Preparação de substratos cerâmicos a partir de aluminas nacionais infiltradas com vidro para aplicação em prótese dentária.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS
→
Mestrado em Ciência e Engenharia de Materiais.
→
Ver item

dc.creator.ID	MAIA, M. Z. A. A.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/7263718409120408	pt_BR
dc.contributor.advisor1	SANTANA, Lisiane Navarro Lima.
dc.contributor.advisor1ID	SANTANA, L. N. L.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/4057799848801141	pt_BR
dc.contributor.referee1	ARAÚJO, Edjânio Barbosa.
dc.contributor.referee2	FOOK, Marcus Vinicius Lia.
dc.contributor.referee3	MONTENEGRO, Robinson Viegas.
dc.description.resumo	Em odontologia, a cerâmica é considerada excelente alternativa de tratamento restaurador da estrutura dental, devido à sua biocompatibilidade, resistência à flexão, condutibilidade térmica semelhante aos tecidos dentais, radiopacidade, integridade marginal, estabilidade de cor e, principalmente, excelente potencial para simular a aparência dos dentes. A presente pesquisa tem como objetivo avaliar as propriedades microestruturais e mecânicas de substratos obtidos a partir de aluminas nacionais e infiltrados com vidro, para aplicação em prótese dentária. Inicialmente as aluminas foram caracterizadas quanto à composição mineralógica e granulométrica. Foram confeccionados corpos de prova de acordo com o método preconizado por um dos fornecedores das matérias primas. Estes foram submetidos a ensaios mecânicos de resistência a flexão e dureza, para avaliar se apresentam características próprias para uso em odontologia. Os substratos foram submetidos à caracterização da morfologia e da superfície de fratura através de microscopia eletrônica de varredura, e observou-se a microestrutura composta com aproximadamente 75% de alumina com a infiltração nos poros do vidro de lantânio. A tomografia por coerência óptica possibilita a análise das amostras por caracterização óptica baseada no coeficiente de espalhamento do laser. Falhas internas da ordem de 50um são reveladas com precisão de forma não invasiva e não destrutível, sem a necessidade de preparação das amostras.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia de Materiais e Metalúrgica	pt_BR
dc.title	Preparação de substratos cerâmicos a partir de aluminas nacionais infiltradas com vidro para aplicação em prótese dentária.	pt_BR
dc.date.issued	2009-09-15
dc.description.abstract	In dentistry, ceramics are considered an excellent alternative for restorative treatment of dental structure due to its biocompatibility, flexure strength, dental tissue-like thermal conductivity, marginal integrity, color stability and mainly for its excellent potential to simulate tooth appearance. The aim of the present work is to evaluate the microstructural and mechanical properties of infiltrated glass alumina substrates for dental prosthesis application. Firstly, both mineralogical composition and granulometry of the different alumina were characterized. Secondly, samples were prepared in accordance with a method provided by one of the raw material suppliers. Flexure strength and hardness were carried on these samples in order to evaluate their proper characteristics for dentistry use. The substrates had their morphology and fracture surface characterized by Scanning Electron Microscopy. It was observed that the microstructure was composed with approximately 75% of alumina with lanthanum glass pores infiltration.. The optical coherent tomography provided the samples evaluation by optical characterization based on the laser scattering coefficient. Internal failures of about 50um were revealed with precision in a not invasive or destructive way, hence, with no need for extra samples preparation.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/4855
dc.date.accessioned	2019-07-11T16:13:35Z
dc.date.available	2019-07-11
dc.date.available	2019-07-11T16:13:35Z
dc.type	Dissertação	pt_BR
dc.subject	Alumina	pt_BR
dc.subject	Infiltração	pt_BR
dc.subject	Vitrea	pt_BR
dc.subject	Cerâmica	pt_BR
dc.subject	Odontológica	pt_BR
dc.subject	Infiltration	pt_BR
dc.subject	Ceramics	pt_BR
dc.subject	Odontology	pt_BR
dc.rights	Acesso Aberto	pt_BR
dc.creator	MAIA, Maria Zilda Albuquerque Araújo.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Preparation of ceramic substrates from national alumina infiltrated with glass for application in dental prostheses.	pt_BR
dc.identifier.citation	MAIA, M. Z. A. A. Preparação de substratos cerâmicos a partir de aluminas nacionais infiltradas com vidro para aplicação em prótese dentária. 2009. 59 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2009. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/4855	pt_BR