dc.creator.ID |
SANTOS, T. T. |
pt_BR |
dc.creator.ID |
SANTOS, TIAGO T. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/7231093946602329 |
pt_BR |
dc.contributor.advisor1 |
CARVALHO, Laura Hecker de. |
|
dc.contributor.advisor1ID |
CARVALHO, L. H. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/6358009621640820 |
pt_BR |
dc.contributor.referee1 |
ARAUJO, Edcleide Maria. |
|
dc.contributor.referee1ID |
Araújo, E. M. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/1097999681102529 |
pt_BR |
dc.contributor.referee2 |
MÉLO, Tomás Jeferson Alves de. |
|
dc.contributor.referee2ID |
MÉLO, T. J. A. |
pt_BR |
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/8562091525519918 |
pt_BR |
dc.description.resumo |
Neste trabalho, nanocompósitos PBAT/argila organofílica contendo 2,5; 5,0 e
7,5%, em massa, de carga foram preparados por duas rotas: (I) mistura direta
em misturador interno, operando a 180°C por 15 minutos e velocidades de 60,
120 e 180 rpm e (II) preparação de concentrado (1:1 PBAT/argila organofilica)
processados a 180°C, 120 rpm por 15 minutos seguido de diluição com a matriz
em extrusora dupla rosca corrotacional até as concentrações desejadas.
Nanocompósitos PBAT/argila organofilica C20A preparados conforme rota (I),
foram analisados por reometria de torque e as formulações assim processadas
foram trituradas, injetadas e caracterizadas por Difração de raios-X (DRX),
Calorimetria exploratória diferencial (DSC), Termogravimetria (TG) e reometria
de placas paralelas. Concentrados PBAT/argila contendo três diferentes argilas
organofilicas (C10A, C20A e C30B) foram preparados pela rota (II). Os
concentrados foram triturados e extrusados em extrusora dupla-rosca co-
rotacional e diluídos com matriz (PBAT). A matriz pura foi processada nas
mesmas condições. Os sistemas obtidos por essa rota foram caracterizados por
DRX, DSC, TG, Análise dinâmico-mecânica (DMA), Microscopia eletrônica de
transmissão (MET) e reometria de placas paralelas. Os resultados indicam que
a condição de processamento em misturador interno que promoveu um maior
grau de mistura e melhorias nas propriedades térmicas e reológicas dos
nanocompósitos foi a 120 rpm e que, apesar de ambas as rotas gerarem
nanocompósitos com estruturas intercaladas a rota II, foi a que gerou estruturas
com maior distância interplanar basal e a um leve aumento no grau de
cristalinidade dos sistemas investigados. Nanocompósitos preparados pela rota
II apresentaram ligeiro aumento na estabilidade térmica que tende a aumentar
com o teor de argila. O módulo elástico, obtido por DMA, variou com a
concentração e foi independente do tipo de argila organofílica. A temperatura de
transição vítrea (Tg) também é independente do teor e tipo de argila. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de materiais |
pt_BR |
dc.title |
Efeito das condições de processamento nas propriedades de nanocompósitos PBAT/argilas organofílicas. |
pt_BR |
dc.date.issued |
2019-04-17 |
|
dc.description.abstract |
In this work, PBAT/organoclay nanocomposites with 2.5; 5,0 e 7,5% filler content
were prepared by two routes: (I) direct mixing in an internal mixer, operating at
180°C for 15 minutes at speeds of 60, 120 and 180 rpm, and (II) preparation of a
masterbatch (1:1 PBAT/organophilic clay) processed at 180°C, 120 rpm for 15
minutes followed by dilution with the matrix in a double screw corrotational
extruder to the desired concentrations. Nanocomposites PBAT/C20A organoclay
prepared by route (I), were analyzed by torque rheometry and the formulations
thus processed were ground, injected and characterized by X-ray Diffraction
(XRD), Differential Scanning Calorimetry (DSC), Thermogravimetry (TG) and
parallel plate rheometry. PBAT/organoclay masterbatches containing three
different organophilic clays (C10A, C20A and C30B) were prepared by route (II).
