dc.creator.ID |
ARAUJO, S. S. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/5879783367155053 |
pt_BR |
dc.contributor.advisor1 |
SILVA, Suédina Maria de Lima. |
|
dc.contributor.advisor1ID |
SILVA, S. M. L. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/6437959556217825 |
pt_BR |
dc.contributor.advisor2 |
RAPOSO, Claudia Maria de Oliveira. |
|
dc.contributor.advisor2ID |
RAPOSO, C. M. O. |
|
dc.contributor.advisor2Lattes |
http://lattes.cnpq.br/1871453162740241 |
|
dc.contributor.referee1 |
CANEDO, Eduardo Luis. |
|
dc.contributor.referee2 |
MALTA, Oscar Manoel Loureiro. |
|
dc.description.resumo |
Neste estudo, nanocompósitos polipropileno/argila foram preparados pelo
método de intercalação por fusão. Na primeira etapa da pesquisa, uma argila
bentonítica, fornecida pela Bentonit União Nordeste, Campina Grande, PB, foi
submetida a um tratamento químico de purificação visando a remoção de
matéria orgânica. As bentonitas, não purificada e purificada foram modificadas
com o sal orgânico brometo de cetil trimetil amônio. Como parâmetro de
comparação utilizou-se uma argila organofílica comercial Closite 20A, fornecida
pela Southern Clay Products, Gonzales, Texas (EUA). As bentonitas foram
caracterizadas por espectroscopia no infravermelho (FTIR) e difração de
raios-X (DRX). Os resultados mostraram que o tratamento de purificação e
organofilização foram bem sucedidos. Os nanocompositos, PP/argila, contendo
1, 3 e 5 % em massa de argila organofílica, foram preparados em extrusora
dupla rosca contra-rotativa acoplada ao reômetro de torque Haake e corpos de
prova, empregados na caracterização mecânica e termomecânica dos
nanocompósitos, foram moldados por injeção. A morfologia dos
nanocompositos foi avaliada por DRX. Medidas de resistência ao impacto,
dureza e temperatura de reflexão térmica também foram realizadas. Os
resultados mostraram que o tipo e teor de argila influenciaram
consideravelmente na morfologia e propriedades dos nanocompósitos. De
forma geral, as melhores propriedades estudadas foram exibidas pelos
nanocompósitos contendo 1% em massa de argila organofílica. Os
nanocompósitos preparados com argila organofílica purificada, sintetizada neste
estudo, mostraram propriedades semelhantes as dos nanocompósitos
preparados com argila organofílica comercial. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.title |
Nanocompósitos PP/argila. Influência do tipo e do teor de silicato em camadas. |
pt_BR |
dc.date.issued |
2008-02-28 |
|
dc.description.abstract |
Polypropylene (PP) and clay nanocomposites were prepared by the melt
intercalation process. Bentonite clay, provided by Bentonit Uniao Nordeste, of
Campina Grande, Paraiba (Brazil), was subject to a chemical purification
treatment in order to remove organic matter impurities. Raw and purified clays
were then modified with the organic salt cetyl trimethyl ammonium bromide.
Clays samples were characterized by infrared spectroscopy and x-ray
diffraction. Results showed that the purification and organofilization treatments
were successful. As a comparative, tests were also performed with a
commercial organoclay (Closite 20A) provided by Southern Clay Products,
Gonzales, Texas (USA). PP/bentonite nanocomposites with 1, 3 and 5 %
organoclay loading (by weight) were prepared in a counter-rotating twin-screw
extruder coupled to a Haake rheometer. Test specimens were injection-molded
for mechanical and thermal characterization. The composites morphology was
evaluated by x-ray diffraction. Hardness, impact, and heat deflection tests were
also performed. Then results showed that the type and amount of clay greatly
affect the morphology and mechanical properties of the composite. In general,
better results were obtained with 1% organofilic clay. Nanocomposites prepared
with the bentonite purified and organofilized in this study showed properties
similar to those prepared with the commercial organoclay tested. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7898 |
|
dc.date.accessioned |
2019-10-09T12:19:55Z |
|
dc.date.available |
2019-10-09 |
|
dc.date.available |
2019-10-09T12:19:55Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Nanocompósitos |
|
dc.subject |
Polipropileno |
|
dc.subject |
Bentonita |
|
dc.subject |
Argilas |
|
dc.subject |
Argila Organofílica |
|
dc.subject |
Argila Bentonítica |
|
dc.subject |
Raios x (DRX) |
|
dc.subject |
Nanocomposites |
|
dc.subject |
Polypropylene |
|
dc.subject |
Bentonite |
|
dc.subject |
Clays |
|
dc.subject |
Organophilic Clay |
|
dc.subject |
Bentonitic Clay |
|
dc.subject |
X-Rays (XRD) |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
ARAÚJO, Sueila Silva. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
PP / clay nanocomposites. Influence of type and silicate content in layers. |
pt_BR |
dc.identifier.citation |
ARAÚJO, Sueila Silva. Nanocompósitos PP/argila. Influência do tipo e do teor de silicato em camadas. 2008. 110f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2008. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7898 |
pt_BR |