dc.creator.ID |
SILVA, F. N. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/6430458195049325 |
pt_BR |
dc.contributor.advisor1 |
COSTA, Ana Cristina Figueiredo de Melo. |
|
dc.contributor.advisor1ID |
COSTA, A. C. F. M. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/6309225172752964 |
pt_BR |
dc.contributor.advisor2 |
SILVA, Adriano Sant'Ana da. |
|
dc.contributor.advisor2ID |
SILVA, A. S. |
|
dc.contributor.referee1 |
ALMEIDA, Ester Pires de. |
|
dc.contributor.referee2 |
VIANA, Kaline Melo de Souto. |
|
dc.description.resumo |
O biodiesel destaca-se como uma alternativa viável frente ao diesel de petróleo. Este
biocombustível, proveniente de matérias primas renováveis, se destaca por ser
biodegradável, seguro, pouco poluente (baixas emissões de dióxido de carbono e enxofre) e por gerar oportunidade econômica para pequenos e médios produtores rurais. Deste modo, o objetivo desta proposta foi obter zircônia (Z1O2) por síntese de combustão e fazer uma análise comparativa quanto a estrutura e morfologia de uma zircônia monoclínica comercial e investigar a sulfatação visando a obtenção de catalisadores ácidos para ser avaliados na esterificação do óleo de algodão para obtenção de biodiesel. A Z1O2 sintética foi obtida por reação de combustão em batelada de 15 g do produto, usado como precursor o n-propóxido de zircônio IV e ureia. A Z1O2 comercial foi fornecida pela empresa Saint-Gobain Zirpro. As amostras foram caracterizadas por difração de raios X (DRX), microscópia eletrônica de varredura (MEV), analise textural por adsorção de nitrogênio (BET), espectroscopia de infravermelho com transformada de Fourier (FTIR), análise termogravimétrica (TG/DrTG) e análise térmica diferencial (DTA), espectroscopia de fluorescência de raios X (EDX), distribuição granulométrica e cromatografia gasosa. A Z1O2 sintetizada mostrou a formação da fase majoritária monoclínica com tracos da fase ortorrômbica, com tamanho de cristalito 16 nm e cristalinidade 57 %. Para a amostra comercial foi identificada apenas a fase única
monoclínica com tamanho de cristalito 39 nm e cristalinidade de 86 %. Com o processo
de sulfatacao e calcinacao de ambas as Z1O2 (sintetizada e comercial), verificou-se o
surgimento de traços da fase tetragonal, tipicas de S0427Zr02, com a permanência da
fase majoritária monoclínica nas duas amostras sulfatadas. Os tamanhos de cristalitos e
cristalinidades resultaram em uma diminuição dos seus valores com a sulfatação,
apresentando tamanho de cristalito 16 nm e cristalinidade 44 % para a S0427Zr02
sintetizada e tamanho de cristalito 27 nm e cristalinidade 67 % para a S0427Zr02
comercial. Ambas as amostras apresentaram morfologia homogênea, constituída de
partículas muito finas de formato aproximadamente esférico. Comparando as amostras
entre si, verificou-se que a síntese por reação de combustão foi eficiente para obter
nanopartículas de Z1O2 monoclínica com tracos da fase ortorrômbica com morfologia das partículas mais finas que a Z1O2 comercial monoclínica. A análise cromatográfica indicou conversão de 26 e 28 % em esteres metílicos para a ZK)2 como sintetizada e comercial, e conversão máximas em torno de 65 e 91% em esteres metílicos para as S042"/Zr02 sintetizada e comercial, respectivamente. Os resultados indicaram que a sulfatação aumenta a acidez e contribui significativamente para o aumento da conversão, indicando que a S042"/Zr02 6 um catalisador promissor para esterificação de biodiesel. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.title |
Preparação e caracterização de catalisadores ácidos zircônia sulfatada para aplicação na esterificação do óleo de algodão. |
pt_BR |
dc.date.issued |
2013-08-23 |
|
dc.description.abstract |
Biodiesel stands out as a viable alternative to petroleum diesel. This one
biofuel from renewable raw materials stands out for being
biodegradable, safe, low-polluting (low carbon dioxide and sulfur emissions) and for generating economic opportunity for small and medium farmers. Thus, the objective of this proposal was to obtain zirconia (Z1O2) by combustion synthesis and to make a comparative analysis regarding the structure and morphology of a commercial monoclinic zirconia and to investigate the sulfation aiming to obtain acid catalysts to be evaluated in the esterification of cotton to obtain biodiesel. Synthetic Z1O2 was obtained by 15 g batch combustion reaction of the product, used as precursor of zirconium IV n-propoxide and urea. Commercial Z1O2 was supplied by the company Saint-Gobain Zirpro. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), textural analysis by nitrogen adsorption (BET), Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TG / DrTG) and differential thermal analysis (DTA), X-ray fluorescence spectroscopy (EDX), particle size distribution and gas chromatography. The synthesized Z1O2 showed the formation of the majority monoclinic phase with traces of the orthorhombic phase, with crystallite size 16 nm and crystallinity 57%. For the commercial sample, only the single phase was identified.
monoclinic with crystallite size 39 nm and crystallinity of 86%. With the process
sulfation and calcination of both Z1O2 (synthesized and commercial),
traces of the tetragonal phase, typical of S0427Zr02, with the permanence of the
majority monoclinic phase in the two sulfated samples. The sizes of crystallites and
crystallinities resulted in a decrease in their values with sulfation,
Featuring 16 nm crystallite size and 44% crystallinity for the S0427Zr02
synthesized and crystallite size 27 nm and crystallinity 67% for the S0427Zr02
commercial. Both samples presented homogeneous morphology, consisting of
very fine particles of approximately spherical shape. Comparing the samples
among them, it was found that the synthesis by combustion reaction was efficient to obtain
monoclinic Z1O2 nanoparticles with traces of the orthorhombic phase with finer particle morphology than commercial monoclinic Z1O2. Chromatographic analysis indicated conversion of 26 and 28% in methyl esters to ZK) 2 as synthesized and commercial, and maximum conversion around 65 and 91% in methyl esters to synthesized and commercial S042 "/ Zr02, respectively. The results indicated that sulfation increases acidity and contributes significantly to increased conversion, indicating that S042 "/ Zr02 6 is a promising catalyst for biodiesel esterification. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/8290 |
|
dc.date.accessioned |
2019-10-21T19:49:14Z |
|
dc.date.available |
2019-10-21 |
|
dc.date.available |
2019-10-21T19:49:14Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Reação de Combustão |
|
dc.subject |
Catalizador - Zr02
. |
|
dc.subject |
Esterificação |
|
dc.subject |
Biodisel |
|
dc.subject |
Combustível |
|
dc.subject |
Matéria-Prima |
|
dc.subject |
Zircônia |
|
dc.subject |
Uréia |
|
dc.subject |
Combustion Reaction |
|
dc.subject |
Catalyst - Zr02 |
|
dc.subject |
Esterification |
|
dc.subject |
Biodisel |
|
dc.subject |
Fuel |
|
dc.subject |
Feedstock |
|
dc.subject |
Zirconia |
|
dc.subject |
Urea |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SILVA, Francisco Nilson da. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Preparation and characterization of sulfated zirconia acid catalysts for application in cotton oil esterification. |
pt_BR |
dc.identifier.citation |
SILVA, Francisco Nilson da. Preparação e caracterização de catalisadores ácidos zircônia sulfatada para aplicação na esterificação do óleo de algodão. 2013. 72f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2013. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/8290 |