dc.creator.ID |
MEDEIROS, P. S. S. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/2143415252503489 |
pt_BR |
dc.contributor.advisor1 |
SANTANA, Lisiane Navarro de Lima. |
|
dc.contributor.advisor1ID |
SANTANA, L. N. L. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/4057799848801141 |
pt_BR |
dc.contributor.advisor2 |
NEVES., Gelmires de Araújo. |
|
dc.contributor.advisor2ID |
NEVES, G. A. |
pt_BR |
dc.contributor.advisor2Lattes |
http://lattes.cnpq.br/3167458244674160 |
pt_BR |
dc.contributor.referee1 |
LIRA, Hélio de Lucena. |
|
dc.contributor.referee1ID |
LIRA, H. L. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/5548799845411781 |
pt_BR |
dc.contributor.referee2 |
MENEZES, Romualdo Rodrigues. |
|
dc.contributor.referee2ID |
MENEZES, R. R. |
pt_BR |
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/1169292996645931 |
pt_BR |
dc.description.resumo |
Durante a extração e o beneficiamento de quartzito grandes quantidades de resíduo
são produzidos, o qual apresenta óxidos que estão presentes nas principais
matérias-primas utilizadas em massas da cerâmica tradicional. Dentro desse
contexto, este trabalho objetiva avaliar as propriedades tecnológicas de peças
cerâmicas obtidas por massas utilizadas na produção de grés sanitárias, contendo
resíduo de quartzito, pela substituição parcial do feldspato. Inicialmente foi realizado
um estudo de caracterização físico-mineralógica do resíduo e das matérias-primas
convencionais que fazem parte da composição da massa, que são: argila, feldspato,
quartzo e caulim. As caracterizações foram realizadas através das seguintes
técnicas: análise granulométrica por difração a laser, difração de raios X,
fluorescência de raios X, análise térmica. Foram formuladas composições variando-
se a quantidade do resíduo, substituindo o feldspato em 10, 15, 20 e 25% em peso.
As propriedades reológicas das barbotinas foram analisadas, enfatizando também o
pH. O processo de colagem foi empregado na etapa de conformação, após secagem
(110oC), foi realizado o tratamento térmico na temperatura de 1200°C, em dois ciclos
de queima. Para caracterização foram realizados os seguintes testes: análise visual
de cor após queima, fusibilidade, absorção de água, perda ao fogo, porosidade,
massa específica aparente, retração de queima, coeficiente de expansão térmica,
resistência à flexão, dureza vickers e módulo de elasticidade. A microestrutura foi
avaliada por microscopia eletrônica de varredura e análise por difração de raios X.
Os resultados mostraram que as características reológicas das suspensões foram
adequadas, quando da substituição parcial do feldspato pelo resíduo de quartzito em
até 25% em peso, para o processo de colagem. Os espécimes produzidos a partir de
composições contendo resíduo de quartzito, na faixa de 10 - 25%, apresentaram
valores de resistência à flexão superiores a 35MPa, absorção de água de
aproximadamente 0,5% e retração linear após queima abaixo de 12%, valores
dentro da faixa recomenda para a fabricação de grés sanitários. A presença do
resíduo de quartzito não alterou as fases cristalinas presentes nas peças
sinterizadas, foi observado a presença de quartzo e mulita. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de materiais |
pt_BR |
dc.title |
Efeito do resíduo de quartzito nas propriedades tecnológicas de peças cerâmicas obtidas a partir de massas para fabricação de grés sanitários. |
pt_BR |
dc.date.issued |
2019-03-15 |
|
dc.description.abstract |
During the extraction and processing of quartzite large amounts of waste are
produced, which presents oxides that are present in the main raw materials used in
traditional ceramic masses. In this context, this work investigated the technological
properties of ceramic pieces obtained by masses used in the production of sanitary
stoneware, containing quartzite residue, by the partial replacement of feldspar.
Initially, a study of the physical and mineralogical characterization of the residue and
of the conventional raw materials, clay, feldspar, quartz and kaolin, of the
composition of the mass were carried out. The characterization was carried out using
the following techniques: granulometric analysis by laser diffraction, X-ray diffraction,
X-ray fluorescence, thermal analysis. Compositions have been formulated by varying
the amount of the residue, replacing the feldspar at 10, 15, 20 and 25% by weight.
