dc.creator.ID |
SIMÔES, V. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/2778227218803881 |
pt_BR |
dc.contributor.advisor1 |
SWARNAKAR, Ramdayal. |
|
dc.contributor.advisor1ID |
SWARNAKAR, R. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/7715418558296303 |
pt_BR |
dc.contributor.advisor2 |
FOSSY, Michel François. |
|
dc.contributor.advisor2ID |
FOSSY, M. F. |
|
dc.contributor.advisor2Lattes |
http://lattes.cnpq.br/2098082949939565 |
|
dc.contributor.referee1 |
SILVA, Paulo Roberto Nagipe. |
|
dc.contributor.referee1ID |
SILVA, P. R. N. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/0216555371437522 |
pt_BR |
dc.description.resumo |
A variação de atividade de desidrogenação do isopropanol com pre-tratamento em
02 e H2 do catalisador redox Cr203/Mn02 e estudada num reator tubular de fluxo
continuo, tipo "U", isotermico e a pressão atmosférica. Foram preparadas as seguintes
amostras em percentagem mássica em Cr203: 0; 2,5; 5,0; 10,0; 20,0 e 100,0, pelo método de evaporação da solução de nitrato de cromo (III) sobre oxido de manganês. Estas foram calcinadas a temperatura de 400, 450 e 700 °C, por um periodo de 5 horas. As atividades foram medidas em termo de conversão percentual do isopropanol, pela
evolução do gás hidrogênio. Foram observados os seguintes resultados: (a) O
catalisador 5% Cr203, Mn02 apresentou a maior atividade (conversão) dentre os
catalisadores preparados, e este foi 0 escolhido para estudar os demais fatores; (b) O
catalisador 5% Cr203'Mn02, quando pre-tratado com 02, foi mais ativo e estável que o
pre-tratado com Ff2, num período de 10 horas de uso continuo; (c) O efeito de difusão
externa do reagente sobre o catalisador 5% Cr203/Mn02 e desprezível ate um fator
tempo de residencia de l,0gcn.h.mol-1; (d) A atividade catalítica do catalisador 5%
Cr203/Mn02 diminuiu com o aumento do tempo de redução e atingiu um valor
constante, nas temperaturas de reação de 300, 330 e 360 °C; (e) Com 0 aumento da
temperatura de reação de 300 a 360 °C, houve acréscimo na atividade (conversão) dos
catalisadores 5% Cr203/Mn02, Cr203 e Mn02; (f) A energia de ativação aparente media
do catalisador 5% Cr203/Mn02 , pre-tratado com 02 e H2, foi de 20,70 Kcal/mol; (g) A
atividade do catalisador 5% Cr203/Mn02, diminuiu com 0 aumento da temperatura de
calcinacao na faixa de 400 a 700 °C. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.title |
Influência do pré-tratamento em O2 e H2 sobre a atividade do Cr2 O3/MnO na desidrogenação do isopropanol. |
pt_BR |
dc.date.issued |
1993-03-29 |
|
dc.description.abstract |
The variation of isopropanol dehydrogenation activity of redox Cr203/Mn02
catalyst pretreated with 02 and H2 has been studied using a "U" type, isothermic,
continuous tubular reactor at atmosferic pressure. The following samples having their
mass percent composition of Cr203 as 0; 2.5; 5.0; 10.0; 20.0 and 100 were prepared by the
method of solution evaporation of Chromium (III) nitrate with manganese oxide. These
precursores were calcined for 5 hours at 400, 450 and 700 °C. The activities were
measured in terms of percent conversion of isopropanol by hydrogen gas evolution. The
following results have been observed: (a) the 5% Cr203/Mn02 catalyst showed highest
activity (conversion) among the prepared catalysts and was selected to study the effect
of other factors; (b) the 5% Cr203, Mn02 catalyst showed higher and stable activity when
pretreated by H2 for a period of 10 hours of continuous use; (c) the effect of external
diffusion of the reagent over 5% Cr203,'Mn02 catalyst was neglegible upto a residence
time of l.Ogcat.h.mol-1; (d) the catalytic activity of 5% Cr203/Mn02 catalyst decreased
with the increase of time of reduction and reached a constant value at reaction
temperatures 300, 330 and 360 °C; (e) with increase in reaction temperature from 300 to
360 °C, the activity of the catalysts 5% Cr203/Mn02, Cr203 and Mn02 got increased; (f)
the average apparent energy of activation of 5% Cr203/Mn02 catalyst pretreated with
02 and H2 is found to be 20.70 Kcal/mol; (g) the activity of 5% Cr203/Mn02 catalyst
decreased with the increase in calcination temperature of the catalysts in the range of
400 to 700 °C. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/9531 |
|
dc.date.accessioned |
2019-11-26T12:51:22Z |
|
dc.date.available |
2019-11-26 |
|
dc.date.available |
2019-11-26T12:51:22Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Isopropanol - desidrogenação |
pt_BR |
dc.subject |
Processos químicos - tratamento |
pt_BR |
dc.subject |
Reator tubular de fluxo contínuo |
pt_BR |
dc.subject |
Nitrato de cromo |
pt_BR |
dc.subject |
Óxido de manganês |
pt_BR |
dc.subject |
Catalisador redox |
pt_BR |
dc.subject |
Isopropanol - dehydrogenation |
|
dc.subject |
Continuous flow tubular reactor |
|
dc.subject |
Chromium nitrate |
|
dc.subject |
Manganese oxide |
|
dc.subject |
Redox catalyst |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SIMÕES, Vicemário. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Influence of pretreatment on O2 and H2 on Cr2 O3 / MnO activity on isopropanol dehydrogenation. |
pt_BR |
dc.identifier.citation |
SIMÕES, Vicemário. Influência do pré-tratamento em O2 e H2 sobre a atividade do Cr2O3/MnO na desidrogenação do isopropanol. 1993. 89f. (Dissertação de Mestrado), Programa de Pós-Graduação em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba - Campina Grande - PB - Brasil, 1993. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/9531 |