dc.description.resumo |
Neste trabalho, as propriedades mecânicas (resistência a tração, modulo
elástico, alongamento e resistência ao impacto) de compósitos de matriz poliéster
reforçados por tecidos de juta, tricotado e tramado, foram avaliadas em função da
arquitetura do tecido. O efeito do tratamento de pós-cura, para os compósitos com
tecidos tricotados, também foi avaliado. Aplicou-se a metodologia matemática,
desenvolvida por Gommers, na qual se pode ter, a partir de ensaios de tração, os
valores consistentes para todos os módulos elásticos e de cisalhamento. Os
resultados mostraram que os compósitos com tecido tricotado apresentaram
resistência a tração e alongamento menores que os da resina poliéster enquanto,
o modulo elástico, foi superior ao da matriz em todos os casos estudados. O teor
otimo de fibra para os compósitos reforçados com tecido tricotado esta próximo
dos 40%, em peso. Os compósitos reforçados por tecidos tramados, apresentaram
resistência a tração menor do que a matriz para um teor de fibra de 26% (duas
camadas de tecido), enquanto, os reforçados por quatro camadas de tecido (38%,
em peso) apresentaram resistência a tração superior. Em todos os casos o
modulo elástico foi superior ao da matriz e o alongamento menor. Em geral os
compósitos reforçados com tecidos tramados apresentaram propriedades
superiores as dos compósitos reforçados por tecidos tricotados, entretanto estes
últimos apresentaram uma maior resistência ao impacto. Quanto a metodologia
matemática, os resultados obtidos se mostraram bastante consistentes,
coincidindo os valores experimentais com os teóricos. Os seguintes resultados
forma obtidos para os módulos elásticos: Exx entre 0,894 e 0,693 GPa; Eyy entre
0,717 e 0,389 GPa; Exy entre 3,314 e 2,564 GPa; e o modulo de cisalhamento, G
entre 0,539 e 0,352 GPa. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia Química. |
|
dc.title |
Propriedades mecânicas de compósitos poliéster/tecidos de juta (tricotado e tramado). |
pt_BR |
dc.date.issued |
2001-05 |
|
dc.description.abstract |
In this work , the mechanical properties of the composites(polyester resin
/jute, knitted and warped) were analysed in function of the architecture of the
fabric ,as well as the effect of the pos-cure treatment under the knitted cloths. For
obtaining the consistent values for all the elastic modules, it was applied the
mathematical methodology developed by Gommers. The results have showed that
the composites with knitted fabric have presented tensile strength and levels of
deformation lower than the polyester resin while elastic modulus were superior to
the matrix in all the analysed cases. The best properties were observed with a
content of 40% (weight) fibre. The composites reinforced whith the weave fabric,
have showed lower tensile strength in relation to the matrix in which the content of
fibre was 26% ( two layers of fabric) while those ones reinforced by 4 layers
(38%,weight ) have showed a higher tensile strength. In all cases the elastic
modulus was superior to the matrix and the deformation was lower. In general,
the composites reinforced with warped cloths have demonstrated superior
properties in relation to the composites reinforced with knitted cloths. Although the
latter ones showing more resistance to impact . Concerning the mathematical
methodology, the results obtained were quite consistent, coinciding the
experimental values with the theoretical ones. The following results for elastic
modulus were: Exx between 0,894 and 0,693 GPa; Eyy between 0,717 and 0,389
GPa; Exy between 3,314 and 2,564 GPa; and the shear module, G between 0,539
and 0,352 GPa. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/6929 |
|
dc.date.accessioned |
2019-09-11T13:00:22Z |
|
dc.date.available |
2019-09-11 |
|
dc.date.available |
2019-09-11T13:00:22Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Compósitos Poliméricos. |
|
dc.subject |
Poliéster. |
|
dc.subject |
Modelagem Matemática. |
|
dc.subject |
Resina Poliéster. |
|
dc.subject |
Fibra de Juta. |
|
dc.subject |
Tecidos Tricotados. |
|
dc.subject |
Tecidos Tramados. |
|
dc.subject |
Tecidos de Juta. |
|
dc.subject |
Polymeric Composites. |
|
dc.subject |
Polyester. |
|
dc.subject |
Mathematical Modeling. |
|
dc.subject |
Polyester resin. |
|
dc.subject |
Jute fiber. |
|
dc.subject |
Knitted fabrics. |
|
dc.subject |
Woven fabrics. |
|
dc.subject |
Jute fabrics. |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
CAVALCANTE, Joselito Medeiros de Freitas. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Mechanical properties of polyester composites / jute fabrics (knitted and woven). |
pt_BR |
dc.identifier.citation |
CAVALCANTE, Joselito Medeiros de Freitas. Propriedades mecânicas de compósitos poliéster/tecidos de juta (tricotado e tramado). 2001. 93f. (Dissertação de Mestrado em Engenharia Química), Curso de Mestrado em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba - Campus II Campina Grande - Brasil, 2001. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/6929 |
pt_BR |