dc.creator.ID |
BARBOSA, W. T. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/6689285779202999 |
pt_BR |
dc.contributor.advisor1 |
FOOK, Marcus Vinicius Lia. |
|
dc.contributor.advisor1ID |
FOOK, M. V. L. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/4149843752530120 |
pt_BR |
dc.contributor.referee1 |
NEVES, Gelmires de Araujo. |
|
dc.contributor.referee1ID |
NEVES, G. A. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/3167458244674160 |
pt_BR |
dc.contributor.referee2 |
SANTANA, Lisiane Navarro de Lima. |
|
dc.contributor.referee2ID |
SANTANA, L. N. L. |
pt_BR |
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/4057799848801141 |
pt_BR |
dc.description.resumo |
O objetivo deste trabalho consiste no desenvolvimento de um novo cimento
aplicado em endodontia à base de aluminato de cálcio e estrôncio, com
adequadas propriedades físicas, quimicas, mecânicas e biologicas, como: curto
tempo de cura e fácil trabalhabilidade, bem como propriedades bioativas. Os
aluminatos foram obtidos pela síntese de combustão de solução por ser um
método simples e eficaz na obtenção de materiais em nano-escala. Os reagentes
utilizados para a síntese foram o nitrato de cálcio tetrahidratado, nitrato de
alumínio nonahidratado e carbonato de estrôncio, como fontes de cálcio,
alumínio e estrôncio, respectivamente. A ureia foi utilizada como combustível e
o ácido nítrico foi utilizado para dissolução do carbonato de estrôncio em nitrato
de estrôncio. Após a síntese, os materiais foram caracterizados por Difração de
Raios X (DRX), Microscopia Eletrônica de Varredura com Emissão de Campo
(MEV-EC), Superfície específica e Tamanho de partículas. Na síntese do
aluminato de cálcio foi obtida uma única fase cristalina referente ao
heptaluminato dodecálcico (C12A7) e na síntese do aluminato de estrôncio foi
obtido o aluminato de tri-estrôncio (S3A) como fase principal, ambos aluminatos
apresentaram estrutura submicrônica com superfície específica de 1,3 e 0,2 m2
/g
e tamanho médio de partícula, após moenda, de 8,2 e 3,1 μm, respectivamente.
A seguinte etapa foi a preparação dos cimentos aluminosos de cálcio e estrôncio,
nas seguintes composições: CS1 (100% C12A7), CS2 (80%C12A7 + 20%S3A),
CS3 (60%C12A7 + 40%S3A), CS4 (40%C12A7 + 60%S3A), CS5 (20%C12A7 +
80%S3A) e CS6 (100%S3A), tendo sido analisados: radiopacidade,
trabalhabilidade com o emprego de aditivo e tempo de cura final. O cimento CS5
apresentou radiopacidade superior a 3 mm na escala de alumínio, estando em
conformidade com a norma ISO 6876-2012. Outra característica avaliada foi a
trabalhabilidade do cimento CS5 quando este foi hidratado com água (CS5A) e
com a adição de polietilenglicol 4000 (PEG) como plastificante e retardante de
cura, na seguintes composições: CS5B (20% de PEG em massa/volume), CS5C
(30% de PEG em massa/volume) e CS5D (40% de PEG em massa/volume),
onde observou-se que os cimentos hidratados com o aditivo PEG apresentaram
boa trabalhabilidade, com destaque para o cimento CS5C hidratado com 30%
em massa de PEG, com curto tempo de cura, de aproximadamente 60 minutos.
