dc.description.resumo |
Neste trabalho foram sintetizadas nanopartículas de ferrita de níquel (NiFe204 ) e
oxido de níquel (NiO) pelos métodos da reação de combustão, a 500°C, e método
Pechini, a 700, 900 e 1100°C. Foram realizadas caracterizações estrutural através
de difração de raios-x (DRX) e microscopia eletrônica de varredura (MEV) e técnica
através da magnetometria por amostra vibrante (VSM). Também foram feitas
analises de adsorção e dessorção (em termos da resistência elétrica versus
umidade relativa) nas amostras para aplicação das mesmas como dispositivos de
sensor de umidade. Através dos refinamentos Rietveld foi possível identificar e
quantificar a presença da fase cristalina da ferrita de níquel e uma pequena
concentração da fase cristalina do oxido de níquel. Os resultados do refinamento de
Rietveld mostraram que os domínios cristalinos das amostras pelo método Pechini
crescem com o aumento da temperatura de 700 para 900°C, ficando estável de 900
para 1100°C. Através das imagens obtidas por MEV, foi possível observar boa
morfologia, que privilegia a formação de poros para todas as amostras. Foi possível
observar também um aumento no tamanho médio dos grãos de partículas com o
aumento da temperatura de tratamento térmico, provavelmente devido a
coalescência entre as partículas favorecida em altas temperaturas. Por meio das
curvas de magnetização, foi observado que houve uma diminuição na magnetização
saturação como o aumento médio dos tamanhos de grãos e de domínio cristalino
para as amostras obtidas pelo método Pechini, talvez em decorrência da maior
coalescência das partículas. Para a aplicação das amostras como dispositivo de
sensor de umidade, foi observado que a amostra obtida pelo método da combustão
a 500°C na forma de filme obteve um menor tempo de resposta. No entanto, a
amostra obtida pelo método Pechini a 700°C na forma de filme obteve a maior
sensibilidade a umidade e menor tempo de recuperação, tendo assim um melhor
desempenho na aplicação. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM FÍSICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Física |
|
dc.title |
Síntese pelos métodos de combustão e Pechini e caracterização de ferrita de níquel para aplicação como dispositivos de sensor de umidade. |
pt_BR |
dc.date.issued |
2012-08-31 |
|
dc.description.abstract |
In this study, nickel ferrite (NiFe204) plus nickel oxide (NiO) nanocomposites were
synthesized by chemical routes: combustion reaction at 500 0 C, and Pechini method
at 700, 900 and 1100 0 C. X-ray diffractometry (XRD) and scanning electron
microscopy (SEM) were used to the structural and morphological characterizations.
Hysteresis curves at room temperature were obtained using a vibrating sample
magnetometer (VSM). Also, the electrical resistance versus relative humidity of the
composites (adsorption and desorption) in the form of fims were obtained. These
measurements characterized the samples for application as humidity sensor devices.
Rietveld refinement of the XRD patterns possibly to identify and quantify the
presence of crystalline nickel ferrite and nickel oxide (in smaller concentration)
phases. The crystallite mean size for the samples obtained by the Pechini method
grows with increasing temperature from 700 to 900 ° C, being stable from 900 to
1100 ° C. The images obtained by SEM showed good morphology for the
nanoparticles, which favors the formation of pores for all samples. However, the
number of pores and volume of pores seems to be different for all samples, showing
influences on the electrical properties (qualities of the humidity sensor). It was also
observed an increase in the average grain size of samples with increasing heat
treatment temperature, probably due to the coalescence between crystallites favored
at higher temperatures. The magnetization curves for the samples showed low
coercivity and high saturation magnetization, which classify it as a soft ferromagnet
(or ferrimagnet). For the electrical resistance versus relative humidity curves, it was
observed that the sample obtained by combustion reaction method showed a shorter
response time, when compared to the Pechini reaction ones. In addition, samples
obtained by Pechini reaction at 700 ° C showed greater sensibility to humidity and
smaller recover time, both related to good performance in humidity sensor
applications. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/9400 |
|
dc.date.accessioned |
2019-11-22T09:58:37Z |
|
dc.date.available |
2019-11-22 |
|
dc.date.available |
2019-11-22T09:58:37Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Métodos Químicos |
|
dc.subject |
Nanopartículas |
|
dc.subject |
Sensor de Umidade |
|
dc.subject |
Ferrita de Níquel |
|
dc.subject |
Magnetização |
|
dc.subject |
Chemical Methods |
|
dc.subject |
Nanoparticles |
|
dc.subject |
Humidity Sensor |
|
dc.subject |
Nickel Ferrite |
|
dc.subject |
Magnetization |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
BATISTA, Sérgio Orlando de Souza. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Synthesis by combustion and pechini methods and characterization of nickel ferrite for application as moisture sensor devices. |
pt_BR |
dc.identifier.citation |
BATISTA, Sérgio Orlando de Souza. Síntese pelos métodos de combustão e Pechini e caracterização de ferrita de níquel para aplicação como dispositivos de sensor de umidade. 2012. 81 f. (Dissertação de Mestrado Física), Programa de Pós-graduação em Física, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2012. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/9400 |
pt_BR |