dc.creator.ID |
SOUSA, J. W. A. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/1355384774544057 |
pt_BR |
dc.contributor.advisor1 |
MELO, Raphael Henrique Falcão de. |
|
dc.contributor.advisor1ID |
MELO, R. H. F. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/9758661753469822 |
pt_BR |
dc.contributor.advisor-co1 |
SANTOS, Marco Antonio dos. |
|
dc.contributor.referee1 |
SANTANA, Renato Alexandre Costa de. |
|
dc.contributor.referee2 |
MACIEL, Theophilo Moura. |
|
dc.contributor.referee3 |
MELO, João Baptista da Costa Agra de. |
|
dc.contributor.referee4 |
RODRIGUES, Luiz Fernando Alves. |
|
dc.description.resumo |
Em meio ao mundo moderno em que estamos inseridos atualmente, a busca por materiais que
conciliem uma relação resistência/peso satisfatória tem sido palco de interesse mundial do setor
industrial, em especial o de transporte. Neste contexto, as ligas de magnésio ganham
protagonismo ao serem empregadas em componentes de automóveis para melhoria de sua
eficiência. Entretanto, um dos desafios a aplicação destes materiais é a obtenção de uniões
soldadas, já que este tipo de material tem apresentado limitações ao serem submetidas aos
processos convencionais por fusão ao arco elétrico. Neste sentido, o processo de soldagem em
estado sólido friction stir welding surge como boa alternativa para união destas ligas. Portanto,
este trabalho tem por objetivo avaliar a influência que os parâmetros de soldagem
desempenham na microestrutura e propriedades mecânicas de juntas soldadas da liga de
magnésio AZ31. As juntas foram produzidas a partir de diferentes condições definidas através
do planejamento experimental empregando uma fresadora universal de três eixos. Foram
realizadas caracterização microestrutural e mecânica das juntas soldadas, conforme
microscopia ótica e ensaios de tração uniaxial e de microdureza Vickers, respectivamente, bem
como análise fractográfica das superfícies de fratura via microscópio eletrônico de varredura.
Os resultados demonstraram um bom aspecto visual das juntas ao constatar-se a ausência de
trincas e falta de preenchimento. Diferentes níveis de resistência mecânica foram obtidos,
chegando a atingir 197 MPa. Os tamanhos médios de grão da zona de mistura foram menores
do que os do material de base, apresentando reduções que chegaram a 74%. Resultando na
obtenção de maiores níveis de microdureza nos casos de menor tamanho de grão. As imagens
fractográficas mostraram considerável presença de dimples, caracterizando fratura dúctil das
juntas soldadas. Diante disso, os variados níveis de temperatura resultante das diferentes
condições de parâmetros de soldagem impostas foram determinantes para o comportamento
microestrutural, o que consequentemente veio a influenciar no comportamento mecânico. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia Mecânica |
pt_BR |
dc.title |
Caracterização, avaliação e otimização das propriedades mecânicas de juntas de liga de magnésio AZ31 soldadas pelo processo FSW |
pt_BR |
dc.date.issued |
2023-12-19 |
|
dc.description.abstract |
In the midst of the modern world in which we currently live, the search for materials that
combine a satisfactory resistance/weight ratio has been a stage of worldwide interest in the
industrial sector, especially the transport sector. In this context, magnesium alloys gain
prominence when used in automobile components to improve their efficiency. However, one
of the challenges in applying these materials is obtaining welded joints, as this type of material
has presented limitations when subjected to conventional processes by electric arc fusion. In
this sense, the solid-state friction stir welding process appears as a good alternative for joining
these alloys. Therefore, this work aims to evaluate the influence that welding parameters have
on the microstructure and mechanical properties of welded joints made of AZ31 magnesium
alloy. The joints were produced based on different conditions defined through experimental
planning using a three-axis universal milling machine. Microstructural and mechanical
characterization of the welded joints were carried out, according to optical microscopy and
uniaxial tensile and Vickers microhardness tests, respectively, as well as fractographic analysis
of the fracture surfaces via scanning electron microscope. The results demonstrated a good
visual appearance of the joints, showing the absence of cracks and lack of filling. Different
levels of mechanical resistance were obtained, reaching 197 MPa. The average grain sizes of
the mixing zone were smaller than those of the base material, showing reductions of up to 74%.
Resulting in obtaining higher levels of microhardness in cases of smaller grain size. The
fractographic images showed a considerable presence of dimples, characterizing ductile
fracture of the welded joints. Therefore, the varied temperature levels resulting from the
different welding parameter conditions imposed were decisive for the microstructural behavior,
which consequently influenced the mechanical behavior. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/36847 |
|
dc.date.accessioned |
2024-07-25T12:16:06Z |
|
dc.date.available |
2024-07-25 |
|
dc.date.available |
2024-07-25T12:16:06Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Planejamento experimental |
pt_BR |
dc.subject |
Microestrutura |
pt_BR |
dc.subject |
Propriedades mecânicas |
pt_BR |
dc.subject |
Liga de Magnésio AZ31 |
pt_BR |
dc.subject |
Friction Stir Welding |
pt_BR |
dc.subject |
Experimental planning |
pt_BR |
dc.subject |
Microstructure |
pt_BR |
dc.subject |
Mechanical property |
pt_BR |
dc.subject |
AZ31 Magnesium alloy |
pt_BR |
dc.subject |
Friction Stir Welding |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SOUSA, José Wallisson de Abreu. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Characterization, evaluation and optimization of the mechanical properties of alloy joints AZ31 magnesium welded by FSW process |
pt_BR |
dc.identifier.citation |
SOUSA, José Wallisson de Abreu. Caracterização, avaliação e otimização das propriedades mecânicas de juntas de liga de magnésio AZ31 soldadas pelo processo FSW. 2023. 109 f. Dissertação (Mestrado em Engenharia Mecânica) – Programa de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologias, Universidade Federal de Campina Grande, Paraíba, Brasil, 2023. |