dc.creator.ID |
MÈLLO, M. C. A. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/4170549666944809 |
pt_BR |
dc.contributor.advisor1 |
KIMINAMI, Claudio Shyinti. |
|
dc.contributor.advisor1ID |
KIMINAMI, C. S. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/5443002033733395 |
pt_BR |
dc.contributor.referee1 |
SANTOS, Marco Antonio dos. |
|
dc.contributor.referee2 |
KIMINAMI, Ruth Herta Goldschmidt Aliaga. |
|
dc.contributor.referee3 |
MATA, Sandoval Farias da. |
|
dc.description.resumo |
Este trabalha apresenta um estudo em superesfriamento de cobre puro pelo método de eliminação de sítios catalíticos do nucleação heterogênea pela técnica de fusão em presença de vidro comercial como fluxo.As amostras envolvidas peIo fluxo foram
acondicionadas em cadinho de quartzo e submetidas a ciclos de aquecimento e resfriamento em forno com aquecimento resistivo com taxas de 60K/min e 10K /min respectivamente. Um super aquecimento de 40K foii utilizado. O controle e registro de temperatura foram realizados com um termopar de 1mm locaIizado no fundo
do cadinho e registradores digital e potenciamétrico X-t . O grau
de superesfriamento foi medido pela detecção da recalescencia da
amostra na solidificação. Altos níveis de superesfriamento foram obtidos, sendo que o máximo alcançado neste trabalho foi ( A T ::= 27 i K ) , superior aos reportados pela literatura. O nível de superesfriamento alcançado aumentou com o aumento do
número de ciclos aquecimento /resfriamento. Analises
metalográficas indicam homogenidade e refino de grão da estrutura das amostras com alto grau de superesfriamento. Isto demonstra a viabilidade da técnica aqui aplicada como método de eliminação de sítios catalíticos de nucleação heterogênea e a eficiência do processo de imposição de altos graus de superesfriamento para a obtenção de estruturas refinadas e homogêneas. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.title |
Superesfriamento de metais fundidos. |
pt_BR |
dc.date.issued |
1988-09 |
|
dc.description.abstract |
This work presents a study on supercooling of pure copper by the method of elimination of catalytic sites of heterogeneous nucleation by the technique of fusion in the presence of commercial glass as flow. Samples involved by the flow were
conditioned in quartz crucible and submitted to heating and cooling cycles in a furnace with resistive heating at rates of 60 K / min and 10 K / min respectively. Overheating 40K was used. Temperature control and recording were performed with a 1mm thermocouple located on the bottom
of the crucible and digital and potentiametric X-t recorders. The degree
supercooling was measured by the detection of the rectal
sample in the solidification. Higher supercooling levels were obtained, and the maximum reached in this work was (A T :: = 27 i K), higher than those reported in the literature. The level of supercooling achieved increased with the increase in
number of heating / cooling cycles. Analyzes
metallography indicate homogeneity and grain refining of the sample structure with a high degree of supercooling. This demonstrates the feasibility of the technique applied here as a method of elimination of catalytic sites of heterogeneous nucleation and the efficiency of the process of imposing high degrees of supercooling to obtain refined and homogeneous structures. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/4147 |
|
dc.date.accessioned |
2019-06-05T16:27:12Z |
|
dc.date.available |
2019-06-05 |
|
dc.date.available |
2019-06-05T16:27:12Z |
|
dc.type |
Dissertação |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
MÉLLO, Manassés da Costa Agra. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Supercooling of molten metals. |
pt_BR |
dc.identifier.citation |
MELLO, Manassés da Costa Agra. Superesfriamento de metais fundidos. 1988. 135f.(Dissertação de Mestrado em Engenharia Mecânica), Curso de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba – Campus II - Campina Grande - PB - Brasil,1988. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/4147 |
pt_BR |