The masterbatches were ground and extruded in co-rotational twin-screw
extruder and matrix diluted to the desired concentrations. The neat matrix was
processed under the same conditions. The systems obtained by this route were
characterized by XRD, DSC, TG, Dynamic-Mechanical Analysis (DMA),
Transmission Electron Microscopy (TEM) and Parallel Plate Rheometry. Results
show the processing condition in the internal mixer that led to nanocomposites
with higher degree of mixing and better thermal and rheological properties was
at 120 rpm and that, although both routes generated nanocomposites with
intercalated structures, route II led to structures with greater basal interplanar
distance and a slight increase in the degree of crystallinity. Nanocomposites
prepared by route II displayed a slight increase in thermal stability which
increased with clay content. The elastic modulus, obtained by DMA, varied with
clay concentration and was independent of the type of organophilic clay. The
glass transition temperature (Tg) is also independent of clay content and identity. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35642 |
|
dc.date.accessioned |
2024-05-14T14:35:36Z |
|
dc.date.available |
2024-05-14 |
|
dc.date.available |
2024-05-14T14:35:36Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
PBAT |
pt_BR |
dc.subject |
Argila |
pt_BR |
dc.subject |
Nanocompósitos |
pt_BR |
dc.subject |
Processamento |
pt_BR |
dc.subject |
Propriedades |
pt_BR |
dc.subject |
Clay |
pt_BR |
dc.subject |
Nanocomposites |
pt_BR |
dc.subject |
Processing |
pt_BR |
dc.subject |
Properties |
pt_BR |
dc.subject |
Arcilla |
pt_BR |
dc.subject |
Nanocompuestos |
pt_BR |
dc.subject |
Procesando |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SANTOS, Tiago Tibério dos. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Effect of processing conditions on properties of PBAT/organophilic clay nanocomposites. |
pt_BR |
dc.title.alternative |
Efecto de las condiciones de procesamiento sobre las propiedades. de PBAT/nanocompuestos de arcilla organófila. |
pt_BR |
dc.identifier.citation |
SANTOS, Tiago Tibério dos. Efeito das condições de processamento nas propriedades de nanocompósitos de
PBAT/argilas organofílicas. 2019. 142 fl. Tese (Doutorado em Ciência e Engenharia de Materiais) – Programa de Pós- Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2019. Disponível em:http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35642 |
pt_BR |
dc.description.resumen |
En este trabajo, se utilizaron nanocompuestos de PBAT/arcilla organófila que contienen 2,5; 5.0 y
Se preparó un 7,5%, en masa, de carga mediante dos rutas: (I) mezcla directa
en batidora interna, funcionando a 180°C durante 15 minutos y velocidades de 60,
120 y 180 rpm y (II) preparación de concentrado (1:1 PBAT/arcilla organofílica)
procesado a 180°C, 120 rpm durante 15 minutos seguido de dilución con la matriz
en una extrusora co-rotacional de doble tornillo hasta alcanzar las concentraciones deseadas.
Nanocompuestos de arcilla organófila PBAT/C20A preparados según la ruta (I),
fueron analizados por reometría de torque y las formulaciones así procesadas
fueron triturados, inyectados y caracterizados por Difracción de Rayos X (DRX),
Calorimetría diferencial de barrido (DSC), termogravimetría (TG) y reometría
de placas paralelas. PBAT/concentrados de arcilla que contienen tres arcillas diferentes
organófilos (C10A, C20A y C30B) se prepararon por la ruta (II). Tú
Los concentrados fueron triturados y extruidos en una extrusora de doble tornillo con
rotacional y diluido con matriz (PBAT). La matriz pura se procesó en
mismas condiciones. Los sistemas obtenidos por esta vía se caracterizaron por
DRX, DSC, TG, Análisis dinámico-mecánico (DMA), Microscopía electrónica
transmisión (MET) y reometría de placas paralelas. Los resultados indican que
la condición de procesamiento en un mezclador interno que promovió una mayor
grado de mezcla y mejoras en las propiedades térmicas y reológicas de
nanocompuestos fue a 120 rpm y que, a pesar de que ambas rutas generaron
nanocompuestos con estructuras intercaladas, la ruta II fue la que generó estructuras
con mayor distancia interplanar basal y un ligero aumento en el grado de
cristalinidad de los sistemas investigados. Nanocompuestos preparados por la ruta.
II mostró un ligero aumento en la estabilidad térmica, que tiende a aumentar
con contenido de arcilla. El módulo elástico, obtenido por DMA, varió con la
concentración y fue independiente del tipo de arcilla organófila. la temperatura de
La transición vítrea (Tg) también es independiente del contenido y tipo de arcilla. |
pt_BR |