dc.creator.ID |
ALMEIDA, Brunna Lima de. |
pt_BR |
dc.creator.ID |
MEDEIROS, Brunna Lima de Almeida Victor. |
pt_BR |
dc.creator.ID |
MEDEIROS, B. L. A. V. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/9966295997259863 |
pt_BR |
dc.contributor.advisor1 |
NEVES, Gelmires de Araújo. |
|
dc.contributor.advisor1ID |
NEVES, G. A. |
pt_BR |
dc.contributor.advisor1ID |
Neves, G. A. |
pt_BR |
dc.contributor.advisor1ID |
G. A. Neves. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/3167458244674160 |
pt_BR |
dc.contributor.advisor2 |
BARBOSA, Normando Perazzo. |
|
dc.contributor.advisor2ID |
BARBOSA, N. P. |
pt_BR |
dc.contributor.advisor2ID |
BARBOSA, NORMANDO PERAZZO. |
pt_BR |
dc.contributor.advisor2ID |
BARBOSA, N.P. |
pt_BR |
dc.contributor.advisor2Lattes |
http://lattes.cnpq.br/6420367558476872 |
pt_BR |
dc.contributor.referee1 |
MENEZES, Romualdo Rodrigues. |
|
dc.contributor.referee1ID |
MENEZES, R. R. |
pt_BR |
dc.contributor.referee1ID |
Menezes, R. R. |
pt_BR |
dc.contributor.referee1ID |
Menezes, Romualdo R. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/1169292996645931 |
pt_BR |
dc.contributor.referee2 |
SEVERO, Cibele Guimarães Silva. |
|
dc.description.resumo |
A geração de resíduos no setor industrial é uma problemática que vem sendo
acompanhada pelo crescimento econômico do setor. Apresentar soluções e
alternativas que minimizem o impacto ambiental causado pela forma incorreta da
destinação final destes resíduos tem sido cada vez mais uma preocupação dos
produtores. Por meio de pesquisas sobre materiais não-convencionais, o setor da
construção civil tem conseguido absorver essa demanda por alternativas sustentáveis.
Esta pesquisa teve como objetivo analisar as propriedades mecânicas, durabilidade e
microestrutura de argamassa de revestimento produzida com a incorporação de
resíduos provenientes da indústria de beneficiamento de Scheelita. A fim de identificar
os potenciais de uso das matérias-primas alternativas, realizou-se a caracterização
deste resíduo através das seguintes técnicas: granulometria, massa específica real e
unitária, difração de raio X, termogravimetria, análise química por fluorescência de
raios x e espectrometria por absorção atômica. Após os ensaios de caracterização,
foram definidos os traços, e com os melhores resultados de desempenho mecânica
destes traços foram determinadas as seguintes propriedades: absorção de água,
potencial de aderência a tração, durabilidade pelos métodos de molhagem e secagem.
A reação álcali-agregado foi investigada por teste de expansão de barra pelo método
acelerado e por meio da análise de imagens obtidas por microscopia eletrônica de
varredura (MEV) e por espectroscopia por energia dispersiva (EDS). Nos resultados
do ensaio de expansão de barras, foram identificadas expansões que indicavam
reatividade do resíduo. As imagens obtidas por MEV e EDS não revelaram a presença
de formação de nenhum gel deletério, porém mostraram a ocorrência de fissuras que
corroboram com os resultados obtidos no ensaio de expansão. A ausência do gel
sugere uma reação do tipo álcali-carbonato, devido a forte presença de calcita nas
amostras. Assim, foi possível concluir que o resíduo pode apresentar reatividade com
os componentes do cimento, podendo ser utilizado como substituto da areia normal
na produção de argamassa de revestimento, desde que o cimento utilizado na
argamassa possa inibir essas reações. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de Materiais |
pt_BR |
dc.title |
Argamassas produzidas com resíduo de scheelita: propriedades mecânicas, durabilidade e microestrutura. |
pt_BR |
dc.date.issued |
2019-04-17 |
|
dc.description.abstract |
The generation of waste in the industrial sector is a problem that has been followed by
the economic growth of the sector. Presenting solutions and alternatives that minimize
the environmental impact caused by the incorrect way of disposal of these wastes has
been increasingly a concern of the producers. Through research on non-conventional
materials, the construction industry has been able to absorb this demand for
sustainable alternatives. This research had as objective to analyze the mechanical
properties and durability of coating mortar produced with the incorporation of residues
from the Scheelite beneficiation industry. In order to identify the potentials for the use
of alternative raw materials, this residue was characterized by the following techniques:
granulometry, specific and unit mass, X-ray diffraction, thermogravimetry, X-ray
fluorescence chemical analysis and spectrometry by absorption. After the
characterization tests, compositions were defined and, with the best results of
mechanical performance of these compositions, were determined the following