The rheological properties of the slips were analyzed, emphasizing also the pH. The
slip casting process was used in the conformation, the specimes were dry (110o) and
sintered at the temperature of 1200 ° C, in two firing cycles. For characterization the
following tests were performed: color variation after firing, fusibility, water absorption,
loss on ignition, porosity, apparent specific mass, firing retraction, coefficient of
thermal expansion, flexural strength, vickers hardness and modulus of elasticity. The
microstructure was evaluated by scanning electron microscopy and X-ray diffraction
analysis. The results showed that the rheological characteristics of the suspensions
were adequate when the partial replacement of the feldspar by the quartzite residue
was used for the bonding process. The specimes produced from compositions
containing quartzite residue, in the range of 10 – 25%, presented the flexural strength
values were greater than 35MPa, water absorption nearly 0.5% and linear retraction
after burning below 12%, values within the range required for the manufacture of
sanitary products. The presence of the quartzite residue did not alter the crystalline
phases in the sintered pieces, was observed only the presence of quartz and mullite. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35766 |
|
dc.date.accessioned |
2024-05-23T12:22:34Z |
|
dc.date.available |
2024-05-23 |
|
dc.date.available |
2024-05-23T12:22:34Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
Cerâmica tradicional |
pt_BR |
dc.subject |
Resíduo de quartzito |
pt_BR |
dc.subject |
Louça sanitária |
pt_BR |
dc.subject |
Traditional pottery |
pt_BR |
dc.subject |
Quartzite Waste |
pt_BR |
dc.subject |
Sanitary ware |
pt_BR |
dc.subject |
Residuos de cuarcita |
pt_BR |
dc.subject |
Artículos sanitarios |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
MEDEIROS, Paula Simone Soares de. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Effect of quartzite residue on technological properties of ceramic pieces obtained from masses for manufacturing of sanitary stoneware. |
pt_BR |
dc.title.alternative |
Efecto del residuo de cuarcita sobre las propiedades tecnológicas. de piezas cerámicas obtenidas a partir de masas para su fabricación de gres sanitario. |
pt_BR |
dc.identifier.citation |
MEDEIROS, Paula Simone Soares de. Efeito do resíduo de quartzito nas propriedades tecnológicas de peças cerâmicas obtidas a partir de massas para fabricação de grés sanitários. 2019. 114 fl. Tese (Doutorado em Ciência e Engenharia de Materiais) – Programa de Pós- Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2019. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35766 |
pt_BR |
dc.description.resumen |
Durante la extracción y procesamiento de cuarcita se generan grandes cantidades de residuos.
se producen, los cuales presentan óxidos que están presentes en la principal
Materias primas utilizadas en las masas cerámicas tradicionales. Dentro de este
En este contexto, este trabajo tiene como objetivo evaluar las propiedades tecnológicas de piezas
Cerámica obtenida a partir de masas utilizadas en la producción de gres sanitario, que contiene
residuo de cuarcita, mediante sustitución parcial de feldespato. Inicialmente se llevó a cabo
un estudio de caracterización físico-mineralógica de los residuos y materias primas
materiales convencionales que forman parte de la composición de la masa, los cuales son: arcilla, feldespato,
cuarzo y caolín. Las caracterizaciones se realizaron a través de las siguientes
técnicas: análisis granulométrico por difracción láser, difracción de rayos X,
Fluorescencia de rayos X, análisis térmico. Las composiciones se formularon variando-
la cantidad de residuo, sustituyendo el feldespato al 10, 15, 20 y 25% en peso.
Se analizaron las propiedades reológicas de las barbotinas, destacando también las
pH. El proceso de encolado se utilizó en la etapa de conformado, luego del secado.
(110°C), el tratamiento térmico se realizó a una temperatura de 1200°C, en dos ciclos
incendio. Para la caracterización se realizaron las siguientes pruebas: análisis visual
color después de la combustión, fusibilidad, absorción de agua, pérdida al fuego, porosidad,
masa específica aparente, contracción por cocción, coeficiente de expansión térmica,
resistencia a la flexión, dureza Vickers y módulo de elasticidad. La microestructura fue
evaluado mediante microscopía electrónica de barrido y análisis de difracción de rayos X.
Los resultados mostraron que las características reológicas de las suspensiones eran
apropiado, cuando se reemplaza parcialmente el feldespato con residuos de cuarcita en
hasta un 25% en peso, para el proceso de encolado. Muestras producidas a partir de
composiciones que contienen residuos de cuarcita, en el rango de 10 - 25%, presentadas
valores de resistencia a la flexión superiores a 35MPa, absorción de agua
aproximadamente 0,5% y contracción lineal después de la quema por debajo del 12%, valores
dentro de la gama recomendada para la fabricación de gres sanitario. La presencia de
El residuo de cuarcita no alteró las fases cristalinas presentes en las piezas
sinterizado se observó la presencia de cuarzo y mullita. |
pt_BR |