dc.contributor.advisor1 |
CASTRO, Walman Benício de. |
|
dc.contributor.advisor1ID |
Benicio DE CASTRO, Walman. |
pt_BR |
dc.contributor.advisor1ID |
CASTRO, W. B. |
pt_BR |
dc.contributor.advisor1ID |
de Castro, W. B. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/3592569966434979 |
pt_BR |
dc.contributor.referee1 |
ARAÚJO, Carlos José de. |
|
dc.contributor.referee1ID |
DE ARAÚJO, C. J. |
pt_BR |
dc.contributor.referee1ID |
De Araujo, C |
pt_BR |
dc.contributor.referee1ID |
DEARAUJO, C |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/9466801408291152 |
pt_BR |
dc.contributor.referee2 |
MACIEL, Theophilo Moura. |
|
dc.contributor.referee2ID |
MACIEL, T. M. |
pt_BR |
dc.contributor.referee2ID |
MACIEL, THEOPHILO MOURA. |
pt_BR |
dc.contributor.referee2ID |
Diego D. S. Diniz. |
pt_BR |
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/9476858938351846 |
pt_BR |
dc.description.resumo |
Este trabalho teve como finalidade estudar uma série de cinco composições
de ligas Ti50Ni50-xZrx (x = 0, 2, 5, 10 e 15 %at.) e avaliar a interferência da
substituição do níquel pelo zircônio e a influência do percentual de zircônio nas
propriedades térmicas, mecânicas e corrosivas. As ligas foram produzidas
empregando o processo de fundição Plasma Skull Push-Pull (PSPP) e estudadas
por diversas técnicas e ensaios para averiguação das características térmicas,
mecânicas e corrosivas. As ligas foram obtidas com sucesso pelo processo PSPP.
Verificou-se que a partir de 15% de zircônio a liga apresentou alta fragilidade devido
a solubilidade parcial do percentual de zircônio no níquel. De forma geral podemos
afirmar que a adição e aumento do percentual de zircônio favoreceram a formação
de fases secundárias que interferiram diretamente nas temperaturas de
transformação, na microdureza e na resistência a corrosão. A transformação da fase
B2 em fase B19' ocorre em uma única etapa e as temperaturas Mi e Ai aumentam de
2oC para 48oC e de -20oC para 93oC para as ligas TiNi50 e TiNi40Zr10,
respectivamente. A adição de zircônio ocasionou o aparecimento de partículas de
segunda fase nos limites de grão da matriz das ligas com 5,10 e 15% de zircônio e
estas fases possuem microdureza mais elevada que a fase matriz. A resistência à
corrosão aumentou de η20,23KΩ para 1007,30KΩ e a microdureza da fase matriz
346HV para 805HV para as ligas TiNi50 e TiNi40Zr10 respectivamente. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de Materiais |
pt_BR |
dc.title |
Influência do percentual de zircônio nas propriedades térmicas, mecânicas e corrosivas de ligas Ti50Ni50-xZrx com memória de forma. |
pt_BR |
dc.date.issued |
2019-07-12 |
|
dc.description.abstract |
The objective of this work was to study a series of five Ti50Ni50-x Zrx alloy
compositions (x = 0, 2, 5, 10 and 15% at.) And to evaluate the interference of nickel
substitution by zirconium and the influence of zirconium percentage on thermal,
mechanical and corrosive properties. The alloys were produced using the Plasma
Skull Push-Pull (PSPP) casting process and studied by various techniques and tests
to verify the thermal, mechanical and corrosive characteristics. The alloys were
successfully obtained by the PSPP process. It was found that from 15% of zirconium
the alloy showed high brittleness due to partial solubility of nickel zirconium
percentage. In general we can state that the addition and increase of zirconium
percentage favored the formation of secondary phases that directly affected the
transformation temperatures, microhardness and corrosion resistance. The
transformation from phase B2 to phase B19 'occurs in a single step and
temperatures Mi and Ai increase from 2oC to 48oC and from -20oC to 93oC for TiNi50
and TiNi40Zr10 alloys, respectively. The addition of zirconium caused the appearance
of second phase particles in the matrix grain boundaries of the alloys with 5.10 and
15% zirconium and these phases have higher microhardness than the matrix phase.