properties: water absorption, traction adhesion potential, durability by wet and dry
cycles method. The alkali-aggregate reaction was investigated by the bar expansion
test by the accelerated method and through analysis of images obtained by scanning
electron microscopy (SEM) and by dispersive energy spectroscopy (EDS). In the
results of the bar expansion test, expansions were identified that indicated residue
reactivity. The images obtained by MEV and EDS did not reveal the presence of
formation of any deleterious gel, but they showed the occurrence of cracks that
corroborate with the results obtained in the expansion test. The absence of the gel
suggests an alkali-carbonate reaction due to the strong presence of calcite in the
samples. Thus, it was possible to conclude that the residue can presents reactivity with
the cement components and can be used as a substitute for normal sand in the
production of coating mortar, provided that the cement used in the mortar can inhibit
these reactions. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35657 |
|
dc.date.accessioned |
2024-05-15T17:12:36Z |
|
dc.date.available |
2023-05-15 |
|
dc.date.available |
2024-05-15T17:12:36Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
Reciclagem |
pt_BR |
dc.subject |
Resíduos Industriais |
pt_BR |
dc.subject |
Agregados |
pt_BR |
dc.subject |
Reatividade |
pt_BR |
dc.subject |
Recycling |
pt_BR |
dc.subject |
Industrial Waste |
pt_BR |
dc.subject |
Aggregates |
pt_BR |
dc.subject |
Reactivity |
pt_BR |
dc.subject |
Reciclaje |
pt_BR |
dc.subject |
Residuos industriales |
pt_BR |
dc.subject |
Agregados |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
MEDEIROS, Brunna Lima de Almeida Victor. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Mortars produced with scheelite residue: mechanical properties, durability and microstructure. |
pt_BR |
dc.title.alternative |
Morteros elaborados con residuos de scheelita: propiedades mecánicas, durabilidad y microestructura. |
pt_BR |
dc.identifier.citation |
MEDEIROS, Brunna Lima de Almeida Victor. Argamassas produzidas com resíduo de scheelita: propriedades mecânicas, durabilidade e microestrutura. 2019. 100 fl. Tese (Doutorado em Ciência e Engenharia de Materiais) – Programa de Pós- Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2019. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35657 |
pt_BR |
dc.description.resumen |
La generación de residuos en el sector industrial es un problema que se ha venido
acompañado del crecimiento económico del sector. Presentar soluciones y
alternativas que minimicen el impacto ambiental causado por la forma incorrecta de
El destino final de estos residuos se ha convertido cada vez más en una preocupación para
productores. A través de la investigación de materiales no convencionales, el
La construcción civil ha logrado absorber esta demanda de alternativas sostenibles.
Esta investigación tuvo como objetivo analizar las propiedades mecánicas, durabilidad y
Microestructura de mortero de revestimiento producido con la incorporación de
residuos de la industria procesadora de Scheelita. Para identificar
del potencial uso de materias primas alternativas, se realizó la caracterización
de este residuo mediante las siguientes técnicas: granulometría, masa específica real y
unidad unitaria, difracción de rayos X, termogravimetría, análisis químico por fluorescencia de
Rayos X y espectrometría de absorción atómica. Después de las pruebas de caracterización,
Se definieron las características y con los mejores resultados de desempeño mecánico.
A partir de estos rasgos se determinaron las siguientes propiedades: absorción de agua,
potencial de adherencia a la tracción, durabilidad mediante métodos de humectación y secado.
La reacción álcali-agregado se investigó mediante la prueba de expansión de barra utilizando el método
acelerada y mediante el análisis de imágenes obtenidas por microscopía electrónica de
escaneo (SEM) y espectroscopia de dispersión de energía (EDS). en los resultados
de la prueba de expansión de la barra, se identificaron expansiones que indicaban
reactividad de los residuos. Las imágenes obtenidas por SEM y EDS no revelaron la presencia
formación de gel no dañino, pero sí mostraron la aparición de fisuras que
corroborar los resultados obtenidos en la prueba de expansión. La ausencia de gel
sugiere una reacción de tipo álcali-carbonato, debido a la fuerte presencia de calcita en el
muestras. Así, se pudo concluir que el residuo puede presentar reactividad con
los componentes del cemento, y se puede utilizar como sustituto de la arena normal.
en la producción de mortero de revestimiento, siempre y cuando el cemento utilizado en el
El mortero puede inhibir estas reacciones. |
pt_BR |