Fotodegradação do poliestireno de alto impacto contendo linhas de solda.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA
→
Mestrado em Engenharia Química
→
Ver item

dc.creator.ID	ALMEIDA, M. A. N. L.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/5814514864018809	pt_BR
dc.contributor.advisor1	RABELLO, Marcelo Silveira.
dc.contributor.advisor1ID	RABELLO, M. S.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/0384726674523131	pt_BR
dc.contributor.referee1	NAVARRO, Rômulo Feitosa.
dc.contributor.referee2	ARAÚJO, Edcleide Maria.
dc.description.resumo	A presença de linhas de solda ocorre com frequência durante o processamento de vários tipos de produtos poliméricos e e das principais causas de falha prematura. Em pecas injetadas, por exemplo, as linhas de solda podem ser formadas em cavidades com mais de um ponto de injeção, gerando uma descontinuidade de fluxo no encontro das varias frentes de material fundido. Muito embora este tipo de fenômeno tenha sido extensivamente estudado no que se refere aos fatores de processamento que controlam a resistência das linhas de solda, pouco se conhece sobre o comportamento degradativo deste tipo de descontinuidade. Este trabalho apresenta um estudo sobre a fotodegradação do poliestireno de alto impacto (HIPS). Amostras moldadas por injeção simples e dupla foram expostas em duas diferentes câmaras de envelhecimento por períodos de ate 150 dias. Os resultados indicaram uma forte deterioração nas propriedades mecânicas e visuais das amostras. A presença de linhas de solda causou uma redução na resistência a tração e deformação na ruptura dos materiais não expostos, mas nas amostras degradadas as linhas de solda não provocaram uma sensibilização mais acentuada quando comparada com as amostras produzidas por injeção simples.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia Química
dc.title	Fotodegradação do poliestireno de alto impacto contendo linhas de solda.	pt_BR
dc.date.issued	2003-02
dc.description.abstract	The presence of weld lines, formed during processing, is very common in polymer products, causing premature failure during service. In injection moulded samples, for example, weld lines are generated in cavities with more than one injection gate, causing a mechanical discontinuity when flow fronts are joined. Although this phenomenon is extensively studied in relation to processing conditions and mechanical properties, very little work was done in the investigation of degradation effects. This article shows a study on the influence of weld line on high-impact polystyrene (HIPS) photodegradation. Tensile bars prepared by single and double-gated injection moulding were exposed under two different exposure conditions for periods of up to 150 days. The results showed that weld lines caused a reduction in tensile strength and maximum elongation of unexposed samples but they do not cause further deterioration in comparison to the single-gated bars. Analyses by infrared spectroscopy revealed a high level of chemical degradation.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/6935
dc.date.accessioned	2019-09-11T14:32:49Z
dc.date.available	2019-09-11
dc.date.available	2019-09-11T14:32:49Z
dc.type	Dissertação	pt_BR
dc.subject	Poliestireno
dc.subject	Hips
dc.subject	Fotodegradação
dc.subject	Linhas de Solda
dc.subject	Linhas de Junção
dc.subject	Descontinuidades Locais
dc.subject	Polystyrene
dc.subject	Hips
dc.subject	Photodegradation
dc.subject	Welding Lines
dc.subject	Junction Lines
dc.subject	Local Discontinuities
dc.rights	Acesso Aberto	pt_BR
dc.creator	ALMEIDA, Marco Aurélio Neves Lima de.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Photodegradation of high impact polystyrene containing welding lines.	pt_BR
dc.identifier.citation	ALMEIDA, Marco Aurélio Neves Lima de. Fotodegradação do poliestireno de alto impacto contendo linhas de solda. 2003. 115f. (Dissertaçã) Mestrado em Engenharia Química, Programa de Pós-graduação em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Campina Grande - Paraíba - Brasil, 2003. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/6935	pt_BR