Aplicação de modelos de fratura elástica e de dano para a simulação numérica da influência do hidrogênio na propagação de trincas em aços de alta resistência.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS
→
Mestrado em Ciência e Engenharia de Materiais.
→
Ver item

dc.creator.ID	CARRASCO, J. A. P.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/9085140310628380	pt_BR
dc.contributor.advisor1	SILVA, Antonio Almeida.
dc.contributor.advisor1ID	SILVA, A. A.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/8361717016612632	pt_BR
dc.contributor.advisor2	SANTOS, Neilor Cesar dos.
dc.contributor.advisor2ID	SANTOS, N. C.
dc.contributor.advisor2Lattes	http://lattes.cnpq.br/4049499502347220
dc.contributor.referee1	SANTOS, Marco Antonio dos.
dc.contributor.referee2	BARBOSA, José Maria Andrade.
dc.description.resumo	Foi implementado um modelo computacional consistente, baseado na Mecânica da Fratura Linear Elástica e na Mecânica do Dano Continuo, para simular o problema da propagação de uma trinca submetida a um esforço mecânico e ao efeito da degradação provocada pela difusão do hidrogênio na estrutura cristalina de um ago de alta resistência. Na implementação dos modelos para o calculo do fator de intensidade de tensões no material hidrogenado e na simulação do crescimento e propagação de trincas, foram utilizados o Método dos Elementos Finitos e o Método de Runge-Kutta de quarta ordem, respectivamente. Os resultados obtidos nas simulações confirmaram a influencia da presença do hidrogênio na variação do fator de intensidade de tensões quando e considerado o seu efeito sobre os módulos elásticos do material. Do mesmo modo, a partir da aplicação do modelo de dano, foi observada a influencia da presença do hidrogênio na diminuição do tempo de início e propagação de trincas.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia de Materiais
dc.title	Aplicação de modelos de fratura elástica e de dano para a simulação numérica da influência do hidrogênio na propagação de trincas em aços de alta resistência.	pt_BR
dc.date.issued	2008-02-29
dc.description.abstract	A consistent computational model based on Elastic Linear Fracture Mechanics and Continuous Damage Mechanics was implemented to simulate the problem of crack propagation under mechanical stress and the effect of degradation caused by hydrogen diffusion in the crystal structure of a ago high strength. In the implementation of the models for the calculation of the stress intensity factor in the hydrogenated material and in the simulation of crack growth and propagation, the Finite Element Method and the Runge-Kutta Method were used. fourth order respectively. The results obtained in the simulations confirmed the influence of the presence of hydrogen on the stress intensity factor variation when considering its effect on the elastic modulus of the material. Likewise, from the application of the damage model, it was observed the influence of the presence of hydrogen in the reduction of crack initiation and propagation time.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7324
dc.date.accessioned	2019-09-25T19:11:10Z
dc.date.available	2019-09-25
dc.date.available	2019-09-25T19:11:10Z
dc.type	Dissertação	pt_BR
dc.subject	Mecânica - Fratura.
dc.subject	Fragilização.
dc.subject	Método dos Elementos Finitos.
dc.subject	Método de Runge-Kutta de Quarta Ordem.
dc.subject	Mecânica da Fratura Linear Elástica.
dc.subject	Mecânica do Dano Contínuo.
dc.subject	Mechanics - Fracture.
dc.subject	Fragility.
dc.subject	Finite Element Method.
dc.subject	Fourth Order Runge-Kutta Method.
dc.subject	Mechanics of Elastic Linear Fracture.
dc.subject	Mechanics of Continuous Damage.
dc.rights	Acesso Aberto	pt_BR
dc.creator	CARRASCO, Jorge Antonio Palma.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Application of elastic fracture and damage models for the numerical simulation of the influence of hydrogen on crack propagation in high strength steels.	pt_BR
dc.identifier.citation	CARRASCO, Jorge Antonio Palma. Aplicação de modelos de fratura elástica e de dano para a simulação numérica da influência do hidrogênio na propagação de trincas em aços de alta resistência. 2008. 134f. (Dissertação) Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Campina Grande - Paraíba - Brasil, 2008. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7324	pt_BR