |
pt_BR |
dc.subject |
High temperatures |
pt_BR |
dc.subject |
Incêndio |
pt_BR |
dc.subject |
Fire |
pt_BR |
dc.subject |
Resistência à tração |
pt_BR |
dc.subject |
Resistance to traction |
pt_BR |
dc.subject |
Resistência à compressão |
pt_BR |
dc.subject |
Compressive strength |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SÁ, Eduardo Freitas de. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Analysis of the structural behavior of concrete submitted to high temperatures. |
pt_BR |
dc.identifier.citation |
Sá, Eduardo Freitas de. Análise do comportamento mecânico do concreto submetido à altas temperaturas. 2023. 24 f. Trabalho de Conclusão de Curso (Bacharelado em Engenharia Civil) - Centro de Ciências e Tecnologia Agroalimentar, Universidade Federal de Campina Grande, Pombal, Paraíba, Brasil, 2023. |
pt_BR |