dc.description.resumo |
Os argilominerais pertencem à família dos filossilicatos lamelares, que podem ser definidos como
silicatos contendo folhas bidimensionais. Os cristais consistem em lamelas tetraédricas e
octaédricas, geralmente do tipo 2:1. As unidades fundamentais são Si(O,OH) 4 , constituindo a rede
tetraédrica e M(O,OH) 6 constituindo a rede octaédrica, com M = Mg 2+ , Al 3+ , Fe 2+ e Fe 3+ . As
argilas são materiais naturais que tem despertado grande interesse, devido suas características
texturais e a possibilidade de reações de modificação para a otimização das propriedades, como é o
caso da lixiviação ácida. O presente estudo avaliou sólidos obtidos a partir de tratamento químico
do argilomineral vermiculita, pelo processo de lixiviação ácida com reutilização do ácido lixiviante,
no intuito de promover aspectos econômicos e ambientais positivos à síntese. Nesse processo, a
argila limpa e monoiônica foi tratada com solução ácida de H 2 SO 4 com concentração de 2,0
mol.dm -3 , razão de 1:10 (argila, ácido), sob refluxo, a uma temperatura de 353 K, obtendo-se assim
o primeiro sólido. Após o procedimento, o ácido utilizado foi recolhido, tanto quanto possível (~30
cm 3 ), seu volume foi completado para 50 cm 3 , sendo assim reutilizado na repetição do
procedimento de lixiviação com uma nova amostra. Esse processo de reutilização do ácido foi
repetido sete vezes afim de avaliar capacidade lixiviante do ácido, obtendo-se um total de 8 sólidos,
sequencialmente: VA1, VA2, VA3, VA4, VA5, VA6, VA7, VA8, que foram submetidos a
caracterização química. Os resultados obtidos a partir da fluorência de raio X, difratometria de raio
X e por espectroscopia na região do infravermelho demonstraram que a síntese com reutilização do
ácido é efetiva, obtendo-se materiais com composição e estrutura cristilina diferentes, com
características amorfas e novos sítios propícios a adsorção e catálise. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Formação de Professores - CFP |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Química. |
pt_BR |
dc.title |
Reutilização de ácido sulfúrico no tratamento químico de Vermiculita. |
pt_BR |
dc.date.issued |
2016-05-28 |
|
dc.description.abstract |
Clay minerals belong to the lamellar phylosilicate family, which can be defined as
silicates containing two-dimensional sheets. The crystals consist of tetrahedral coverslips and
octahedral, usually of the 2: 1 type. The fundamental units are Si (O, OH) 4, constituting the
tetrahedral and M (O, OH) 6 constituting the octahedral network, with M = Mg 2+, Al 3+, Fe 2+ and Fe 3+. At
Clays are natural materials that have aroused great interest due to their characteristics.
textures and the possibility of modification reactions for the optimization of properties, such as the
case of acid leaching. The present study evaluated solids obtained from chemical treatment
vermiculite clay, by the acid leaching process with reuse of the leaching acid,
in order to promote positive economic and environmental aspects to synthesis. In this process,
Clean, monoionic clay was treated with H 2 SO 4 acid solution with a concentration of 2.0
mol.dm -3, 1:10 (clay, acid) at reflux at a temperature of 353 K to give
The first solid. After the procedure, the acid used was collected as much as possible (~ 30
cm 3), its volume was completed to 50 cm 3, thus being reused in the repetition of the
leaching procedure with a new sample. This acid reuse process was
repeated seven times to assess acid leaching capacity, yielding a total of 8 solids,
sequentially: VA1, VA2, VA3, VA4, VA5, VA6, VA7, VA8, who underwent
chemical characterization. Results obtained from X-ray fluorescence, X-ray diffraction
X-ray and infrared spectroscopy demonstrated that the synthesis with reuse of the
acid is effective, obtaining materials with different composition and structure crystalline, with
amorphous characteristics and new sites for adsorption and catalysis. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/8260 |
|
dc.date.accessioned |
2019-10-21T13:57:19Z |
|
dc.date.available |
2019-10-21 |
|
dc.date.available |
2019-10-21T13:57:19Z |
|
dc.type |
Trabalho de Conclusão de Curso |
pt_BR |
dc.subject |
Vermiculita |
pt_BR |
dc.subject |
Ácido sulfúrico - reutilização |
pt_BR |
dc.subject |
Lixiviação ácida |
pt_BR |
dc.subject |
Vermiculite |
pt_BR |
dc.subject |
Sulfuric Acid - Reuse |
pt_BR |
dc.subject |
Acid leaching |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
NUNES FILHO, Francisco Gilmário. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Sulfuric acid reuse in chemical treatment of vermiculite. |
pt_BR |
dc.identifier.citation |
NUNES FILHO, Francisco Gilmário. Reutilização de ácido sulfúrico no tratamento químico de Vermiculita. 2016. 24f. Trabalho de Conclusão de Curso (Licenciatura em Química) - Centro de Formação de Professores, Universidade Federal de Campina Grande, Cajazeiras, Paraíba, Brasil, 2016. |
pt_BR |