The corrosion resistance increased from η20.23KΩ to 1007.30KΩ and the
microhardness of the 346HV matrix phase to 805HV for TiNi50 and TiNi40Zr10 alloys
respectively. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35601 |
|
dc.date.accessioned |
2024-05-10T11:44:22Z |
|
dc.date.available |
2024-05-10 |
|
dc.date.available |
2024-05-10T11:44:22Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
Engenharia de materiais |
pt_BR |
dc.subject |
Ligas de TiNiZr |
pt_BR |
dc.subject |
Efeito de memória de forma |
pt_BR |
dc.subject |
Corrosão |
pt_BR |
dc.subject |
Microdureza |
pt_BR |
dc.subject |
Materials engineering |
pt_BR |
dc.subject |
TiNiZr alloys |
pt_BR |
dc.subject |
Effect of shape memory |
pt_BR |
dc.subject |
Corrosion |
pt_BR |
dc.subject |
Microhardness |
pt_BR |
dc.subject |
Ingenieria de materiales |
pt_BR |
dc.subject |
Aleaciones de TiNiZr |
pt_BR |
dc.subject |
Efecto de Memoria de forma |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
RAMOS, Alana Pereira. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Influence of zirconium percentage on thermal properties, mechanical and corrosive properties of Ti50Ni50-xZrx shape memory alloys. |
pt_BR |
dc.title.alternative |
Influencia del porcentaje de circonio en las propiedades térmicas. Propiedades mecánicas y corrosivas de las aleaciones con memoria de forma Ti50Ni50-xZrx. |
pt_BR |
dc.identifier.citation |
RAMOS, Alana Pereira. Influência do percentual de zircônio nas propriedades térmicas, mecânicas e corrosivas de ligas Ti50Ni50-xZrx com memória de forma. 2019. 83 fl. Tese (Doutorado em Engenharia de Materiais) - Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande, Paraíba, Brasil, 2019. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35601 |
pt_BR |
dc.description.resumen |
Este trabajo tuvo como objetivo estudiar una serie de cinco composiciones.
de aleaciones Ti50Ni50-xZrx (x = 0, 2, 5, 10 y 15 % at.) y evaluar la interferencia de
sustitución del níquel por circonio y la influencia del porcentaje de circonio en
Propiedades térmicas, mecánicas y corrosivas. Las aleaciones fueron producidas
utilizando el proceso de fundición Plasma Skull Push-Pull (PSPP) y estudiado
mediante diversas técnicas y pruebas para investigar las características térmicas,
mecánico y corrosivo. Las aleaciones se obtuvieron con éxito mediante el proceso PSPP.
Se encontró que a partir del 15% de circonio la aleación presentaba alta fragilidad debido a
la solubilidad parcial del porcentaje de circonio en níquel. En general podemos
afirman que la adición y aumento del porcentaje de circonio favoreció la formación
de fases secundarias que interfirieron directamente en las temperaturas de
transformación, microdureza y resistencia a la corrosión. La transformación de fase
B2 en la fase B19' ocurre en un solo paso y las temperaturas Mi y Ai aumentan en
2oC a 48oC y de -20oC a 93oC para las aleaciones TiNi50 y TiNi40Zr10,
respectivamente. La adición de circonio provocó la aparición de partículas de
segunda fase en los límites de grano de la matriz de aleación con 5,10 y 15% de circonio y
Estas fases tienen una microdureza mayor que la fase matriz. la resistencia a
la corrosión aumentó de η20,23 KΩ a 1007,30 KΩ y la microdureza de la fase de la matriz
346HV a 805HV para aleaciones TiNi50 y TiNi40Zr10 respectivamente. |
pt_BR |