dc.creator.ID |
SOARES, R.L. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/0494374289705105 |
pt_BR |
dc.contributor.advisor1 |
CASTRO, Walman Benício de. |
|
dc.contributor.advisor1ID |
CASTRO, W. B. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/3592569966434979 |
pt_BR |
dc.contributor.referee1 |
MACIEL, Theophilo Moura. |
|
dc.contributor.referee1ID |
MACIEL, T. M. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/9476858938351846 |
pt_BR |
dc.contributor.referee2 |
AMORIM JUNIOR, Wanderley Ferreira de. |
|
dc.contributor.referee2ID |
AMORIM JÚNIOR, W. F. |
pt_BR |
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/8131607733881361 |
pt_BR |
dc.description.resumo |
O presente estudo teve por objetivo central a obtenção de ligas Ni50Ti50-XHfX .at%
com EMF por meio de três tipos de processamentos: ( i ) fundição ao arco de plasma
(método SPP - Skull Push-Pull) na câmera EDG Discovery All Metal; ( ii )
solidificação rápida pelo método melt-spinning; ( iii ) fusão ao arco elétrico (arc
melting). Depois, segue-se a caracterização térmica (por meio da técnica DSC) e
microestrutural (por efeito dos ensaios DRX, MO e MEV/EDS). Na caracterização
térmica foram registradas e discutidas as temperaturas de transformação [TTs],
fluxos de calor [W/g], densidades energéticas [J/g] e histereses térmicas [ΔP e ΔT].
Esses resultados foram correlacionados com as análises qualitatitavas e
quantitativas de fases que foram detectadas por meio de DRX nas 5 composições
substitucionais estudadas (Hf = 8, 11, 14, 17 e 20 .at%). O método Rietveld foi usado
para fazer refinamento de estrutura e determinação de variáveis tais quais
densidade específica, percentual de fases, parâmetros de rede [a b c; α ȕ Ȗ],
indexação de planos cristalográficos (h k ), cálculo do grau relativo de cristalinidade
[Xc] e percentual amorfo, além de mensurar as composições químicas das fases
observadas. Com base em regressões não-lineares, os resultados dos experimentos
de difração de raios X foram ainda utilizados como ferramenta estatística para
estabelecer uma relação matemática entre a distância interplanar [d, Å] & fração de
identificação cristalina 1/d2
com o ângulo de Bragg [βș, o]. Posteriormente, as
amostras embutidas à frio foram atacadas quimicamente para observação por meio
de microscopia óptica (MO) e microscopia eletrônica de varredura (MEV) a fim de se
observar aspectos superficiais, texturas, contornos e tamanhos de grão (largura,
comprimento, perímetro e área). A técnica EDS foi usada para determinação da
percentagem atômica (.at%) dos elementos das ligas em áreas específicas.
Demonstrou-se nesse trabalho que apesar das ligas ricas em Ni terem sido
preparadas com a mesma metodologia, mesmos materiais e composições nominais,
os resultados térmicos e microestruturais foram considerados bem distintos, com
peculiaridades que direcionam a discussão individualizada em cada um dos 3
processamentos. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de materiais |
pt_BR |
dc.title |
Caracterização térmica e estrutural de ligas Ni50Ti50-XHfX .at% com efeito memória de forma. |
pt_BR |
dc.date.issued |
2019-02-28 |
|
dc.description.abstract |
The objective of the present study was to obtain Ni50Ti50-XHfX .at% alloys with EMF by
means of three types of processes: (i) plasma arc casting (SPP method) on EDG
Discovery camera All Metal ; (ii) fast solidification by the melt spinning method; (iii)
arc melting. Then, it continues with the thermal characterization (by means of the
DSC technique) and microstructural characterization (by the XRD, OM and SEM/EDS
tests). In the thermal characterization were recorded and discussed the
transformation temperatures [TTs], heat flows [W/g], energy densities [J/g] and
thermal hystereses [ΔP and ΔT]. These results were correlated with qualitative and
quantitative phase analyzes that was detected by XRD in the 5 substituting
compositions studied (Hf = 8, 11, 14, 17 and 20 .at%). The Rietveld method was
used to make structure refinement and to determinate the variables such as specific
density, percentage of phases, network parameters [a b c; α ȕ Ȗ], indexing of
crystallographic planes (h k ), calculation of the relative degree of crystallinity [Xc]
and amorphous percentage, in addition to measuring the chemical compositions of
the observed phases. Based on non-linear regressions, the results of the X-ray
diffraction experiments were also used as a statistical tool to establish a
mathematical relationship between the interplanar distance [d, Å] & crystalline
