Estudo do comportamento de fratura em compósitos polímero/madeira (WPC'S) através do método EWF.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS
→
Doutorado em Ciência e Engenharia de Materiais.
→
Ver item

dc.creator.ID	SANTOS, Z. I. G.	pt_BR
dc.contributor.advisor1	RABELLO, Marcelo Silveira.
dc.contributor.advisor1ID	RABELLO, M. S.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/0384726674523131	pt_BR
dc.contributor.advisor2	UEKI, Marcelo Massayoshi.
dc.contributor.advisor2ID	UEKI, M. M.
dc.contributor.referee1	CIOFFI, Maria Odila Hilário.
dc.contributor.referee2	MEDEIROS, Eliton Souto de.
dc.contributor.referee3	CARVALHO, Laura Hecker de.
dc.description.resumo	As propriedades mecânicas e comportamento de fratura do polipropileno heterofásico (PP) e compósitos deste com partículas de madeira foram estudados através do método Trabalho Essencial de Fratura (EWF). Para tanto foram preparadas, em extrusora de dupla rosca corratacional, composições com 0, 5, 15 e 25% em massa de partículas de madeira, com e sem agente de acoplamento e os corpos de prova, tipo DENT (entalhados duplamente nas faces opostas), foram confeccionados a partir de placas moldadas por injeção. Os dados usados para determinar os parâmetros do método EWF foram obtidos do ensaio de tração unidirecional. Inicialmente foram realizados ensaios na matriz polimérica para verificar a validade do uso do método EWF para o polipropileno (PP). Em seguida foram avaliados a influencia do teor de partículas de madeira, presença de agente de acoplamento, espessura das amostras e envelhecimento acelerado sobre os parâmetros do método EWF. Os resultados obtidos permitem concluir que o método EWF se mostrou eficiente para avaliar o comportamento de fratura do polipropileno puro e seus compósitos com e sem um agente de acoplamento. Alem disso, ficou evidente que o trabalho essencial especifico de fratura, we, dos compósitos foi consideravelmente menor, do que aquele apresentado pelo PP puro, e a dissipação de energia plastica, Bwp, diminuiu acentuadamente com o aumento do teor de partículas de madeira. Concluiu-se ainda que a presença de um agente de acoplamento promoveu uma recuperação no valor do we, enquanto que a presença deste aditivo levou a uma diminuição do trabalho não-essencial especifico de fratura (J3wp). Os parâmetros do método EWF foram afetados pela espessura dos corpos de prova sendo este efeito mais pronunciado no valor do trabalho essencial de fratura (we ) , enquanto que o trabalho não-essencial especifico de fratura (pwp) sofre pouca influencia deste fator. Concluiu-se ainda que, sob as condições usadas, não se conseguiu valores validos para os parâmetros do método EWF para amostras apos envelhecimento acelerado. Mostrando grande efeito de borda e transição de estado piano de tensão/deformação durante realização dos ensaios. Mesmo assim, foram obtidos valores para uma analise qualitativa, ficando evidente que o processo de fotodegradação da matriz foi acelerado pela presença das partículas de madeira.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.title	Estudo do comportamento de fratura em compósitos polímero/madeira (WPC'S) através do método EWF.	pt_BR
dc.date.issued	2012-12-17
dc.description.abstract	Mechanical properties and fracture behavior of heterophasic polypropylene (PP) and PP composites with wood particles were studied by the Essential Work of Fracture (EWF) method. All formulations, with and without coupling agent containing 0, 5, 15 and 25% wood particles were prepared by twin screw extrusion; and the specimens type DENT were injection molded. The data used to determine the EWF parameter's were obtained from tensile test. Firstly, it was verified the validity of EWF method for PP matrix. The influence of wood particle content, coupling agent, sample thickness and accelerated aging on the EWF parameters was studied. The results show that it is possible to use the EWF method to evaluate the fracture behavior of pure polypropylene and its composites with and without a coupling agent. Results also show that specific essential work of fracture, we, of the composites was significantly smaller than that pure PP, and plastic energy dissipation, (3wp decreased markedly with increasing content particle. It was concluded that the coupling agent promoted an increase in the we value and a decrease in the specific non-essential work of fracture (fiwp). The effects of thickness on EWF parameters was more pronounced on essential work of fracture (we ) parameter, while non-essential specific work of fracture (/3wp) was. It was also shown that non valid values of EWF parameter were observed for aged samples, showing great edge effect and transition from plane stress to plane strain. It was observed that photodegradation process of the PP matrix was accelerated by the presence of the wood particles.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7902
dc.date.accessioned	2019-10-09T13:14:30Z
dc.date.available	2019-10-09
dc.date.available	2019-10-09T13:14:30Z
dc.type	Tese	pt_BR
dc.subject	Polímero Madeira (WPC)
dc.subject	Compósitos
dc.subject	Mecânica da Fratura
dc.subject	Trabalho Essencial de Fratura (EWF)
dc.subject	Matriz de Prolipopileno
dc.subject	Partículas de Madeira
dc.subject	Método EWF
dc.subject	Wood Polymer (WPC)
dc.subject	Composites
dc.subject	Fracture Mechanics
dc.subject	Essential Work Fracture (EWF)
dc.subject	Prolipopylene Matrix
dc.subject	Wood Particles
dc.subject	EWF Method
dc.rights	Acesso Aberto	pt_BR
dc.creator	SANTOS, Zora Ionara Gama dos.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Study of fracture behavior in polymer / wood composites (WPC'S) using the EWF method.	pt_BR
dc.identifier.citation	SANTOS, Zora Ionara Gama dos. Estudo do comportamento de fratura em compósitos polímero/madeira (WPC'S) através do método EWF. 2012. 150f. (Tese de Doutorado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2012. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7902	pt_BR