dc.creator.ID |
GONÇALVES, W. P. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/3056392424689139 |
pt_BR |
dc.contributor.advisor1 |
SANTANA, Lisiane Navarro de Lima. |
|
dc.contributor.advisor1ID |
SANTANA, L. N. L. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/4057799848801141 |
pt_BR |
dc.contributor.advisor2 |
NEVES, Gelmires de Araújo. |
|
dc.contributor.advisor2ID |
NEVES, G. A. |
pt_BR |
dc.contributor.advisor2Lattes |
http://lattes.cnpq.br/3167458244674160 |
pt_BR |
dc.contributor.referee1 |
MENEZES, Romualdo Rodrigues. |
|
dc.contributor.referee2 |
SILVA, Valmir José da. |
|
dc.description.resumo |
Argilas são componentes fundamentais das massas dos materiais cerâmicos
tradicionais e que promovem durante a sinterização o desenvolvimento de cristais de
mulita, fase que confere resistência mecânica ao produto final. Uma inovação
importante nas ultimas décadas no setor cerâmico e a utilização de queima rápida, o
que pode induzir mudanças durante as transformações térmicas das matérias primas
e de suas composições. Para se implementar mudanças nos parâmetros de
queima e de fundamental importância o conhecimento prévio das transformações de
fases das argilas e das massas, sendo necessária em algumas situações a
formulação de novas composições. O objetivo desse trabalho e analisar a influencia
de diferentes tratamentos térmicos sobre as mudanças de fases e microestruturais
de argila esmectita e esmectita/caulinita, enfatizando a presença da mulita. Foram
utilizadas três argilas, duas nacionais e uma importada. As amostras foram
inicialmente submetidas a um processo de beneficiamento. Em seguida foi realizada
a etapa de delaminação, por meio dos processos de hidratação, congelamento,
desaglomeração, variando-se o teor de defloculante e o tempo de agitação.
Posteriormente, foram submetidas as caracterizações granulométricas e
mineralógicas. As amostras foram submetidas a tratamento térmico na faixa de
temperaturas entre 800 a 1250°C, com taxa de aquecimento entre 5 e 30°C/min e
tempo de permanência de 10 e 60 min. Os melhores resultados do processo de
delaminação foram observados para as amostras que não apresentaram oxido de
sódio. A partir dos difratogramas de raios X observou-se que a taxa de aquecimento
influencia sobre as reações durante o aquecimento, a estrutura da argila foi mantida
ate 800°C para as taxas mais rápidas, no entanto, para 5°C/min não se observou
picos característicos da mesma. Foi observado também que a menor taxa
influenciou sobre a nucleação de mulita e cordierita. Com relação as propriedades
físico-mecânicas, observou-se que a amostra com maior relação alumina/sílica
apresentou os melhores resultados. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.title |
Avaliação da influência de diferentes tratamentos térmicos sobre as transformações de fases de argilas-bentonita e bentonita/caulinita. |
pt_BR |
dc.advisor1 |
Ceramics |
|
dc.advisor1 |
Ceramics |
|
dc.date.issued |
2014-02-13 |
|
dc.description.abstract |
Clays are essential components of the traditional ceramic materials and
promote the development of mullite crystals during firing, which confers
mechanical strength to the final product. An important innovation in recent
decades in the ceramic industry is the use of fast firing, which can induce
changes during thermal processing of the materials and their composition. To
implement changes in firing parameters is crucial prior knowledge of phase
transformations of clays and traditional ceramic materials, being necessary in
some situations the formulation of new compositions. The aim of this study was
analyze the influence of different heat treatments on the microstructure and
phase changes of smectite and smectite/kaolinite clays, emphasizing the
presence of mullite. It was used in this work two samples of natural bentonite
and one imported. The effect of some parameters used on the delamination of
clays such as: hydration, freezing, milling and centrifugation were investigated,
varying the amount of dispersant and stirring time. The clays were heat treated
between 800 and 1250°C with heating rate between 5 and 30°C/min and kept at
the maximum temperature for 10 and 60 min. The phase evaluation in the
powders before and after heating was investigated by X-ray diffraction and the
surface morphology was investigated by a scanning electron microscope. The
best results of the delamination process were observed for samples that
showed no sodium oxide. From the diffraction X-ray observed that the heating
rate influence on the reactions during heating, the structure of the clay was kept
to 8 0 0 X for faster rates and the peaks of mullite and cordierite were detected
to lower temperatures when the heating rate was slower. Regarding the
physical and mechanical properties, it was observed that the sample with higher
alumina/silica ratio showed the best results. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7724 |
|
dc.date.accessioned |
2019-10-04T14:32:45Z |
|
dc.date.available |
2019-10-04 |
|
dc.date.available |
2019-10-04T14:32:45Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Argilas |
|
dc.subject |
Argilas Bentonitas |
|
dc.subject |
Argilas Caulinitas |
|
dc.subject |
Delaminação |
|
dc.subject |
Defloculante |
|
dc.subject |
Raios - X(DRX) |
|
dc.subject |
Cerâmica |
|
dc.subject |
Clay |
|
dc.subject |
Bentonite Clay |
|
dc.subject |
Kaolinite Clays |
|
dc.subject |
Delamination |
|
dc.subject |
Dispersant |
|
dc.subject |
X-Rays (XRD) |
|
dc.subject |
Ceramics |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
GONÇALVES, Wherllyson Patrício. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Evaluation of the influence of different heat treatments on the phase transformations of bentonite and bentonite / kaolinite clays. |
pt_BR |
dc.identifier.citation |
GONÇALVES, Wherllyson Patricio. Avaliação da influência de diferentes tratamentos térmicos sobre as transformações de fases de argilas-bentonita e bentonita/caulinita. 2014. 82 f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2014. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7724 |
pt_BR |