identification fraction 1/d2
with the Bragg angle [2ș, o]. Afete that, the cold-embedded
samples were chemically attacked by optical microscopy (OM) and scanning electron
microscopy (SEM) with the objetive to observe surface aspects, textures, contours
and grain sizes (width, length, perimeter and area). The EDS technique was used to
determine the atomic percentage (.at%) of the elements of the alloys in specific
areas. It was demonstrated in this work that although Ni-rich alloys were prepared
using the same methodology, materials and nominal compositions, the thermal and
microstructural results were considered very distinct, with peculiarities that direct us
to the individualized discussion in each of the 3 processes. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35685 |
|
dc.date.accessioned |
2024-05-16T13:48:24Z |
|
dc.date.available |
2024-05-16 |
|
dc.date.available |
2024-05-16T13:48:24Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
Arco elétrico |
pt_BR |
dc.subject |
Fusão ao arco de plasma |
pt_BR |
dc.subject |
Liga de memória de forma |
pt_BR |
dc.subject |
Melt-spinning |
pt_BR |
dc.subject |
Electric arc |
pt_BR |
dc.subject |
Plasma arc fusion |
pt_BR |
dc.subject |
Alloy memory form |
pt_BR |
dc.subject |
Melt-spinning |
pt_BR |
dc.subject |
Arco eléctrico |
pt_BR |
dc.subject |
Fusión por arco de plasma |
pt_BR |
dc.subject |
Memoria de aleación molde |
pt_BR |
dc.subject |
Hilado fundido |
pt_BR |
dc.subject |
Ni-Ti-Hf |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SOARES, Roniere Leite. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Thermal and structural characterization of Ni50Ti50-XHfX .at% alloys with shape memory effect. |
pt_BR |
dc.title.alternative |
Caracterización térmica y estructural de Aleaciones Ni50Ti50-XHfX .at% con efecto memoria de forma. |
pt_BR |
dc.identifier.citation |
SOARES,Roniere Leite. Caracterização térmica e estrutural de ligas Ni50Ti50-XHfX .at% com efeito memória de forma. 2019. 380 fl.Tese (Doutorado em Ciência e Engenharia de Materiais) – Programa de Pós- Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2019. Disponível em:http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35685 |
pt_BR |
dc.description.resumen |
El objetivo principal del presente estudio fue obtener aleaciones Ni50Ti50-XHfX .at%
con EMF a través de tres tipos de procesamiento: (i) fundición por arco de plasma
(SPP - método Skull Push-Pull) en la cámara EDG Discovery All Metal; (ii)
solidificación rápida mediante el método de hilado en fusión; (iii) fusión al arco eléctrico (arco
derritiendo). Luego sigue la caracterización térmica (utilizando la técnica DSC) y
microestructural (debido a los efectos de las pruebas XRD, MO y SEM/EDS). En caracterización
temperaturas de transformación térmica [TTs],
flujos de calor [W/g], densidades de energía [J/g] e histéresis térmica [ΔP y ΔT].
Estos resultados se correlacionaron con resultados cualitativos y
Fases cuantitativas que se detectaron mediante XRD en las 5 composiciones.
variables sustitucionales estudiadas (Hf = 8, 11, 14, 17 y 20 .at%). Se utilizó el método Rietveld.
para refinar la estructura y determinar variables como
densidad específica, porcentaje de fases, parámetros de red [a b c; α ȕ Ȗ],
indexación de planos cristalográficos (h k), cálculo del grado relativo de cristalinidad
[Xc] y porcentaje amorfo, además de medir las composiciones químicas de las fases
observado. Basado en regresiones no lineales, los resultados de los experimentos.
La difracción de rayos X también se utilizó como herramienta estadística para
establecer una relación matemática entre la distancia interplanar [d, Å] y la fracción de
identificación cristalina 1/d2
con el ángulo de Bragg [βș, o]. Posteriormente, el
Las muestras incluidas en frío se grabaron químicamente para su observación utilizando
microscopía óptica (OM) y microscopía electrónica de barrido (SEM) para
observar aspectos de la superficie, texturas, contornos y tamaños de grano (ancho,
longitud, perímetro y área). Se utilizó la técnica EDS para determinar la
porcentaje atómico (.at%) de elementos de aleación en áreas específicas.
En este trabajo se demostró que aunque las aleaciones ricas en Ni han sido
elaborados con la misma metodología, mismos materiales y composiciones nominales,
Los resultados térmicos y microestructurales se consideraron muy diferentes, con
peculiaridades que dirigen la discusión individualizada en cada uno de los 3
Procesando. |
pt_BR |