Solidificação de ligas Al-Si super resfriadas pela técnica de fluxo.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA
→
Mestrado em Engenharia Mecânica.
→
Ver item

dc.creator.ID	SILVEIRA, A. F.	pt_BR
dc.contributor.advisor1	CASTRO, Walman Benício de.
dc.contributor.advisor1ID	CASTRO, W. B.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/3592569966434979	pt_BR
dc.contributor.referee1	ALVES JÚNIOR, Clodomiro.
dc.contributor.referee2	LEITE, Josinaldo Pereira.
dc.description.resumo	O presente trabalho apresenta o estudo da solidificação de ligas do sistema Al-Si, super-resfriadas pela técnica de Fusão em Presença de Fluxo. Os resultados mostraram que a técnica de fluxo foi eficiente na obtenção de altos níveis de super-resfriamento para ligas do sistema Al-Si. Tanto para as ligas hipo-eutéticas quanto para as ligas hiper-eutéticas, um aumento do super-resfriamento foi observado, quando as amostras foram solidificadas envolto com o B2O3 como fluxo. Isto comprova que o fluxo atuou na eliminação ou redução de heterogeneidades presentes nas amostras e/ou evitando o contato das amostras com as paredes do cadinho. Contudo, apesar do aumento de AT ser bastante significativo, da ordem de 20K, não foram observadas mudanças significativas nas microestruturas dessas ligas.Isto, provavelmente, porque não se atingiu o nível de super-resfriamento critico para as ligas em estudo.Os resultados mostraram que o aumento de soluto nas ligas hipo-eutéticas provocou uma diminuição no nível de super-resfriamento, provavelmente porque o Si tem crescimento facetado, o que fornece baixos ângulos de molhamento.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia Mecânica
dc.title	Solidificação de ligas Al-Si super resfriadas pela técnica de fluxo.	pt_BR
dc.date.issued	2001-06-08
dc.description.abstract	This work aimed at the study of the solidification Al-Si alloys by the fluxing technique.The results showed that technique was efficient to obtain large undercoolings. The increasing undercooling was observed when the alloys used B2O3 as flux. The flux B2O3, probably, acted in removed impurities or changed structures and make them less active, and/or isolated the molten metal from contact with the crucible and atmosphere.I lowevcr, a morphological change did not occur in spit of increasing of undercooling. That is probable of the critical undercooling unattainable in the alloys.The results showed that the increasing of the solute for hypoeuteclic alloys decreased the level undercooling, probably of the solute Si has growth faceted.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/8033
dc.date.accessioned	2019-10-11T20:38:37Z
dc.date.available	2019-10-11
dc.date.available	2019-10-11T20:38:37Z
dc.type	Dissertação	pt_BR
dc.subject	Solidificação
dc.subject	Ligas Al-Si
dc.subject	Ligas do sistema Al-Si - Super-resfriamento
dc.subject	Técnica de Fluxo
dc.subject	Ligas Hipo-eutélicas
dc.subject	Crescimento Facetado
dc.subject	Solidification
dc.subject	Al-Si Leagues
dc.subject	Alloys of the Al-Si System - Super-cooling
dc.subject	Flow Technique
dc.subject	Hypo-eutelic Alloys
dc.subject	Faceted Growth
dc.rights	Acesso Aberto	pt_BR
dc.creator	SILVEIRA, Alessandro Frederico da.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Solidification of supercooled Al-Si alloys by flow technique.	pt_BR
dc.identifier.citation	SILVEIRA, Alessandro Frederico da. Solidificação de ligas Al-Si super resfriadas pela técnica de fluxo. 2001. 81f. (Dissertação de Mestrado em Engenharia Mecânica), Curso de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba – Campus II - Campina Grande - PB - Brasil, 2001. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/8033	pt_BR