Efeito do alívio de tensões sobre as propriedades mecânicas de uma junta soldada do aço API 5L X60.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA
→
Mestrado em Engenharia Mecânica.
→
Ver item

dc.creator.ID	MELO, J. B. C. A.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/7962147028271194	pt_BR
dc.contributor.advisor1	MACIEL, Theophilo Moura.
dc.contributor.advisor1ID	MACIEL, T. M.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/947685893835184	pt_BR
dc.contributor.referee1	BRACARENSE, Alexandre Queiroz.
dc.contributor.referee2	SANTOS, Marco Antônio dos.
dc.description.resumo	A proposta deste trabalho foi analisar a influencia do tempo e da temperatura no tratamento térmico para alivio de tensões no que se refere as propriedades de energia de impacto e dureza de uma junta soldada de uma tubulação de aço API 5L X60, usada para a condução de petróleo. Para tanto foram realizados ensaios de dureza Vickers com carga de 98,IN (lOkgf) e testes de resistência ao impacto Charpy a uma temperatura de 253K (-20 C) em corpos de prova com os entalhes confeccionados nas regiões de metal de base, zona termicamente afetada (ZTA) e metal de solda. Todos os corpos de prova foram submetidos a tratamentos térmicos para alivio de tensões a uma temperatura de 823K (550 C) por uma hora e a temperatura de 923K (650 C) por tempos de: 1 , 5 , 8 e 11 horas. Os resultados obtidos indicaram que com relação ao metal de solda houve um acréscimo na tenacidade em ambas as temperaturas de tratamento para o tempo de 1 hora, com maior eficiência neste aspecto com relação a temperatura de 823K (550 C). Para tempos maiores, na temperatura de 923K (650 C) observou-se uma tendência a estabilização desta propriedade. Com relação ao metal de base verificou-se uma acentuada queda da tenacidade para tratamentos a 923K (650 C) por uma hora se comparado ao mesmo tempo para 823K (550 C) e uma tendencia de estabilização da dureza para temperatura de 923K (650 C). Com relação a ZTA observou-se uma acentuada variação dos valores de resistência ao impacto.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia Mecânica
dc.title	Efeito do alívio de tensões sobre as propriedades mecânicas de uma junta soldada do aço API 5L X60.	pt_BR
dc.advisor1	Alívio de Tensões - Efeito.
dc.date.issued	2002-05-03
dc.description.abstract	The purpose of this work was to analyze the influence of the time and temperature of relief stress thermal treatment on the hardness and impact resistance of a welded joint of an API 5L X60 steel pipeline used for petroleum transmission. For this, Vickers hardness and Charpy impact test at 253K (-20 C) were executed in specimens extracted from weld metal, heat affected zone (HAZ) and base metal submitted to thermal treatment at 823K (550 C) and 923K (650 C) for 1 hour and at 923K (650 C) for. lh, 5h, 8h and 11 hours. The results indicated an increase of weld metal and HAZ impact resistance for treatment of 1 hour at both temperatures, with larger efficiency at temperature of 823K (550yC). However, it was observed a great decrease of metal base impact resistance at temperature of 923K (650 C). A decrease of the impact resistance for all the welded joints regions was observed for time higher than 8 hours at 923K (650 C), in spite of the stability of hardness values.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/8433
dc.date.accessioned	2019-10-23T19:29:28Z
dc.date.available	2019-10-23
dc.date.available	2019-10-23T19:29:28Z
dc.type	Dissertação	pt_BR
dc.subject	Tratamento Térmico
dc.subject	Junta Soldada - Propriedades Mecânicas
dc.subject	Tubulação de Aço API 5L X60
dc.subject	Alívio de Tensões
dc.subject	Microestrutura da ZTA
dc.subject	Ensaios de Iimpacto CHARPY
dc.subject	Heat Treatment
dc.subject	Welded Joint - Mechanical Properties
dc.subject	API 5L X60 Steel Pipe
dc.subject	Stress Relief
dc.subject	ZTA Microstructure
dc.subject	Impacto CHARPY Assays
dc.rights	Acesso Aberto	pt_BR
dc.creator	MELO, João Baptista da Costa Agra de.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Stress relief effect on the mechanical properties of a welded joint of API 5L X60 steel.	pt_BR
dc.identifier.citation	MELO, João Baptista da Costa Agra de. Efeito do alívio de tensões sobre as propriedades mecânicas de uma junta soldada do aço API 5L X60. 2002. 107f. (Dissertação de Mestrado em Engenharia Mecânica), Curso de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba – Campus II - Campina Grande - PB - Brasil, 2002. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/8433	pt_BR