Microporous membranes were obtained from nanocomposites polyamide66 and regional bentonite clay, through the technique of immersion precipitation. The nanocomposites were obtained by solution with a pre-stabelished reaction time. The clay was treated with quaternary ammonium salt (Cetremide®) in order to make it organophilic. Untreated and treated clay were characterized by X-ray fluorescence (XRF) spectroscopy, Fourier transform infrared (FTIR), X-ray diffraction (XRD) and thermogravimetry (TG), which confirmed the insertion of the Cetremide® salt in the layers of clay and their thermal stability. While the membranes were characterized by XRD, TG, differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and flow measurements. The results of XRD, TG and DSC confirmed the thermal stability and morphological structure
with intercalated/partially exfoliated lamellae of clay in the polymer matrix. By SEM, it was revealed an asymmetric morphology consisting of a skin layer and a porous sublayer. The higher clay content in the membrane give the lower film thickness. This influencing directly the flow measurements of the membranes produced from the nanocomposites. In general, the initial flow with distilled water throught the membranes decrease and stabilise after 60 min, this due to a compression or swelling occurred in the membranes. In tests of water-oil separation it was found that the relationship J/J0 tends to be greater when using
emulsions with lower concentration. The water-oil separation tests at concentrations of 300 and 500 ppm for all membranes showed a significant reduction in oil concentration in the permeate, thus showing that these membranes have potential for this application.