Esse cimento apresentou baixa temperatura de reação de hidratação, resistência
à compressão suficiente para a finalidade de sua aplicação, o ensaio de
biodegradação in vitro evidenciou a liberação dos íons Sr2+, Ca2+ e Al3+
,
responsáveis pelo pH alcalino do meio o que favoreceu a atividade
antimicrobiana frente a todas as cepas bacteriológicas. Como também
apresentou capacidade bioativa, e satisfatória adesão e desenvolvimento celular
in vitro. Com os resultados apresentados pode-se concluir que o cimento CS5C
torna-se muito promissor para potencial aplicação em endodontia. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Combustão |
pt_BR |
dc.title |
Desenvolvimento de cimentos á base de aluminatos de estrôncio/cálcio para endodontia. |
pt_BR |
dc.date.issued |
2019-03-12 |
|
dc.description.abstract |
The objective of this work is the development of a new cement applied in
endodontics based on calcium aluminate and strontium, with adequate physical,
chemical, mechanical and biological properties, such as: short setting time and
easy workability as well as bioactive properties. The aluminates were obtained
by the combustion synthesis of solution because it is a simple and efficient
method to obtain nanoscale materials. The reagents used for the synthesis were
calcium nitrate tetrahydrate, aluminum nitrate nonahydrate and strontium
carbonate, as sources of calcium, aluminum and strontium, respectively. Urea
was used as fuel and nitric acid was used for the dissolution of strontium
carbonate in strontium nitrate. After the synthesis, the materials were
characterized by X-ray Diffraction (XRD), Scanning Electron Microscopy with
Field Emission (SEM-FEG), Specific Surface and Particle Size. In the synthesis
of the calcium aluminate, a single crystalline phase was obtained for dodecalcium
heptaluminate (C12A7) and in the synthesis of the strontium aluminate the tri-
strontium aluminate (S3A) was obtained as the main phase, both aluminates
presented a submicron structure with specific surface area of 1,3 and 0,2 m2
/g
and average particle size, after grinding, of κ,2 and 3,1 ȝm, respectively. The
following step was the preparation of calcium and strontium aluminous cements
in the following compositions: CS1 (100% C12A7), CS2 (80%C12A7 + 20%S3A),
CS3 (60%C12A7 + 40%S3A), CS4 (40%C12A7 + 60%S3A), CS5 (20%C12A7 +
80%S3A) and CS6 (100%S3A), having been analyzed: radiopacity, workability
with the use of additive and final setting time. The CS5 cement showed
radiopacity greater than 3 mm in the aluminum scale, being in compliance with
ISO 6876-2012. Another characteristic evaluated was the workability of CS5
cement when it was hydrated with water (CS5A) and with the addition of
polyethylene glycol 4000 (PEG) as plasticizer and curing retarder in the following
compositions: CS5B (20% PEG in mass/volume), CS5C (30% PEG in
mass/volume) and CS5D (40% PEG in mass/volume), where it was observed
that the cements hydrated with the PEG additive showed good workability, CS5C
cement hydrated with 30% by mass/volume of PEG, with short setting time, of
approximately 60 minutes. This cement had low temperature of hydration
reaction, sufficient compressive strength for the purpose of its application, the in
vitro biodegradation test evidenced the release of ions Sr2+, Ca2+ and Al3+
,
responsible for the alkaline pH of the medium, which favored the antimicrobial
activity against all the bacteriological strains. It also presented bioactive capacity
and satisfactory cell adhesion and development in vitro. With the results
presented, it can be concluded that the CS5C cement becomes very promising
for potential application in endodontics. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35589 |
|
dc.date.accessioned |
2024-05-09T19:33:39Z |
|
dc.date.available |
2024-05-09 |
|
dc.date.available |
2024-05-09T19:33:39Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
Engenharia de materiais |
pt_BR |
dc.subject |
Materiais dentários |
pt_BR |
dc.subject |
Endodontia |
pt_BR |
dc.subject |
Combustão |
pt_BR |
dc.subject |
Cimento |
