dc.creator.ID |
LARANJEIRA, E. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/3574545531102928 |
pt_BR |
dc.contributor.advisor1 |
CARVALHO, Laura Hecker de. |
|
dc.contributor.advisor1ID |
CARVALHO, L. H. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/6358009621640820 |
pt_BR |
dc.contributor.advisor2 |
SILVA, Suédina Maria de Lima. |
|
dc.contributor.advisor2ID |
SILVA, S. M. L. |
pt_BR |
dc.contributor.advisor2Lattes |
http://lattes.cnpq.br/6437959556217825 |
pt_BR |
dc.contributor.referee1 |
D'Almeida, José Roberto Moraes. |
|
dc.contributor.referee2 |
GOMES, Ailton de Souza. |
|
dc.contributor.referee3 |
SOUZA, Antônio Gouveia de. |
|
dc.contributor.referee4 |
SANTANA, Lisiane Navarro de Lima. |
|
dc.description.resumo |
0 presente trabalho trata das propriedades dos compósitos poliéster/juta, dos sistemas poliéster/bentonita e dos híbridos poliéster/juta/bentonita. A performance mecânica (propriedades tênseis e de impacto) desses compósitos foram investigadas em função do teor e orientação da fibra; teor e modificação química da argila e composição do sistema. Também foi avaliada a influência da adição de um sistema retardante de chama nas propriedades mecânicas e de inflamabilidade de compósitos selecionados. As propriedades de sorção de água de alguns desses sistemas, também foram determinadas. A argila foi tratada com ácido clorídrico (0,3 N) e com dois sais quaternários de amônio (Dodigen e Cetremide). As argilas natural e modificada foram caracterizadas por análise química, espectroscopia de infravermelho, difração de raios X e termogravimetria indicando que ativação acida provocou esfoliação, enquanto as modificações com os sais quaternários de amônio promoveram organofilização. Os resultados mostraram que as propriedades dos compósitos são fortemente dependentes da orientação da fibra, sendo as maiores propriedades para os compósitos testados
na direção do eixo das fibras. Propriedades mecânicas superiores as da matriz
foram obtidas mesmo a baixo teores (10% em peso) de fibra. A modificação da
argila afetou as propriedades dos compósitos, especialmente o alongamento na
ruptura e a resistência ao impacto. Os maiores valores de tenacidade foram apresentados pelos sistemas poliéster/bentonita e poliéster/juta/bentonita contendo a argila tratada com HCI e com Dodigen no teor de 2% em peso. Dados de difração de raios X mostraram que, a incorporação da bentonita tratada com Cetremide ao poliéster favoreceu a formação de um nanocompósito o que resultou no aumento da retardância de chama do sistema. Apenas a matriz e o compósito poliéster/5%bentonita tratada com Cetremide, contendo 5, 6, 7,5% e 5% em peso de bromo no sistema retardante de chama, respectivamente, conseguiram classificação V-0 no ensaio de inflamabilidade UL 94-V. 0 sistema poliéster/5%bentonita natural com 5% em peso de bromo no sistema retardante de chama foi classificado como V-1. Os demais sistemas não apresentaram
classificação. A sorção de água aumentou com adição da fibra de juta e da argila
na matriz. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharias |
|
dc.title |
Propriedades de compósitos poliéster/juta. Influência da adição de carga mineral nanoparticulada e sistema antichama. |
pt_BR |
dc.date.issued |
2004-09-03 |
|
dc.description.abstract |
The present work deals with the properties of polyester/jute composites; of the
systems polyester/bentonite and polyester/jute/bentonite. The mechanical
performance (tensile and impact properties) of these composites was investigated
as a function of fiber content and orientation; clay content and chemical
modification and system composition. The influence of a flame retarding system
addition on the mechanical, thermal and burning characteristics of selected
composites was also analyzed. The water sorption characteristics of some of
these systems were determined. The clay was modifiied with hydrochloric acid
(0.3N) and with two different quaternary ammonium salts (Dodigen and
Cetremide). Both natural and modified clays were characterized by chemical
analysis, FTIR spectroscopy, X ray diffraction and thermogravimetry which
indicated that acid activation promoted exfoliation while quaternary ammonium salt
modifications promoted organophilization. The results show composite properties
to be strongly dependent on fiber orientation, being much higher in composites
tested along the jute fiber axis direction. Mechanical properties higher than those
of the matrix were achieved at fiber contents as low as 10% in weight. It was
shown that composite properties, mainly those of elongation at break and impact
strength, were dependent on clay modification. Better toughness was displayed by
polyester/bentonite and polyester/jute/bentonite systems with HCI and Dodigen
modified clays at 2% w/w clay contents. X ray diffraction data showed that a
polyester/bentonite nanocomposite was obtained with the cetremide modified clay
incorporation which led to an increase in flame resistance of the system. Only the
matrix and the composite Polyester/bentonite 5% w/w with the Cetremide modified
clay having 5, 6, 7,5% and 5% w/w bromine in the flame retardant system,
respectively, achieved V-0 classification on the UI-94V test. The system
polyester/5%bentonite natural and 5% w/w bromine in the flame retardant system
achieved V-1 classification. The remainder did not achieve classification. Water
sorption increased with jute fiber and with clay addition in the matrix. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/6847 |
|
dc.date.accessioned |
2019-09-09T17:49:46Z |
|
dc.date.available |
2019-09-09 |
|
dc.date.available |
2019-09-09T17:49:46Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
Nanocompósitos |
|
dc.subject |
Compósitos Poliéster/juta |
|
dc.subject |
Carga Mineral Nanoparticulada |
|
dc.subject |
Sistema Antichama |
|
dc.subject |
Poliéster |
|
dc.subject |
Bentonita |
|
dc.subject |
Juta 5 |
|
dc.subject |
Nanocomposites |
|
dc.subject |
Polyester / jute composites |
|
dc.subject |
Nanoparticulate Mineral Load |
|
dc.subject |
Anti-flame System |
|
dc.subject |
Polyester |
|
dc.subject |
Bentonite |
|
dc.subject |
Jute 5 |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
LARANJEIRA, Edilâne. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Properties of polyester / jute composites. Influence of the addition of nanoparticulate mineral filler and flame retardant system. |
pt_BR |
dc.identifier.citation |
LARANJEIRA, Edilâne. Propriedades de compósitos poliéster/juta. Influência da adição de carga mineral nanoparticulada e sistema antichama. 2004. 179f. (Tese de Doutorado em Engenharia de Processos), Programa de Pós-graduação em Engenharia de Processos, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2004. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/6847 |
pt_BR |