dc.creator.ID |
CARVALHO, R. S. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/6145935752794997 |
pt_BR |
dc.contributor.advisor1 |
SANTANA, Lisiane Navarro de Lima. |
|
dc.contributor.advisor1ID |
SANTANA, L. N. L. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/4057799848801141 |
pt_BR |
dc.contributor.advisor2 |
LIRA, Hélio de Lucena. |
|
dc.contributor.advisor2ID |
LIRA, H. L. |
pt_BR |
dc.contributor.advisor2Lattes |
http://lattes.cnpq.br/5548799845411781 |
pt_BR |
dc.contributor.referee1 |
MENEZES, Romualdo Rodrigues. |
|
dc.contributor.referee1ID |
MENEZES, R. R. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/1169292996645931 |
pt_BR |
dc.contributor.referee2 |
SILVA, Valmir José da. |
|
dc.contributor.referee2ID |
SILVA, V. J. |
pt_BR |
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/1004326748734018 |
pt_BR |
dc.description.resumo |
Os materiais cerâmicos estão presentes em muitas aplicações de componentes
eletrônicos, destacando-se a mulita e os compósitos à base de mulita. Este trabalho
teve como objetivo estudar formulações contendo aluminossilicatos e alumina
visando obter composições adequadas para aplicações dielétricas. Inicialmente, os
precursores caulim, ball clay e alumina foram submetidos às caracterizações:
química, mineralógica e granulométrica. A partir da composição química de cada foi
definida a quantidade dos componentes nas massas cerâmicas. Foram produzidos
corpos de prova ((50 mm x 15 mm x 5 mm) (50 mm x 3 mm)) por prensagem uniaxial
a 19,6 MPa. Os espécimes foram secos à 110oC e sinterizados nas temperaturas de
1400, 1450 e 1500°C, com taxa de aquecimento de 5°C/min e patamar de queima
de 60 minutos. Posteriormente, estes foram submetidos a caracterizações físico-
químicas, mecânicas e dielétricas. A constante dielétrica relativa (ɛr) e tangente de
perdas (tan į) foram avaliadas para as frequências de 0,1 kHz, 1 kHz, 10 kHz e 100
kHz à temperatura ambiente. Foi observada a cristalização majoritária da fase mulita
para a faixa de temperatura estudada, com morfologia na forma de agulhas.
Composições contendo maior teor de fundentes apresentaram menor porosidade
(~1,84) e absorção de água (0,74) e melhor resistência à flexão (~ 66 MPa). Os
valores de constante dielétrica foram próximos aos da mulita (İr = 3,5 a ~ 4,5) na
frequência de 1 kHz, para as composições sinterizadas à 1400°C. Menores perdas
dielétricas (tan į ~0,01) foram observadas à 1400-1500°C a 100 kHz. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de materiais |
pt_BR |
dc.title |
Composições á base de aluinissilicatos e alumina para aplicações dielétricas. |
pt_BR |
dc.date.issued |
2019-10-09 |
|
dc.description.abstract |
The ceramic materials are present in many applications of electronic components,
highlighting mullite and mullite-based composites. The objective of this work was to
study formulations containing aluminosilicates and alumina in order to obtain
compositions suitable for dielectric applications. Initially, the precursors kaolin, ball
clay and alumina were submitted to the characterizations: chemical, mineralogical
and granulometric, and from the chemical composition it was defined the quantity of
components in the masses. Specimens were produced ((50 mm x 15 mm x 5 mm)
(50 mm x 3 mm)) by uniaxial pressing to 19, 6 MPa. The specimens were dried at
110 oC and sintered at temperatures of 1400, 1450 and 1500 °C, with heating rate of
5 °C/min and firing level of 60 minutes. Subsequently, the specimens were submitted
to the characterizations: physicochemical, mechanical and dielectric. The relative
dielectric constant (İr) and the tangent of losses (tan į) were evaluated for the
frequencies of 0.1 kHz, 1 kHz, 10 kHz and 100 kHz at room temperature. It was
observed the majority crystallization of the mullite phase for the studied temperature
range, with morphology in the form of needles. Compositions containing higher
content of fluxes presented lower porosity (~ 1.84) and water absorption (~0.74) and
better flexural strength (~ 66 MPa). The dielectric constant values were close to
those of mullite (İr = ~ 3,5 to ~ 4,5) in the frequency of 1 kHz, for the compositions
sintered at 1400 °C. Lower dielectric losses (tan į ~ 0.01) were observed at 1400-
1500°C and 100 kHz. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35694 |
|
dc.date.accessioned |
2024-05-16T19:46:48Z |
|
dc.date.available |
2024-05-16 |
|
dc.date.available |
2024-05-16T19:46:48Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Aluminossilicatos |
pt_BR |
dc.subject |
Alumina |
pt_BR |
dc.subject |
Mulita |
pt_BR |
dc.subject |
Constante dielétrica |
pt_BR |
dc.subject |
Tangente de perdas |
pt_BR |
dc.subject |
Aluminosilicates |
pt_BR |
dc.subject |
Dielectric constant |
pt_BR |
dc.subject |
Tangent of losses |
pt_BR |
dc.subject |
Tangente de perdidas |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
CARVALHO, Roberta Sarmento. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Compositions based on aluminum silicates and alumina for dielectric applications. |
pt_BR |
dc.title.alternative |
Composiciones a base de silicatos de aluminio y alúmina para Aplicaciones dieléctricas. |
pt_BR |
dc.identifier.citation |
CARVALHO,Roberta Sarmento.Composições á base de aluinissilicatos e alumina para aplicações dielétricas. 2019. 68 fl.Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande, Paraíba, Brasil, 2019. Disponível em:http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35694 |
pt_BR |
dc.description.resumen |
Los materiales cerámicos están presentes en muchas aplicaciones de componentes.
electrónica, destacando la mullita y los compuestos a base de mullita. Este trabajo
destinado a estudiar formulaciones que contienen aluminosilicatos y alúmina.
con el objetivo de obtener composiciones adecuadas para aplicaciones dieléctricas. Inicialmente, el
Se caracterizaron precursores de caolín, arcilla bola y alúmina:
químicos, mineralógicos y granulométricos. Según la composición química de cada uno.
Se define la cantidad de componentes en las masas cerámicas. fueron producidos
probetas ((50 mm x 15 mm x 5 mm) (50 mm x 3 mm)) mediante prensado uniaxial
a 19,6 MPa. Las muestras se secaron a 110oC y se sinterizaron a temperaturas
1400, 1450 y 1500°C, con una velocidad de calentamiento de 5°C/min y umbral de combustión
60 minutos. Posteriormente, estos fueron sometidos a castigos físicos.
químicos, mecánicos y dieléctricos. La constante dieléctrica relativa (ɛr) y la tangente de
Se evaluaron pérdidas (tan į) para frecuencias de 0,1 kHz, 1 kHz, 10 kHz y 100 kHz.
kHz a temperatura ambiente. Se observó una cristalización importante de la fase de mullita.
para el rango de temperatura estudiado, con morfología en forma de aguja.
Las composiciones que contenían un mayor contenido de fundente mostraron una menor porosidad.
(~1,84) y absorción de agua (0,74) y mejor resistencia a la flexión (~66 MPa). Tú
Los valores de la constante dieléctrica fueron cercanos a los de la mullita (İr = 3,5 a ~ 4,5) en
frecuencia de 1 kHz, para composiciones sinterizadas a 1400°C. Menores pérdidas
Los valores dieléctricos (tan į ~0,01) se observaron a 1400-1500°C a 100 kHz. |
pt_BR |