dc.creator.ID |
SANTOS, É. S. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/0868041575610986 |
pt_BR |
dc.contributor.advisor1 |
CAMPOS, Ana Regina Nascimento. |
|
dc.contributor.advisor1ID |
CAMPOS, A. R. N. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/9510211229362397 |
pt_BR |
dc.contributor.advisor-co1 |
SANTANA, Renato Alexandre Costa de. |
|
dc.contributor.advisor-co1ID |
SANTANA, R. A. C. |
pt_BR |
dc.contributor.advisor-co1Lattes |
http://lattes.cnpq.br/1438381290031148 |
pt_BR |
dc.contributor.referee1 |
RAMOS, Wagner Brandão. |
|
dc.contributor.referee2 |
DANTAS, Josiane Costa. |
|
dc.description.resumo |
A eletrodeposição vem sendo muito utilizada no desenvolvimento de ligas metálicas, a fim de
produzir revestimentos resistentes a corrosão. Estuda-se várias composições de banhos
eletrolíticos para obtenção da liga Ni-Co, desta forma, adição de citrato de sódio (complexante)
ao banho tem ganhado destaque nos estudos. Para otimizar o processo foi utilizado um
Delineamento Composto Central Rotacional (DDCR) 2² com pontos axiais (
α
α) e 2 pontos
centrais, totalizando 10 experimentos. A partir do banho de citrato foi possível observar que
houve o comportamento anômalo característico das ligas de Ni-Co, revestimentos obtidos em
zonas ácidas apresentaram uma morfologia mais uniforme, maior magnetização de saturação,
porém, baixos valores para resistência a corrosão devido ao alto teor de cobalto em sua
composição, além disso, apresentaram uma mistura de fases (fcc+hcp). Já os revestimentos
obtidos em zonas alcalinas, apresentaram uma morfologia nodular, semelhante a couve-flor que
se atrela ao maior teor de níquel na liga conforme resultados de composição química. Esses
revestimentos apresentaram baixa magnetização de saturação, porém, bons resultados para
corrosão. Portanto, conclui-se que no estudo foi possível obter ligas com altos teores de níquel
o que possibilita aplicações como revestimentos protetores e ligas com altos teores de cobalto
possibilitando a utilização no setor de materiais magnéticos. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia Química |
pt_BR |
dc.title |
Estudo sobre as propriedades magnéticas e corrosivas da liga ni-co obtida pelo processo de eletrodeposição a partir de um banho com citrato de sódio |
pt_BR |
dc.date.issued |
2024-03-22 |
|
dc.description.abstract |
Electrodeposition has been widely used in the development of metallic alloys, in order to
promote corrosion-resistant coatings. Various electrolytic bath compositions are studied to
obtain the Ni-Co alloy, therefore, the addition of sodium citrate (complexant) to the bath has
gained prominence in studies. To optimize the process, a 2² Rotational Central Composite
Design (DDCR) was used with axial points (-α, +α) and 2 central points, totaling 10
experiments. From the citrate bath it was possible to observe that there was the anomalous
behavior characteristic of Ni-Co alloys, coatings obtained in acidic zones presented a more
uniform morphology, greater saturation magnetization, however, low values for corrosion
resistance due to the high content of cobalt in their composition, in addition, they presented a
mixture of phases (fcc+hcp). The coatings obtained in alkaline zones presented a nodular
morphology, similar to cauliflower, which is linked to the highest nickel content in the alloy
according to chemical composition results. These coatings showed low saturation
magnetization, however, good results for corrosion. Therefore, it is concluded that in the study
it was possible to obtain alloys with high nickel contents, which allows applications such as
protective coatings and alloys with high cobalt contents, enabling their use in the magnetic
materials sector. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/37805 |
|
dc.date.accessioned |
2024-09-18T13:28:29Z |
|
dc.date.available |
2024-09-18 |
|
dc.date.available |
2024-09-18T13:28:29Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Ni-Co |
pt_BR |
dc.subject |
Citrato |
pt_BR |
dc.subject |
Revestimento metálico |
pt_BR |
dc.subject |
Nickel-Cobalt |
pt_BR |
dc.subject |
Citrate |
pt_BR |
dc.subject |
Metallic coating |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SANTOS, Évany Silva dos. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Study on the magnetic and corrosive properties of the ni-co alloy obtained by the electrodeposition process from a bath with sodium citrate |
pt_BR |
dc.identifier.citation |
SANTOS, Évany Silva dos. Estudo sobre as propriedades magnéticas e corrosivas da liga ni-co obtida pelo processo de eletrodeposição a partir de um banho com citrato de sódio. 2024. 71 f. Dissertação (Mestrado em Engenharia Química) – Programa de Pós-Graduação em Engenharia Química, Centro de Ciências e Tecnologias, Universidade Federal de Campina Grande, Paraíba, Brasil, 2024. |
pt_BR |