pt_BR |
dc.subject |
Materials engineering |
pt_BR |
dc.subject |
Dental materials |
pt_BR |
dc.subject |
Endodontics |
pt_BR |
dc.subject |
Combustion |
pt_BR |
dc.subject |
Cement |
pt_BR |
dc.subject |
Ingenieria de materiales |
pt_BR |
dc.subject |
Materiales dentales |
pt_BR |
dc.subject |
Endodoncia |
pt_BR |
dc.subject |
Combustión |
pt_BR |
dc.subject |
Cemento |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
BARBOSA, Willams Teles. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Development of cements based on aluminates strontium/calcium for endodontics. |
pt_BR |
dc.title.alternative |
Desarrollo de cementos a base de aluminatos estroncio/calcio para endodoncia. |
pt_BR |
dc.identifier.citation |
BARBOSA, Willams Teles. Desenvolvimento de cimentos á base de aluminatos de estrôncio/cálcio para endodontia. 2019. 119 fl. Tese (Doutorado em Ciência e Engenharia de Materiais) – Programa de Pós- Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2019. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35589 |
pt_BR |
dc.description.resumen |
El objetivo de este trabajo es desarrollar un nuevo cemento
aplicado en endodoncia a base de aluminato de calcio y estroncio, con
adecuadas propiedades físicas, químicas, mecánicas y biológicas, tales como: corta
tiempo de curado y fácil trabajabilidad, así como propiedades bioactivas. Tú
Los aluminatos se obtuvieron mediante síntesis de combustión en solución, ya que es un
Método sencillo y eficaz para la obtención de materiales a nanoescala. los reactivos
Para la síntesis se utilizaron nitrato de calcio tetrahidratado,
nonahidrato de aluminio y carbonato de estroncio, como fuentes de calcio,
aluminio y estroncio, respectivamente. La urea se utilizó como combustible y
Se utilizó ácido nítrico para disolver el carbonato de estroncio en nitrato.
de estroncio. Después de la síntesis, los materiales se caracterizaron por difracción.
Rayos X (XRD), microscopía electrónica de barrido por emisión de campo
(SEM-EC), Superficie específica y Tamaño de partícula. En la síntesis de
aluminato de calcio, se obtuvo una fase monocristalina haciendo referencia a la
heptaluminato de dodecalcio (C12A7) y en la síntesis de aluminato de estroncio fue
Se obtuvo aluminato de tri-estroncio (S3A) como fase principal, ambos aluminatos
presentó una estructura submicrónica con una superficie específica de 1,3 y 0,2 m2
/gramo
y tamaño medio de partícula, después de la molienda, de 8,2 y 3,1 µm, respectivamente.
El siguiente paso fue la preparación de cementos aluminosos de calcio y estroncio,
en las siguientes composiciones: CS1 (100% C12A7), CS2 (80%C12A7 + 20%S3A),
CS3 (60%C12A7 + 40%S3A), CS4 (40%C12A7 + 60%S3A), CS5 (20%C12A7 +
80%S3A) y CS6 (100%S3A), habiéndose analizado: radiopacidad,
trabajabilidad con el uso de aditivo y tiempo de curado final. cemento CS5
presentó radiopacidad mayor a 3 mm en la escala de aluminio, estando en
cumplimiento de la norma ISO 6876-2012. Otra característica evaluada fue la
trabajabilidad del cemento CS5 cuando se hidrató con agua (CS5A) y
con la adición de polietilenglicol 4000 (PEG) como plastificante y retardante de fuego
curado, en las siguientes composiciones: CS5B (20% PEG en masa/volumen), CS5C
(30% PEG en masa/volumen) y CS5D (40% PEG en masa/volumen),
donde se observó que los cementos hidratados con el aditivo PEG presentaron
buena trabajabilidad, con énfasis en cemento CS5C hidratado con 30%
en masa de PEG, con un corto tiempo de curado de aproximadamente 60 minutos.
Este cemento presentó una temperatura de reacción de hidratación baja,
compresión suficiente para el propósito de su aplicación, el
La biodegradación in vitro mostró la liberación de iones Sr2+, Ca2+ y Al3+.
,
responsable del pH alcalino del ambiente, lo que favoreció la actividad
Antimicrobiano contra todas las cepas bacteriológicas. Así como
presentó capacidad bioactiva, y adhesión y desarrollo celular satisfactorios
in vitro. Con los resultados presentados se puede concluir que el cemento CS5C
se vuelve muy prometedor para una posible aplicación en endodoncia. |