Obtenção de nanofibras de SnO2 dopadas com manganês.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS
→
Mestrado em Ciência e Engenharia de Materiais.
→
Ver item

dc.creator.ID	NASCIMENTO, E. P.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/8176311608210936	pt_BR
dc.contributor.advisor1	MENEZES, Romualdo Rodrigues.
dc.contributor.advisor1ID	MENEZES, R. R.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/1169292996645931	pt_BR
dc.contributor.referee1	COSTA, Ana Cristina Figueiredo de Melo.
dc.contributor.referee1ID	COSTA, A. C. F. M.	pt_BR
dc.contributor.referee1Lattes	http://lattes.cnpq.br/6309225172752964	pt_BR
dc.contributor.referee2	BARROS, Bráulio Silva.
dc.contributor.referee2ID	BARROS, B. S.	pt_BR
dc.contributor.referee2Lattes	http://lattes.cnpq.br/8938691250105531	pt_BR
dc.description.resumo	O dióxido de estanho (SnO2) é um óxido metálico semicondutor que tem sido bastante investigado e preparado na forma de nanofibras para aplicações em fotocatálise, no sensoriamento de gases, em eletrodos transparentes para células solares, entre outras. Assim sendo, este trabalho propôs-se a sintetizar nanofibras de SnO2 dopadas com manganês (Mn) (0; 1,5; 3,0; 5,0; 7,0 e 10,0 %at de Mn) utilizando a técnica de fiação por sopro em solução (SBS) e analisar a influência da concentração do Mn nas propriedades térmicas, morfológicas, estruturais e elétricas das nanofibras produzidas. Foram obtidas com sucesso nanofibras híbridas utilizando como sistema precursor uma solução constituída por etanol/N,N-dimetilformamida (DMF), poli(vinil pirrolidona) (PVP), acetato de manganês e cloreto de estanho dihidratado, as quais foram submetidas a calcinação à temperatura de 700 ºC para conversão dos precursores na fase SnO2 com e sem dopante. As nanofibras foram caracterizadas quanto ao seu comportamento térmico, morfologia, composição química e propriedades estruturais e elétricas. As fibras obtidas apresentaram morfologia tubular (oca) e diâmetros médios na faixa de nanômetros. A formação da fase SnO2 foi confirmada para todas as amostras e foi observado que o Mn formou solução sólida com SnO2. Além disso, o Mn provocou uma redução nos parâmetros de rede e no tamanho de cristalito do SnO2. As nanofibras de SnO2 puro e dopado com Mn apresentaram, no geral, comportamento ôhmico nas curvas de corrente voltagem (I-V) e houve uma tendência de aumento da corrente elétrica com o aumento do teor de Mn. As dimensões nanométricas das fibras obtidas neste trabalho, aliadas à dopagem com Mn, à morfologia tubular e ao comportamento ôhmico observado nas curvas de I-V de todas as amostras são características promissoras para aplicação no sensoriamento de gases.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM LETRAS EM REDE PROFLETRAS (UFRN)	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia de Materiais	pt_BR
dc.title	Obtenção de nanofibras de SnO2 dopadas com manganês.	pt_BR
dc.date.issued	2018-08-17
dc.description.abstract	Tin oxide (SnO2) is a semiconductor metal oxide that has been extensively investigated and prepared in the form of nanofibers for application in photocatalysis, gas sensing, transparent electrodes for solar cells, among others. Thus, this work aimed to synthesize SnO2 nanofibers doped with manganese (Mn) (0, 1,5, 3,0, 5,0, 7,0 and 10,0 at.% Mn) using solution blow spinning technique (SBS) and to analyze the influence of Mn concentration on the thermal, morphological, structural and electrical properties of the nanofibres produced. Hybrid nanofibers were successfully obtained using a solution consisting of ethanol/N,N-dimethylformamide (DMF), poly (vinyl pyrrolidone) (PVP), manganese acetate and tin chloride dihydrate, which were subjected to calcination at 700 ºC to convert the precursors in SnO2 phase with and without dopant. The nanofibers were characterized in terms of their thermal behavior, morphology, chemical composition, and structural and electrical properties. The obtained fibers presented tubular (hollow) morphology and average diameters in the nanometer range. The SnO2 phase formation was confirmed for all samples and it was observed that Mn formed solid solution with SnO2. In addition, Mn caused a reduction in SnO2 lattice parameters and in crystallite size. Nanofibers of pure and Mn-doped SnO2 showed, in general, ohmic behavior in the current-voltage (I-V) curves and there was a trend of increasing electric current with increasing Mn content. The nanometric dimensions of the fibers obtained in this work, together with Mn doping, their tubular morphology and the ohmic behavior observed in the I-V curves of all samples are promising characteristics for application in the gas sensing.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/36990
dc.date.accessioned	2024-08-01T17:23:36Z
dc.date.available	2024-08-01
dc.date.available	2024-08-01T17:23:36Z
dc.type	Dissertação	pt_BR
dc.subject	Fiação por Sopro em Solução	pt_BR
dc.subject	Nanofibras Ocas de SnO2, SnO2	pt_BR
dc.subject	Dopado com Manganês	pt_BR
dc.subject	Propriedades Elétricas	pt_BR
dc.subject	Solution Blow Spinning	pt_BR
dc.subject	Hollow SnO2 Nanofibers	pt_BR
dc.subject	Mn-doped SnO2	pt_BR
dc.subject	Electrical Properties	pt_BR
dc.rights	Acesso Aberto	pt_BR
dc.creator	NASCIMENTO, Emanuel Pereira do.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Obtaining SnO2 nanofibers doped with manganese.	pt_BR
dc.identifier.citation	NASCIMENTO, Emanuel Pereira do. Obtenção de nanofibras de SnO2 dopadas com manganês. 2018. 80 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Universidade Federal de Campina Grande, Centro de Ciências e Tecnologia, Campina Grande, Paraíba, Brasil, 2018.	pt_BR